A COMPARATIVE STUDY ON THE STRESS INTENSITY FACTOR OF CARBON EPOXY COMPOSITE PLATES HAVING CENTRAL HOLES

Year 2000, Volume: 6 Issue: 2, 109 - 112, 01.02.2000

M. Hüsnü Dirikolu Alaattin Aktaş

Abstract

In this paper, a comparative study regarding the determination of stress intensity factors (SIF) for non-standard thin composite plates is presented. Carbon-Epoxy composite plates are considered for the study. Unnotched specimens and specimens containing either 4, 6, or 8 mm dia. holes are prepared and then tested. Based on the experimental data thus obtained, two analytical approaches and a finite element fracture analysis tool called FRANC have been used to compare the critical SIF values for this composite material.

Keywords

Stress intensity factor, Fracture, Crack, Composite, Carbon epoxy

DELİKLİ KARBON-EPOKSİ PLAKALARIN GERİLME ŞİDDETİ FAKTÖRLERİ ÜZERİNDE KARŞILAŞTIRMALI BİR ÇALIŞMA

Abstract

Makalede standart olmayan ince kompozit levhaların gerilme şiddeti faktörlerinin (GŞF) hesaplanmasıyla ilgili karşılaştırmalı bir çalışma sunulmaktadır. Çalışmada Karbon-Epoksi kompozit levhalar kullanılmıştır. Çentiksiz ve üzerinde 4, 6 veya 8 mm çapında delik bulunan deney numuneleri hazırlanıp test edilmiştir. Elde edilen deney sonuçlarına dayanarak, iki analitik yaklaşım ve FRANC-sonlu elemanlar programı kullanılarak kompozitin kritik GŞF'leri hesaplanıp karşılaştırmalar yapılmıştır.

Keywords

Gerilme şiddeti faktörü, Kırılma, Çatlak, Kompozit, Karbon epoksi