DECREASING HEAT TREATMENT COST OF SURFACE HARDENED MACHINE PARTS BY CASE CARBURIZATION

Year 1997, Volume: 3 Issue: 3, 429 - 433, 01.03.1997

Abstract

Machine parts are surface hardened to increase fatigue strength and wear resistance. Carburization is the most common surface hardening process in practice. In order to have optimum properties, a machine part must have certain hardness depth. To obtain required hardness depth, the parts must be kept in a carburizing medium at certain temperature for certain time. As the time and temperature is increased hardness depth increases. In practice, carburization temperature is about 930 °C. Machine parts are kept at this temperature for required time depending on required hardness depth. The increase of temperature reduces treatment time, considerably. But, heat treaters do not tend to use high temperatures due to the concern of distortion of parts, and deterioration of mechanical properties. In this study, the increase of temperature for reducing carburization time in salt bath, and consequently change of mechanical properties have been investigated using DIN C20 case carburization steel. As a result of experiments, it was found that mechanical properties were not effected negatively.

KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI

Year 1997, Volume: 3 Issue: 3, 429 - 433, 01.03.1997

Abstract

Hareket eden makina parçalarının pek çoğu, aşınmasının azaltılması ve yorulma mukavemetinin arttırılması için yüzey sertleştirme işlemlerine tabi tutulmaktadır. Makina parçasının optimum özelliklerde olabilmesi için belirli bir sertlik derinliğine sahip olması gerekir. Gerekli sertlik derinliğinin elde edilmesi, karbürizasyon ortamında belirli bir sıcaklıkta belirli bir süre bekletilmekle olur. Sıcaklık ve süre artarken sertlik derinliği de artmaktadır. Pratikte karbürizasyon 930 °C civarında yapılmaktadır. Bu sıcaklıkta makina parçaları istenilen sertlik derinliğine göre belirli bir süre bekletilir. Halbuki sıcaklığın arttırılması, süreyi önemli miktarda azaltmaktadır. Fakat ısıl işlemciler parçanın çarpılması, mekanik özelliklerinin zayıflaması vs. gibi nedenlerden dolayı daha yüksek sıcaklıklara çıkmamaktadırlar. Bu çalışmada, DIN C20 karbürizasyon çeliği kullanılarak, tuz banyolarında karbürizasyon süresinin kısaltılması için sıcaklığın artırılması ve bunun neticesi mekanik özelliklerdeki değişmeler araştırılmıştır. Deneyler neticesi mekanik özelliklerin olumsuz yönde etkilenmedikleri görülmüştür.

There are 0 citations in total.

Details

Primary Language Turkish
Journal Section Research Article
Authors

Ahmet Çetin Can This is me

Ali Rıza Tarakcılar This is me

Yılmaz Özmen This is me

Publication Date March 1, 1997
Published in Issue Year 1997 Volume: 3 Issue: 3

Cite

APA Can, A. Ç. ., Tarakcılar, A. R. ., & Özmen, Y. . (1997). KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi, 3(3), 429-433.
AMA Can AÇ, Tarakcılar AR, Özmen Y. KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi. March 1997;3(3):429-433.
Chicago Can, Ahmet Çetin, Ali Rıza Tarakcılar, and Yılmaz Özmen. “KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI”. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi 3, no. 3 (March 1997): 429-33.
EndNote Can AÇ, Tarakcılar AR, Özmen Y (March 1, 1997) KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi 3 3 429–433.
IEEE A. Ç. . Can, A. R. . Tarakcılar, and Y. . Özmen, “KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI”, Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi, vol. 3, no. 3, pp. 429–433, 1997.
ISNAD Can, Ahmet Çetin et al. “KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI”. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi 3/3 (March 1997), 429-433.
JAMA Can AÇ, Tarakcılar AR, Özmen Y. KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi. 1997;3:429–433.
MLA Can, Ahmet Çetin et al. “KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI”. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi, vol. 3, no. 3, 1997, pp. 429-33.
Vancouver Can AÇ, Tarakcılar AR, Özmen Y. KARBÜRİZASYONLA YÜZEYİ SERTLEŞTİRİLEN MAKİNA PARÇALARININ ISIL İŞLEM MALİYETLERİNİN AZALTILMASI. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi. 1997;3(3):429-33.

ESCI_LOGO.png    image001.gif    image002.gif        image003.gif     image004.gif