Investigation of the Use of Sludge from Cement Industry for Brick Manufacture

Year 1998, Volume: 37 Issue: 1, 27 - 34, 01.03.1998

Oktay Bayat Belgin Bayat

Abstract

Five different levels of sludge from Adana Cement Industry was added to brick making clay and fired at the furnaces of brick plant for five days at the temperatures ranged from 850 °C to 900 °C. Physical properties of the produced bricks were determined. The bricks were tested for total weight change and shrinkage, cold water absorption, density after firing and compressive strength according to TS 705 and the results were assessed in comparison with reference bricks. The use of sludge in brick up to 20% by weight meets with the TS 705 standard specifications

ÇİMENTO SANAYİ ATIKSU ARITMA ÇAMURUNUN TUĞLA ÜRETİMİNDE KULLANIMININ ARAŞTIRILMASI

Abstract

Adana Çimento Sanayi atıksu arıtma çamuru beş farklı oranda tuğla kiline katılarak tuğla fabrikasında beş gün boyunca 850-900 °C'de pişirilmiştir. Elde edilen tuğla örneklerinin fiziksel özellikleri belirlenmiştir. Tuğla örneklerinin TS 705'e göre toplam küçülme, su emme, kızdırma kaybı, birim ağırlık ve basma dayanımları tespit edilmiş ve sonuçlar referans tuğla örnekleri ile mukayese edilmiştir. Atıksu arıtma çamurunun tuğla içinde maksimum ağırlıkça %20 oranına kadar kullanılması halinde üretilen tuğlaların TS 705'de belirtilen fabrika tuğlası standardına uygun olduğu belirlenmiştir

Keywords

Çimento, Tuğla, Atıksu, Atıksu Arıtma Çamuru, Atık Değerlendirme