Abstract
The current potential curves of molybdenum were obtained in basic solutions at different potential ranges using the cyclic voltammetric method. The sodium hydroxide solutions of different concentrations were used as the working media. The anodic behaviours of molybdenum in stirred basic solutions were investigated. It was found that the stability of the passive film on molybdenum in basic solutions decreases due to formation of soluble species and the potentials of the transpassive dissolution depend on the concentration of solutions. In basic solutions a dissolution peak was observed before the transpassive dissolution\'s peak, which was not found in acidic solutions.
Abstract
Bu çalışmada molibdenin bazik çözeltiler içinde değişik potansiyel aralıklarında geri dönüşümlü akım-potansiyel eğrileri (cyclic voltammogram) elde edilmiştir. Çalışma ortamı olarak sodyum hidroksitin farklı derişimlerdeki çözeltileri seçilmiştir. Molibden elektrotun sürekli hareket halinde olan ( karıştırılan ) sodyum hidroksit çözeltileri içindeki anodik davranışı incelenmiştir. Bu çözeltiler içinde molibdenin pasifliğinin bozulup transpasif çözünmenin başladığı potansiyel değerinin derişime göre değiştiği saptanmış ve asidik ortamlarda gözlenemeyen transpasif çözünme pikinden önce bir çözünme piki daha bulunmuştur.
Details
| Primary Language | Turkish |
|---|---|
| Journal Section | Articles |
| Authors | |
| Publication Date | June 1, 2002 |
| Published in Issue | Year 2002 Volume: 22 Issue: 2 |