The Effect of Cooling Rate on Microstructure and Mechanical Properties of Al-Mg-Si (6063) Alloy

Year 2015, Volume: 21 Issue: 1, 11 - 14, 23.02.2015

Mustafa Türkmen , Oğuzhan Akdemir Yusuf Taşpınar Murat Yıldız Süleyman Gündüz

Abstract

In this study, the effect of cooling rate on microstructure and mechanical properties of Al-Mg-Si (6063) alloys was investigated. In order to obtain different cooling rate, samples heat treated at 520 oC for 2 h and then cooled in furnace, sand, air, oil and water environments. A decrease in the cooling rate caused the growth of grains and precipitates as the strength of Al-Mg-Si alloys reduced. As a result, Al-Mg-Si alloy was found to change significantly the properties of strength and forming depending on the cooling conditions.

Keywords

Aluminium alloy, Cooling rate, Mechanical properties

Al-Mg-Si Alaşımının Mikroyapı ve Mekanik Özelliklerine Soğuma Hızının Etkisi

Abstract

Bu çalışmada, soğuma hızının Al-Mg-Si (6063) alaşımından elde edilen numunelerin mikroyapı ve mekanik özelliklerine etkisi deneysel olarak araştırılmıştır. Farklı soğuma hızı elde edebilmek için numuneler 520 °C’de 2 saat solüsyona alındıktan sonra fırın, kum, hava, yağ ve su ortamlarında soğutulmuşlardır. Soğuma hızının düşmesi tane ve çökeltilerin büyümesine neden olarak Al-Mg-Si alaşımının dayanımını düşürmüştür. Çalışma sonucunda soğuma şartlarına bağlı olarak Al-Mg-Si alaşımının dayanım ve şekillenebilme özelliklerinde belirgin bir değişme olduğu tespit edilmiştir.

Keywords

Anahtar Mekanik özellikler kelimeler

References

• Altenpohl DG. Aluminum Technology, Applications and Environment, A Profile of a Modern Metal. 6th ed. NYS, USA, Wiley, 1998.
• Troeger LP, Starke EA. “Microstructural and Mechanical Characterization of a Superplastic 6xxx Aluminum Alloy”. Materials Science and Engineering: A, 277(1-2), 102-113, 2000.
• Helby M. “Aluminium Extrusion”. A Flexible Approach Construction Mater World”. 1, 101–102, 1993.
• Sun Y. Wear Behavior of Heat Treatable Aluminium Alloys. MSc Thesis, İstanbul Technical University, İstanbul, Turkey, 1998. [5] Şendeniz M. Seçilen Bir Al-Mg-Si Alaşımının (AlMgSi0.5: Değişimlerinin İncelenmesi. Yüksek Lisans Tezi, Uludağ Üniversitesi, Bursa, Türkiye, 2006. Özellik
• Siddiqui RA, Abdullah HA. “Influence of aging Parametres on the Mechanical Properties of 6063 Aluminium Alloy”. Journal of Materials Processing Technology, 102, 234-240, 2000.
• Gavgali M, Totik Y, Sadeler R. “The Effect of Artificial Aging on Wear Properties of AA 6063 Alloy”. Materials Letters, 57(24-25), 3713-3721, 2003.
• Rafiq AS, Hussein AA, Khamis RA. “Infuence of Aging Parameters on the Mechanical Properties of 6063 Aluminium Alloy”. Journal of Materials Processing Technology, 102, 234-240, 2000.
• Meyveci A. Yaşlandırılmış 2XXX ve 6XXX Serisi Alüminyum Alaşımlarının Aşınma Davranışlarının İncelenmesi. Yüksek Lisans Tezi, Karabük Üniversitesi, Karabük, Türkiye, 2007.
• Gündüz S. “Kimyasal Bileşim ve Soğuma Hızının Arayer Atomu İçermeyen Mikroalaşım Çeliklerinin Mekanik Özelliklerine Etkisi”. Gazi Üniversitesi Fen Bilimleri Enstitüsü Dergisi, 16(1), 171–178, 2003.
• Gündüz G, Kaçar R. "Strengthening of 6063 Aluminium Alloy 46(6), 345-350, 2008. Kovove Materialy,
• Güleryüz K, Kaçar R. “Deformasyon Yaşlanmasının AA7075 Alüminyum Alaşımının Mekanik Özelliklerine Etkisinin İncelenmesi”. 6th International Advanced Technologies Symposium (IATS’11), Elazığ, Türkiye, 16-18 May 2011.