THERMAL CONDUCTIVITY OF ALUMINUM OXIDE PARTICLE FILLED POLYETHYLENE COMPOSITES

Year 2003, Volume: 5 Issue: 2, 19 - 25, 01.05.2003

Dilek Kumlutaş İsmail H. Tavman

Abstract

In this study, the effective thermal conductivity of high density polyethylene composites is
investigated experimentally as a function of filler concentration and the measured values are
compared with the existing theoretical and empirical models. Samples are prepared by mixing
commercial high density polyethylene and filler materials at various volumetric concentrations, the
mixed powder is then placed in a die and melted at 185 °C under 4 MPa pressure. After cooling and
solidification under pressure, the sample is taken out of the die. The thermal conductivity of the
prepared samples is measured using the Shotherm QTM-D2 thermal conductivity meter working with
a modified hot wire technique in a temperature range from about 0 °C to 70 °C.

Keywords

Thermal conductivity, Composite, Polyethylene.

ALÜMİNYUM OKSİT TANE KATKILI POLİETİLEN MATRİKSLİ KOMPOZİTLERİN ISI İLETİM KATSAYISI

Abstract

Bu çalışmada, yüksek yoğunluklu polietilen kompozit malzemelerin ısı iletim katsayısı, dolgu
malzemesi konsantrasyonunun bir fonksiyonu olarak deneysel şekilde araştırılmıştır ve elde edilen
ölçüm değerleri, literatürdeki teorik ve ampirik model sonuçlarıyla karşılaştırılmıştır. Yüksek
yoğunluklu polietilen ve toz katkı malzemesi kullanılarak değişik hacimsel konsantrasyonlarda
karışımlar elde edilmiştir. Bu toz halindeki karışımlar, 4 MPa basınç altında 185 °C sıcaklıkta
sıkıştırma işlemine tabi tutulmuştur ve soğumaya bırakılarak katılaşması sağlanmıştır. Hazırlanan
örneklerin ısı iletim katsayıları, "Hot-Wire" yöntemi ile çalışan ve 0 °C den 70 °C ye kadar olan
sıcaklık aralığında ölçüm yapabilecek şekilde geliştirilmiş olan "Shotherm QTM-D2" cihazı ile
ölçülmüştür.

Keywords

Isı iletim katsayısı, Kompozit, Polietilen