Manufacturing methods and the applied heat treatment are important for the properties of materials. Building safe constructions with the materials used depends on the knowledge and correct use of their properties. In this study, cold drawn bar specimens of Ç1040 are heat treated in three different temperatures (500 o C, 650 o C, 840 o C) and the strength, hardness, and strain values are compared with those of untreated materials. Cold drawn bars has shown higher strength values when compared with the hot rolled bars. This is because of the type of process selected for manufacturing. By heat treatment, strain has increased, hardness and strength have decreased. It has been observed that the rate of increasing or decreasing depends on the temperature and duration of the heat treatment.
Keywords
Abstract
Malzemelerin özelliklerinde, imalat usulleri ve yapılan ısıl işlemler önemli olmaktadır. Makine konstrüksiyonunda, kullanılan malzemelerle emniyetli konstrüksiyon oluşturmak, bu özelliklerin bilinmesi ve doğru kullanılmasına bağlıdır. Bu çalışmada; soğuk çekme çubuklarından Ç1040 numunesine, üç farklı sıcaklıkta (500 o C, 650 o C, 840 o C) ısıl işlem uygulanmış ve ısıl işlem uygulanmamış ( 25 o C'deki ) numunelerle mukavemet, sertlik ve % uzama değerleri karşılaştırılmıştır. Soğuk çekme çubukları, sıcak haddelenmiş çubuklara oranla daha fazla mukavemet değerleri göstermiştir. Bunun sebebi imalatta seçilen işlem türüdür. Isıl işlem ile sertlik, mukavemet değerleri azalmış, süneklik (% uzama değerleri) artmıştır. Artış ve azalış oranının, uygulanan ısıl işlem sıcaklığına göre değiştiği görülmüştür.
Keywords
Details
| Primary Language | Turkish |
|---|---|
| Journal Section | Research Article |
| Authors | |
| Publication Date | February 1, 1999 |
| Published in Issue | Year 1999 Volume: 5 Issue: 2 |