Abstract
In this aim study, determineted of effect positive and negatife of amount SiC at microsstructure and Al/SiC metal foam. For this aim, pure Al foams manufactured 99% pure Al powder with an average dimension of 60 µm to added with 0,5% and 1% proportions TiH2. Temperature to become foams 6500C was selected. After to fix of suitable TiH2, Al/TiH2/SiC metal foams was produced with to added 5 and 10% SiC in weight percent ceramic powder. Metal foams were examined with optic microscopy and SEM, and then the mixture proportions for this metal foam were determined. In order to avoid open cell formation, matrix rate should be increased or reinforced rate should be decreased in main composite.
Keywords
Abstract
Bu çalışmanın amacı; Al/SiC metal köpüğü ve mikroyapısına SiC miktarının olumlu ve olumsuz etkisinin belirlenmesidir. Bu amaç için ortalama 60 µm tane boyutuna sahip %99 saflıktaki Al tozuna %0,5 ve %1 oranlarında TiH2 eklenerek saf alüminyum köpükler elde edildi. Köpükleşme sıcaklığı olarak 6500C seçildi. Uygun TiH2 oranı tespit edildikten sonra ağırlıkça %5 ve %10'luk SiC seramik tozları ilave edilerek Al/TiH2/SiC metal köpükler üretildi. Üretilen metal köpüklerin optik mikroskop ve SEM fotoğraflarının mikroyapı incelemeleri yapılarak uygun karışım oranı belirlendi. Burada; açık hücreli yapıdan kaçınmak için, matris oranı artırılmalı veya takviye oranı azaltılmalıdır.
Keywords
Details
| Primary Language | Turkish |
|---|---|
| Journal Section | Electrical Machines |
| Authors | |
| Publication Date | April 1, 2008 |
| Published in Issue | Year 2008 Volume: 3 Issue: 3 |