DIMENSIONAL STABILITY OF LAMINATED VENEER LUMBERS MANUFACTURED BY USING DIFFERENT ADHESIVES AFTER THE STEAM TEST

Abstract

ABSTRACT

Composite materials manufactured from wood with different adhesives are being used increasingly in the construction of furniture frames and buildings. In this study, LVLs were manufactured from pine (Pinus sylvestris L.), poplar (Populus tremula L.) and mulbery (Morus alba L.) veneers with phenolformaldehyde (PF), polyvinyl acetate (PVAc), Desmodur-VTKA (D-VTKA) and urea –formaldehyde (UF) adhesives. Dimensional stability of LVL were measured after being exposed to steam for 2,6,12,24,48 and 96 hour-period according to the procedure of the Turkish Standards (TS) 3639. As a result, the highest density was determined for LVL with PF adhesive in all wood species. The highest weight increment as 113 % for poplar control , the highest radial swelling as 7.99 % for mulberry control, the highest tangential swelling as 5.7 % for mulberry control and the highest longitudinal swelling as 0.58 % for mulberry LVL with PF and PVAc adhesive were determined after being exposed to 96 h steam. Mulberry wood and VTKA and UF are proposed to manufacture of LVL used in damp condition

Keywords

• Key Words: Mechanical properties of adhesives, Composites, Steam

FARKLI TUTKALLARLA ÜRETİLEN LAMİNA KAPLAMA ELEMANLARIN BUHAR DENEYİ SONRASI BOYUTSAL KARARLILIĞI

Abstract

Yapılarda ve mobilya çerçeve konstrüksiyonlarında, farklı tutkallar kullanılarak elde edilen kompozit malzemelerin kullanımı artmaktadır. Bu çalışmada lamine kaplama elemanlar, fenol formaldehit, PVAc, desmodur- VTKA ve üre formaldehit tutkalları kullanılarak, çam (Pinus sylvestris L.), kavak (Populus tremula L.) ve dut (Morus alba L.) odunlarından üretilmiştir. Lamina kaplama elemanların boyutsal stabilitesi, TS 3639 standardına göre 2, 6, 12, 24, 48 ve 96 saat su buharı etkisinden sonra ölçülmüştür. Sonuçlara göre en yüksek yoğunluk, fenol formaldehit tutkalı kullanılarak elde edilen lamina kaplama elemanlarda gözlemlenmiştir. En yüksek ağırlık artışı, % 113 ile kavak ağacı kontrol örneklerinde, kalınlık artışı % 7,99’ luk ve liflere dik yöndeki genişlik artışı da % 5,7’lik artış ile dut kontrol örneklerinde, liflere paralel artış ise % 0,58’lik artış ile fenol formaldehit ve PVAc tutkalı kullanılarak dut odunlarından üretilen laminalarda belirlenmiştir

Keywords

• Boyutsal stabilite, Lamine kaplama eleman, Tutkallar, Su buharı testi

References

1. Beekman, W. B., “Elsevier’s Wood Dictionary I, Commercial and Botanical Nomenclature of World-Timbers Sources of Supply”, Elsevier Publishing Company, INC., New York
2. Bozkurt, Y., Ağaç Teknolojisi, İ. Ü., Orman Fakültesi, Yayın No: 3403- 380, İstanbul, 1986
3. Örs, Y,. Özçifçi, A. and Atar, M., “Klebit 303, Kleıberit 305.0 ve Süper Lackleim 308 Tutkallarının Yapısma Dirençleri”, Turk J Agric For 23 (3): 757–761 (1999).
4. Badwin, R. F., Plywood and Veneer-Based Products: Manufacturing Practices, Miller Freeman Inc., San Francisco.
5. Colak, S. Aydın, I. Demirkır, C. and . Colakoğlu, G., “Some Technological Properties of Laminated Veneer Lumber Manufactured from Pine (Pinus sylvestris L.) Veneers with Melamine Added- UF Resins”, Turk J Agric For 28 (1):109-113 (2004)
6. Pizzi, A., “Wood Adhesives”, Chemistry and Technology, Vol. 1., Marcel Dekker, New York, 1993.
7. Cremonini, C. Pizzi, A. and Toro, C., “Improved waterproofing of UF Plywood Adhesives by Melamine Salts as Glue Mix Hardeners: System Performance Optimization”, Holzforschung und Holzverwertung, 49: 11-15 (1997).
8. Cremonini, C. Pizzi, A., “Field Weathering of Plywood Panels Bonded with UF Adhesives and Low Proportions of Melamine Salts”, Holz als Roh-und Werkstoff, 57: 318 (1999).

9. Ors Y. Kama Disli Birlesmeli Masif Agaç Malzemede Mekanik Özellikler, Yardımcı Ders Kitabı, K.T.Ü. Orman Fakültesi, Trabzon, 29–34 (1987).
10. TS 3891. Yapıstırıcılar-Polivinilasetat Emilsiyon, Türk Standartları Enstitüsü; Ankara, 1983.
11. Producer Firm Text, Polisan Dilovası-Gebze, Bolu, Turkey 1999.
12. Colakoğlu, G., “Wood Adhesives”, Karadeniz Technical University, Forest Industry Engineering, 32-58 (1998).
13. Sellers, T., Plwood and Adhesive Technology, Marcel Dekker Inc. Newyork-Basel, s. 661, 1985
14. TS EN 3639 Odun Lifi Levhaları-Sert ve Orta Sert Levhalar Su Emme ve Kalınlığına Şişmenin Tayini, Ankara, 1981.
15. TS 5430.Ağaç Endüstrisinde Kullanılan Yapıştırıcıların Yapıştırma Mukavemetine Göre Sınıflandırılması, Ankara, 1988.
16. TS 4084 Odunda Radyal ve Teğet Doğrultuda Şişmenin Tayini, Ankara, 1983.
17. TS 3634 Odun Lifi Levhaları-Deney Parçası Boyutlarının Ölçülmesi, Ankara, 1981.
18. Rowell, R. M., “Chemistry of Solid Wood”, Advances in Chemistry Series No.207, American Chemical Society, Washington, DC, (1984).