MICROSTRUCTURE AND PRODUCED OF Al/SiC METAL FOAMS

Yıl 2008, Cilt 3, Sayı 3, 530 - 537, 01.04.2008

Öz

In this aim study, determineted of effect positive and negatife of amount SiC at microsstructure and Al/SiC metal foam. For this aim, pure Al foams manufactured 99% pure Al powder with an average dimension of 60 µm to added with 0,5% and 1% proportions TiH2. Temperature to become foams 6500C was selected. After to fix of suitable TiH2, Al/TiH2/SiC metal foams was produced with to added 5 and 10% SiC in weight percent ceramic powder. Metal foams were examined with optic microscopy and SEM, and then the mixture proportions for this metal foam were determined. In order to avoid open cell formation, matrix rate should be increased or reinforced rate should be decreased in main composite.

Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI

Yıl 2008, Cilt 3, Sayı 3, 530 - 537, 01.04.2008

Öz

Bu çalışmanın amacı; Al/SiC metal köpüğü ve mikroyapısına SiC miktarının olumlu ve olumsuz etkisinin belirlenmesidir. Bu amaç için ortalama 60 µm tane boyutuna sahip %99 saflıktaki Al tozuna %0,5 ve %1 oranlarında TiH2 eklenerek saf alüminyum köpükler elde edildi. Köpükleşme sıcaklığı olarak 6500C seçildi. Uygun TiH2 oranı tespit edildikten sonra ağırlıkça %5 ve %10'luk SiC seramik tozları ilave edilerek Al/TiH2/SiC metal köpükler üretildi. Üretilen metal köpüklerin optik mikroskop ve SEM fotoğraflarının mikroyapı incelemeleri yapılarak uygun karışım oranı belirlendi. Burada; açık hücreli yapıdan kaçınmak için, matris oranı artırılmalı veya takviye oranı azaltılmalıdır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Elektrik Makinaları
Yazarlar

Ayhan ORHAN Bu kişi benim

Yayımlanma Tarihi 1 Nisan 2008
Yayınlandığı Sayı Yıl 2008, Cilt 3, Sayı 3

Kaynak Göster

Bibtex @ { nwsatecapsci213988, journal = {Technological Applied Sciences}, eissn = {1308-7223}, address = {}, publisher = {E-Journal of New World Sciences Academy}, year = {2008}, volume = {3}, number = {3}, pages = {530 - 537}, doi = {10.12739/10.12739}, title = {Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI}, key = {cite}, author = {Orhan, Ayhan} }
APA Orhan, A. (2008). Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI . Technological Applied Sciences , 3 (3) , 530-537 . Retrieved from https://dergipark.org.tr/tr/pub/nwsatecapsci/issue/20187/213988
MLA Orhan, A. "Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI" . Technological Applied Sciences 3 (2008 ): 530-537 <https://dergipark.org.tr/tr/pub/nwsatecapsci/issue/20187/213988>
Chicago Orhan, A. "Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI". Technological Applied Sciences 3 (2008 ): 530-537
RIS TY - JOUR T1 - Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI AU - Ayhan Orhan Y1 - 2008 PY - 2008 N1 - DO - T2 - Technological Applied Sciences JF - Journal JO - JOR SP - 530 EP - 537 VL - 3 IS - 3 SN - -1308-7223 M3 - UR - Y2 - 2022 ER -
EndNote %0 Technological Applied Sciences Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI %A Ayhan Orhan %T Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI %D 2008 %J Technological Applied Sciences %P -1308-7223 %V 3 %N 3 %R %U
ISNAD Orhan, Ayhan . "Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI". Technological Applied Sciences 3 / 3 (Nisan 2008): 530-537 .
AMA Orhan A. Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI. NWSA. 2008; 3(3): 530-537.
Vancouver Orhan A. Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI. Technological Applied Sciences. 2008; 3(3): 530-537.
IEEE A. Orhan , "Al/SiC METAL KÖPÜKLERİN ÜRETİMİ ve MİKROYAPISI", Technological Applied Sciences, c. 3, sayı. 3, ss. 530-537, Nis. 2008, doi:10.12739/10.12739