FIRE RESISTANCE OF DOUGLAS FIR [Pseudotsuga menziesii (Mirb.) Franco] WOOD TREATED WITH SOME CHEMICALS

Year 1998, Volume: 4 Issue: 2, 613 - 624, 01.02.1998

M. Kemal Yalınkılıç Zafer Demirci Ergün Baysal

https://izlik.org/JA55UH54XC

Abstract

Combustible properties of treated douglas wood specimens and fire-retardancy of some preservatives were tested in this study. Crib test of ASTM E 160-150 was followed. Results indicated that, aqueous solutions of boric acid (BA), borax (Bx) (Na2BO7 10H2O) or BA + Bx mixture (7: 3, w: w) had fire retardant efficacy (FRE) over untreated wood and reduced the combustibility of vinil monomers (Styrene and methylmetacrylate) which were applied as secondary treatment.

Keywords

Fire , Boron , Fire-retardant effect , Impregnation , Douglas wood

ÇEŞİTLİ EMPRENYE MADDELERİNİN DUGLAS [Pseudotsuga menziesii (Mirb.) Franco] ODUNUNUN YANMA ÖZELLİKLERİ ÜZERİNE ETKİLERİ

https://izlik.org/JA55UH54XC

Abstract

Odunun biyotik ve abiyotik zararlılarına karşı korunması amacıyla kullanıma konu oluşturan çeşitli emprenye maddelerinin duglas odununda yanma özelliklerini ne ölçüde etkilediği bu çalışmada ele alınmıştır. Sonuçlar, borlu bileşiklerin sulu çözeltilerinin önemli derecede yanmayı önleyici etki (YÖE) gösterdiğini, polietilenglikol (PEG)- 400'de çözündürülen borik asit + boraks (BA + Bx)'ın (7: 3, ağırlık: ağırlık) YÖE'de bulunmadığını ortaya koymuştur. Yanmayı artırıcı etkileri bilinen çeşitli su itici maddelerin (SİM) ise borlu bileşiklerle emprenyeli oduna ikinci bir işlem olarak uygulanmaları durumunda yanmada oluşturdukları olumsuz etki azaltılabilmiştir. Öte yandan BA ve Bx'ın YÖE'leri bu maddelerin karışım halinde birlikte kullanılmaları durumunda iyileşmektedir. Borlu bileşiklerin çeşitli yanma özellikleri bakımından fosforik asit (FA), monoamonyum fosfat (MAP) ve Pyresote (Pyr) ile rekabet edebilecek nitelikte olduğu gözlenmiştir.

Keywords

Yangın , Bor , Emprenye , Yanmayı önleyici etki , Duglas odunu