EFFECTS OF EDGE COVERING ON TENSILE STRENGTH OF MDF

Year 1999, Volume: 5 Issue: 3, 1173 - 1177, 01.03.1999

Yalçın Örs Musa Atar Ayhan Özçifçi

https://izlik.org/JA74AR97WF

Abstract

Dowels, 6, 8 and 10 mm ? diameters were bonded with PVAc adhesive on Medium Density Fiberboard (MDF). Edges were covered with 5, 8 and 12 mm beech wood materials, drilled 25 mm depth. Tensile strength measurments were made on the samples. The highest tensile strength value was given as 6 mm ? dowel and MDF covered with 8 mm thickness beech wood material (2.294 N/mm2), the lowest value was obtained with 10 mm ? dowel and with unprocessed MDF (1.314 N/mm2).

Keywords

MDF , Dowel , Tensile strength , PVAc

KENARLARI MASİFLİ VE MASİFSİZ MDF LEVHALARINDA KAVELA ÇAPLARININ ÇEKME DİRENCİNE ETKİLERİ

https://izlik.org/JA74AR97WF

Abstract

Bu çalışmada, kenarları 5, 8 ve 12 mm kalınlığında kayın masif malzeme ile masiflenmiş ve masiflenmemiş orta yoğunlukta lif levha (MDF) deney örneklerine 6, 8 ve 10 mm çapındaki kavelalar, 25 mm derinlikte delikler açılarak PVAc tutkalı ile yapıştırılmıştır. Hazırlanan örneklere aynı amaçla yapılmış bir çalışma örnek alınarak çekme deneyi uygulanmış ve kavela çapı ile masif malzeme kalınlığının kavela çekme direncine etkileri araştırılmıştır. Sonuç olarak kavela çekme direnci; en yüksek ? 6 mm kavela ve 8 mm kalınlıkta masifli MDF?de (2.294 N/mm 2 ), en düşük ?10 mm kavela ve masifsiz MDF?de (1.314 N/mm 2 ) gerçekleşmiştir.

Keywords

MDF , Çekme direnci , Kavela , Kenar masifleme , PVAc