Östemperleme Sıcaklığının Karbür İçermeyen Beynitik Çelik Dökümün Aşınma Davranışı Üzerine Etkisi

Abstract

The objective of this study is to elucidate how the microstructural features and wear performance of carbide-free bainitic cast steel (CFB cast steel) are influenced by the applied austempering temperature. In this scope, the specimens were first subjected to an austenitizing treatment at 900°C for 60 min. Subsequently, for the austempering stage, the samples were held isothermally for 90 min in molten salt baths prepared at four different temperatures: 275°C, 300 °C, 325°C, and 350 °C. Microstructural characterization was carried out using optical microscopy. The volume fraction of retained austenite in the material was determined by X-ray diffraction (XRD). To evaluate the wear behavior, wear tests were performed in accordance with the procedures specified in ASTM G133-22, and the volume loss on the worn surfaces after testing was measured with high precision using an optical profilometer. The results obtained have shown that the austempering temperature plays a determinative role in the microstructure and mechanical properties. The finest microstructure was achieved in the specimen austempered at 275°C for 90 min, whereas the coarsest microstructure was obtained after treatment at 350°C. These microstructural differences were also reflected in the hardness values. The highest hardness (54.9 HRC) was measured in the sample treated at 275 °C, while the lowest hardness (48.2 HRC) was recorded in the specimen austempered at 350 °C. The retained austenite volume fraction exhibited a directly proportional variation with austempering temperature; the lowest fraction (17.5%) was found in the samples treated at 275 °C, and the highest fraction (24.2%) was measured in those processed at 350 °C. The wear test results revealed that the heat treatment significantly improved the wear resistance. The as-cast showed the poorest performance, with a volume loss of 0.3304 mm³ and a wear rate of 1.32 × 10⁻⁴ mm³/N·m. Among the austempered samples, the best wear resistance was observed in the specimen treated at 275 °C. This specimen exhibited the lowest wear rate of 6.68 × 10⁻⁶ mm³/N·m, the minimum volume loss of 0.0167 mm³, and the lowest average coefficient of friction (μ = 0.684). In contrast, the sample austempered at 350 °C displayed the highest wear values, with a wear rate of 1.62 × 10⁻⁵ mm³/N·m, a volume loss of 0.0406 mm³, and an average coefficient of friction of μ = 0.709.

Keywords

• Carbide-free bainitic cast steel
• austempering temperature
• wear behavior
• retained austenite.

Supporting Institution

Gazi University Scientific Research Projects Coordination Unit

Project Number

FYL-2022-8060

Ethical Statement

The authors state no conflict of interest. The authors have accepted responsibility for the entire content of this manuscript and approved its submission. The authors declare that no AI writing tools were used in this paper.

Thanks

We would like to thank the Scientific Research Projects Coordination Unit of Gazi University for supporting this research with project code FYL-2022-8060.

Östemperleme Sıcaklığının Karbür İçermeyen Beynitik Çelik Dökümün Aşınma Davranışı Üzerine Etkisi

Abstract

Bu araştırmanın amacı, karbürsüz beynitik çelik döküm (KİB-ÇD) malzemenin mikroyapısal özellikleri ve aşınma performansının, uygulanan östemperleme sıcaklığından ne şekilde etkilendiğini ortaya koymaktır. Bu kapsamda, numuneler öncelikle 900°C sıcaklıkta 60 dakika süreyle östenitleme işlemine tabi tutulmuştur. Ardından, östemperleme aşaması için 275°C, 300°C, 325°C ve 350°C olmak üzere dört farklı sıcaklıkta hazırlanan tuz banyolarında, her bir numune 90 dakika boyunca izotermal olarak bekletilmiştir. Mikroyapısal karakterizasyon, optik mikroskop kullanılarak gerçekleştirilmiştir. Malzeme yapısındaki kalıntı östenit fazının hacimsel oranı ise X-ışını kırınımı (XRD) tekniği ile tespit edilmiştir. Aşınma davranışının belirlenmesi amacıyla, ASTM G133-22 standardında belirtilen prosedürlere uygun olarak aşınma testleri yapılmış ve test sonrası yüzeylerde meydana gelen hacim kayıpları optik profilometre ile hassas bir şekilde ölçülmüştür. Elde edilen bulgular, östemperleme sıcaklığının mikroyapı ve mekanik özellikler üzerinde belirleyici bir rol oynadığını göstermiştir. En ince taneli mikroyapı, 275°C'de gerçekleştirilen 90 dakikalık östemperleme işlemi sonucunda elde edilirken, en kaba taneli yapıya 350°C'de yapılan işlemle ulaşılmıştır. Bu mikroyapısal farklılıklar, malzemenin sertlik değerlerine de yansımıştır. En yüksek sertlik değeri (54,9 HRC) 275°C'de işlem gören numunede ölçülürken, en düşük sertlik (48,2 HRC) 350°C'de östemperlenen numunede kaydedilmiştir. Kalıntı östenit hacim oranı da östemperleme sıcaklığı ile doğru orantılı bir değişim sergilemiştir; en düşük oran (%17,5) 275°C'de, en yüksek oran (%24,2) ise 350°C'de işlem görmüş numunelerde tespit edilmiştir. Aşınma testi sonuçları, ısıl işlemin aşınma direncini önemli ölçüde iyileştirdiğini ortaya koymuştur. Döküm halindeki numune, 0,3304 mm³'lük hacim kaybı ve 1,32x10⁻⁴ mm³/N.m'lik aşınma hızı ile en zayıf performansı göstermiştir. Östemperlenmiş numuneler arasında ise en üstün aşınma direnci, 275°C'de işlem gören numunede gözlemlenmiştir. Bu numune, 6,68x10⁻⁶ mm³/N.m ile en düşük aşınma hızına, 0,0167 mm³ ile en az hacim kaybına ve μ=0,684 ile en düşük ortalama sürtünme katsayısına sahip olmuştur. Buna karşılık, 350°C'de östemperlenen numune, 1,62x10⁻⁵ mm³/N.m'lik aşınma hızı, 0,0406 mm³'lük hacim kaybı ve μ=0,709'luk sürtünme katsayısı ile en yüksek aşınma değerlerini sergilemiştir.

Keywords

• Karbür içermeyen beynitik çelik döküm
• östemperleme sıcaklığı
• aşınma davranışı
• kalıntı östenit.

Supporting Institution

Gazi Üniversitesi Bilimsel Araştırma Projeleri Koordinasyon Birimi

Project Number

FYL-2022-8060

Ethical Statement

Yazarlar herhangi bir çıkar çatışması olmadığını beyan ederler. Yazarlar bu makalenin tüm içeriğinin sorumluluğunu üstlenmiş ve makalenin yayınlanmasını onaylamışlardır. Yazarlar bu makalede herhangi bir yapay zeka yazma aracı kullanılmadığını beyan ederler.

Thanks

Bu araştırmayı FYL-2022-8060 kodlu projeyle destekleyen Gazi Üniversitesi Bilimsel Araştırma Projeleri Koordinasyon Birimine teşekkür ederiz.

References

1. [1] S. K. Putatunda, Fracture toughness of a high carbon and high silicon steel. Materials Science and Engineering A, 297 (2000) 31-43.
2. [2] S. K. Putatunda, A. V. Singar, R. Tackett, G. Lawes, Development of a high strength high toughness ausferritic steel. Materials Science and Engineering A, 513-514 (2009) 329-339.
3. [3] H. K. D. H. Bhadeshia, D. V. Edmonds, Bainite in silicon steels, new composition property approach. Metal Science, 17: 9 (1983) 420-425.
4. [4] P. V. Moghaddam, On the role of microstructure in wear of nanostructured carbide-free bainitic steels. Doctoral thesis, Luleå University of Technology, Department of Applied Physics and Mechanical Engineering, Division of Machine Elements, Sweden (2020).
5. [5] Ö. F. Murathan, V. Kılıçlı, Nano bainitic steel. Journal of Polytechnic, 19: 2 (2016) 115-128.
6. [6] R. Kumar, R. K. Dwivedi, R. K. Arya, P. Sonia, A. S. Yadav, K. K. Saxena, M. I. Khan, S. B. Moussa, Current development of carbide free bainitic and retained austenite on wear resistance in high silicon steel. Journal of Materials Research and Technology, 24 (2023) 9171-9202.
7. [7] R. Kumar, A. Tripathi, R. K. Dwivedi, R. K. Arya, A. S. Yadav, A. Agarwal, Influence of austempering temperature on carbide free bainite development, a critical review. Journal of Physics: Conference Series, 2484 (2023) 012029.
8. [8] C. S. Brown, J. G. Speer, E. D. Moor, Influence of retained austenite on abrasive wear performance of bainitic steels. Wear, 522 (2023) 204720.

9. [9] B. Liu, W. Li, X. Lu, X. Jia, X. JinLiu, The effect of retained austenite stability on impact-abrasion wear resistance in carbide-free bainitic steels. Wear, 428-429 (2019) 127-136.
10. [10] A. M. Gola, M. Ghadamgahi, S. W. Ooi, Microstructure evolution of carbide-free bainitic steels under abrasive wear conditions. Wear, 376-377 (2017) 975-982.
11. [11] P. V. Moghaddam, J. Hardell, E. Vuorinen, B. Prakash, The role of retained austenite in dry rolling/sliding wear of nanostructured carbide-free bainitic steels. Wear, 428-429 (2019) 193-204.
12. [12] A. D. Basso, I. Toda-Caraballo, A. Eres-Castellanos, D. San-Martin, J. A. Jimenez, F. G. Caballero, Effect of microsegregation and bainitic reaction temperature on the microstructure and mechanical properties of a high-carbon and high-silicon cast steel. Metals, 11: 2 (2021) 220-251.
13. [13] O. Haiko, S. Pallaspuro, V. Javaheri, P. Kaikkonen, S. Ghosh, K. Valtonen, A. Kaijalainen, J. Kömi, High-stress abrasive wear performance of medium-carbon direct-quenched and partitioned, carbide-free bainitic, and martensitic steels. Wear, 526-527 (2023) 204925.
14. [14] V. G. Efremenko, O. Hesse, Th. Friedrich, M. Kunert, M. N. Brykov, K. Shimizu, V. I. Zurnadzhi, P. Šuchmann, Two-body abrasion resistance of high-carbon high-silicon steel metastable austenite vs nanostructured bainite. Wear, 418-419 (2019) 24-35.
15. [15] S. Das Bakshi, P. H. Shipway, H. K. D. H. Bhadeshia, Three-body abrasive wear of fine pearlite, nanostructured bainite and martensite. Wear, 308: 1-2 (2013) 46-53.
16. [16] S. K. Md. Hasan, D. Chakrabarti, S. B. Singh, Dry rolling/sliding wear behaviour of pearlitic rail and newly developed carbide-free bainitic rail steels. Wear, 408-409 (2018) 151-159.
17. [17] J. P. Liu, Y. Q. Li, Q. Y. Zhou, Y. H. Zhang, Y. Hu, L. B. Shi, W. J. Wang, F. S. Liu, S. B. Zhou, C. H. Tian, New insight into the dry rolling-sliding wear mechanism of carbide-free bainitic and pearlitic steel. Wear, 432-433 (2019) 202943.
18. [18] S. Sharma, A. Tripathi, R. K. Dwivedi, R. Kumar, A. Agarwal, A critical review on wear and corrosion of carbide free bainitic steel. IOP Conference Series: Materials Science and Engineering, 1136: 1 (2021) 012027.
19. [19] R. Kumar, R. K. Dwivedi, S. Ahmed, Stability of retained austenite in carbide free bainite during the austempering temperature and its influence on sliding wear of high silicon steel. Silicon, 13: 4 (2021) 1249-1259.
20. [20] ASTM E975-22, Standard practice for X-ray determination of retained austenite in steel with near random crystallographic orientation. ASTM International (2025). (https://www.astm.org/e0975-22.html).
21. [21] ASTM G133-22, Standard test method for linearly reciprocating ball-on-flat sliding wear. ASTM International (2025). (https://www.astm.org/standards/G133).
22. [22] N. E. Tenaglia, J. M. Massone, A. D. Basso, R. E. Boeri, Influence of the austempering time on the mechanical properties of carbide-free bainitic cast steels. International Journal of Metalcasting, 15: 3 (2020) 906-915.
23. [23] N. E. Tenaglia, R. E. Boeri, A. D. Basso, J. M. Massone, Macro and microstructural characterisation of high Si cast steels, study of microsegregation patterns. International Journal of Cast Metals Research, 30: 2 (2017) 103-111.
24. [24] P. V. Moghaddam, J. Hardell, E. Vuorinen, B. Prakash, Effect of retained austenite on adhesion-dominated wear of nanostructured carbide-free bainitic steel. Tribology International, 150 (2020) 106348.
25. [25] N. E. Tenaglia, R. E. Boeri, J. M. Massone, A. D. Basso, Assessment of the austemperability of high-silicon cast steels through Jominy hardenability tests. Materials Science and Technology, 34: 16 (2018) 1990-2000.
26. [26] A. Basso, I. Toda-Caraballo, D. San-Martín, F. G. Caballero, Influence of cast part size on macro and microsegregation patterns in a high carbon high silicon steel. Journal of Materials Research and Technology, 9: 3 (2020) 3013-3025.
27. [27] X. Chen, E. Vuorinen, In situ X-ray observation of bainitic transformation of austempered silicon alloyed steel. Journal of Materials Research, 24: 4 (2009) 1559-1566.
28. [28] N. E. Tenaglia, R. E. Boeri, J. M. Massone, A. D. Basso, Assessment of the austemperability of high-silicon cast steels through Jominy hardenability tests. Materials Science and Technology, 34: 16 (2018) 1990-2000.
29. [29] N. E. Tenaglia, J. Massone, A. Basso, R. Boeri, Development of ultra-high strength carbide-free bainitic cast steels. International Journal of Cast Metals Research, 33: 6 (2020) 258-265.
30. [30] M. Franceschi, C. Soffritti, A. Fortini, L. Pezzato, G. L. Garagnani, M. Manuele Dabal, Evaluation of wear resistance of a novel carbide-free bainitic steel. Tribology International, 178 (2023) 108071.
31. [31] P. V. Moghaddam, J. Hardell, E. Vuorinen, B. Prakash, Dry sliding wear of nanostructured carbide-free bainitic steels, effect of oxidation-dominated wear. Wear, 454-455 (2020) 203317.
32. [32] P. V. Moghaddam, J. Hardell, E. Vuorinen, B. Prakash, Effect of retained austenite on adhesion-dominated wear of nanostructured carbide-free bainitic steel. Tribology International, 150 (2020) 106348.
33. [33] X. Chen, Y. Li, Microstructure and mechanical properties of a new type of austempered boron alloyed high silicon cast steel. International Journal of Metalcasting, 10 (2020) 155-161.
34. [34] A. F. Santacruz-Londoño, O. Rios-Diez, J. A. Jiménez, C. Garcia-Mateo, R. Aristizábal-Sierra, Microstructural and mechanical characterization of a nanostructured bainitic cast steel. Metals, 10: 5 (2020) 612.
35. [35] A. D. Basso, I. Toda-Caraballo, A. Eres-Castellanos, D. San-Martin, J. A. Jimenez, F. G. Caballero, Effect of the microsegregation on martensitic and bainitic reactions in a high carbon-high silicon cast steel. Metals, 10: 5 (2020) 574-601.
36. [36] M. Franceschi, L. Pezzato, C. Gennari, A. Fabrizi, M. Polyakova, D. Konstantinov, K. Brunelli, M. Dabalà, Effect of intercritical annealing and austempering on the microstructure and mechanical properties of a high silicon manganese steel. Metals, 10: 11 (2020) 1148.
37. [37] A. Leiro, E. Vuorinen, K. G. Sundin, B. Prakash, T. Sourmail, V. Smanio, F. G. Caballero, C. Garcia-Mateo, R. Elvira, Wear of nano-structured carbide-free bainitic steels under dry rolling-sliding conditions. Wear, 298-299 (2013) 42-47.
38. [38] E. Wang., Q. He, C. Gu., Y. Wang. (2023). Effect of austempering temperature on microstructure evolution, mechanical properties and wear resistance of carbon-free nano-bainite steel. Journal of materials research and technology, 26, 6703-6718.