THE EFFECT OF HOT PRESSİNG PRESSURE TO PRODUCTİON OF Al BASED METALLİC FOAMS BY HOT PRESSİNG METHODS

Year 2012, Volume: 1 Issue: 4, 14 - 19, 01.11.2012

Halil Karakoça Hanifi Çinicib Ramazan Çıtakc

Abstract

In this study, Alumix 231 and 1% titanium hydrate (TiH2) powders were mixed. Compressing the mixture of powders was carried out in two steps. Firstly, powders are compressed at 50 MPa at room temperature. Secondly, the constant temperature (450 ˚C) and at different pressures (100,200,300 MPa) for a period of 30 minutes was then subjected to hot pressing. After compression specimens have been made famable tablets. Samples obtained from the foamable tablets subjected to the process of foaming temperature of 690 ˚C so Al-based metallic foams were produced. Produced metallic foams pressing pressure were studied on the foaming behavior

Keywords

Aluminum Foam, Alumix 231, B4C, Foaming Behaviour

SICAK PRESLEME YÖNTEMİ İLE AL ESASLI METALİK KÖPÜK ÜRETİMİNE PRESLEME BASINCININ ETKİLER

Abstract

Bu çalışmada ön alaşımlı Alumix 231 tozu içerisine, % 1 oranında TiH2 ilave edilerek karıştırılmıştır. Karışım tozlar önce 50 MPa basınç altında soğuk olarak sıkıştırıldıktan sonra sabit sıcaklıkta (450 oC), farklı basınçlarda (100,200,300 MPa) tek yönlü preste 30 dakika süre ile sıkıştırılmıştır. Sıkıştırma sonrası numuneler köpürebilir tablet haline getirilmiştir. Elde edilen toz tablet numuneler 690˚C sıcaklıkta köpürtme işlemine tabi tutularak Al esaslı metalik köpükler üretilmiştir. Üretilen metalik köpüklerde presleme basıncının köpürme davranışı üzerine etkileri araştırılmıştır

Keywords

Alüminyum Köpük, Alumix 231, Sıcak Presleme, Köpürme Davranışı