IMPORTANT DEGRADATIONS IN POLYETHYLENE TERAPHTALATE EXTRUSION PROCESS

Year 2003, Volume: 9 Issue: 1, 89 - 93, 01.01.2003

Şule Altun Yusuf Ulcay

Abstract

Polyethylene terephthalate (PET) is one of the most used thermo-plastic polymers. The total consumption of PET has been about 30 million tons in the year 2000. Polyester fibers constitute about 60 % of total synthetic fibers consumption. During extrusion, PET polymer is faced to thermal, thermo-oxidative and hydrolytic degradation, which result in severe reduction in its molecular weight, thereby adversely affecting its subsequent melt processability. Therefore, it is essential to understand degradation processes of PET during melt extrusion.

Keywords

Degradation, PET fiber spinning, Extrusion

POLİETİLEN TERAFTALAT (PET) POLİMERİNDE EKSTRUDER İÇERİSİNDE ÖNEMLİ OLAN BOZUNMALAR

Abstract

Bu makalede, Türkiye'de ve dünyada en fazla üretilen sentetik lif olan polietilen teraftalat (PET) lifinde ekstruder içerisinde meydana gelen bozunmalar anlatılmıştır. Önce, PET polimerinde görülen bozunmalardan söz edilmiş, daha sonra ekstruder içerisinde gerçekleşen bozunmalar üzerinde durulmuştur. Sonuç bölümünde de ekstruder içerisinde meydana gelen bozunmaların, ürün özellikleri üzerindeki etkilerinden söz edilmiştir.

Keywords

Bozunma, PET lif üretimi, Ektsrüzasyon