Comparative Evaluation of Colour Stability and Translucency Parameter of Different Microhybrid Composite Resin Materials: An in Vitro Study

Year 2024, , 17 - 22, 26.04.2024

Yeşim Turan , Güler Burcu Senirkentli , Ezgi Sonkaya , Volkan Ciftci , Eda Çakmak

https://doi.org/10.15311/selcukdentj.1193448

Abstract

Background: The aim of this study is to compare discoloration and translucency parameters changes of coffee and distilled water immersions on different microhybrid composite resins.
Methods: 60 disks (20 samples from each material) were prepared from three different composites [G-eanial Anterior (GC, Japan), Filtek Z250 (3M, USA) and a newly developed material universal composite Dolgunn (Himg, Turkey)]. Half of the samples were stored in distilled water and the other half in coffee solution. For color stability; the measurements were conducted at baseline, after 1st and 4th weeks and for transluceny parameter (TP); after 1st and 4th week by a spectrophotometer. The mean discoloration value of L*, a*, b* parameters was applied to the CIEDE2000 formula. For discoloration parameter; color difference values (ΔE00) and whereas for TP; translucency parameter values (TP00) were calculated. The assumption of sphericity was assessed by Mauchly's W test. For the analysis of repeated measurements, two-way analysis of variance and for multiple correlations LSD tests were used (p<0.05).
Results: Significant discoloration (ΔE00: 3.45-7.93) was observed after 1 and 4 weeks of coffee immersion. The highest color change observed in Dolgunn group (p<0.001; p=0.001). There were no significant difference in TP values of the composites in coffee and control group (F=1.821 p=0.181; F=0.191 p=0.828).
Conclusion: The results of our study concluded that structural properties of the composite materials such as content and composition were important components in color stability when exposed to discoloration contents, however there was no significant change in the transluceny parameter.
Keywords: Color stability; Composite resin; Translucency parameter.
Sorumlu

Keywords

Colos stability, Composite Resin, Translucency parameter

Ethical Statement

This article is not the version of a presentation. This article has not been prepared on the basis of a master’s/ doctoral thesis. It is declared that during the preparation process of this study, scientific and ethical principles were followed and all the studies benefited are stated in the bibliography.

Project Number

Proje no: D-DA22/02

Farklı Mikrohibrit Kompozitlerin Renk Stabilitesi ve Translüsensi Parametresi Açısından Karşılaştırılması: in Vitro Çalışma

Abstract

Amaç: Bu in vitro çalışmada farklı mikrohibrid kompozitlerin distile su veya kahvede bekletildikten sonra renk stabilitelerinin ve translüsensi parametrelerinin (TP) karşılaştırılması amaçlanmıştır.
Gereç ve Yöntem: Üç farklı mikrohibrit kompozit rezin materyalden [G-eanial Anterior (GC, Japonya), Filtek Z250 (3M, ABD), yeni geliştirilen Üniversal Kompozit (Dolgunn-Himg, Türkiye)] her gruptan 20 adet ve toplamda 60 adet disk olacak şekilde örnekler oluşturuldu. Örneklerin yarısı distile suda diğer yarısı hazır kahve içeren kaplarda bekletildi. Renk stabilitesini değerlendirmek için başlangıç, 1. ve 4. hafta sonunda; TP için ise başlangıç ve 4. hafta sonunda bir spektrofotometre ile ölçümler yapıldı. Ortalama L*,a*, b* renk değişim değerleri CIEDE2000 renk formülüne (ΔE00) uygulandı. Renk parametresi için; renk değişim değerleri (ΔE) ve TP için; translüsensi değişim değerleri (ΔTP) hesaplandı. Verilerin analizinde tekrarlı ölçümlerde iki yönlü varyans analizi kullanılmıştır. Küresellik varsayımı Mauchly’nin W testi ile değerlendirilmiştir. Çoklu karşılaştırmalarda LSD testi kullanılmıştır (p<0.05).
Bulgular: Kompozit rezin örneklerde 1 ve 4 hafta kahvede bekletme sonrası anlamlı düzeyde renk değişimi (ΔE: 3.45-7.93) gözlendi. En yüksek renk değişimi Dolgunn kompozit grubunda (p<0.001; p=0,001) saptandı. Kahve ve kontrol grubunda yer alan kompozitlerin TP değerlerinde farklılık gözlenmedi (F=1,821 p=0,181; F=0,191 p=0,828).
Sonuç: Çalışmada, restoratif materyallerin renk stabilitesinde içerik ve kompozisyonu gibi yapısal özelliklerinin renklenmeye neden olan içeriklere maruz kalmaları durumunda önemli bir bileşen olduğu, ancak optik özellikleri belirleyen translüsensi parametresinde anlamlı değişikliğine neden olmadığı gözlenmiştir.

Keywords

Kompozit rezin, Renk stabilitesi, Translüsensi parametresi

Ethical Statement

Bu makale, sempozyum ya da kongrede sunulan bir tebliğin içeriği geliştirilerek ve kısmen değiştirilerek üretilmemiştir. Bu çalışma, yüksek lisans ya da doktora tezi esas alınarak hazırlanmamıştır. Bu çalışmanın hazırlanma sürecinde bilimsel ve etik ilkelere uyulduğu ve yararlanılan tüm çalışmaların kaynakçada belirtildiği beyan olunur.

Supporting Institution

Başkent Üniversitesi

Project Number

Proje no: D-DA22/02

References

• 1. Tonçara Kıvrak T, Gökay O. Kompozit rezinlerin renk stabilitesine etki eden faktörler A.Ü. Diş Hek. Fak. Derg. 2018;45:105-114.
• 2.Valizadeh S, Asiaie Z, Nazanin Kiomarsi N, Kharazifard MJ. Color stability of self-adhering composite resins in different solutions. Dent Med Probl. 2020;57:31–38.
• 3.ElSayad II. Color and translucency of finished and un- finished esthetic restorative materials after staining and bleaching. Saudi Dent J. 2018;30:219–25.
• 4.Güler E, Gönülol N, Yücel AÇ, Yılmaz F, Ersöz E. Farklı içeceklerde bekletilen kompozit rezinlerin renk stabilitelerinin karşılaştırılması. Atatürk Üniver Diş Hek. Fakül Derg 2013;21:24-29.
• 5.Fontes ST, Fernandez MR, de Moura CM, Meireles SS. Color stability of a nanofill composite: effect of different immersion media. J Appl Oral Sci 2009;17:388-91.
• 6.Mundim FM, Garcia Lda FR, Cruvinel DR, Lima FA, Bachmann L, Pires-de-Souza Fde C. Color stability, opacity and degree of conversion of pre-heated composites. J Dent 2011;39:e25-9.
• 7.Poggio C, Beltrami R, Scribante A , Colombo M , Chiesa M. Surface discoloration of composite resins: Effects of staining and bleaching. Dent Res J. 2012:9;567-73.
• 8.Gül P, Akgül N. Farklı kompozit rezinlerin translüsensi ve maskeleme özelliklerinin karşılaştırılması. Dent Fac Atatürk Uni. 2013;21:30–6.
• 9.Johnston WM, Reisbick MH. Color and translucency changes during and after curing of esthetic restorative materials. Dent Mater. 1997;13:89-97.
• 10.Lee YK, Lim BS, Rhee SH, Yang HC, Powers JM. Color and translucency of A2 shade resin composites after curing, polishing and thermocycling. Oper Dent. 2005;30:436-42.
• 11. Salas M, Lucena C, Herrera LJ, Yebra A, Della Bona A, Pérez MM. Translucency thresholds for dental materials. Dent Mater. 2018;34:1168–74.
• 12. Haas K, Azhar G, Wood DJ, Moharamzadeh K, van No- ort R. The effects of different opacifiers on the translu- cency of experimental dental composite resins. Dent Mater. 2017;33:310-6.
• 13.Mutlu ŞN, Tuncdemir MT. Beyazlatıcı ağız gargara- sının renklendirilmiş kompozit rezinin renk değişi- mine ve yüzey pürüzlülüğüne etkisi. Selcuk Dent J. 2020;7:435–9.
• 14.Malekipour MR, Sharafi A, Kazemi S, Khazaei S, Shi- rani F. Comparison of color stability of a composite resin in different color media. Dent Res J (Isfahan). 2012;9:441-6.
• 15. Um CM, Ruyter IE. Staining of resinbased veneering materials with coffee and tea. Quint int 1991;22:377-87.
• 16.Zajkani E, Abdoh Tabrizi M, Ghasemi A, Torabzade H, Kharazifard M. Effect of staining solutions and repolishing on composite resin color change. JIDA. 2013;25:139–46.
• 17.Poggio C, Vialba L, Berardengo A, Federico R, Colombo M, Beltramiet R, et al. Color Stability of New Esthetic Restorative Materials: A Spectrophotometric Analysis. J Funct Biomater. 2017;8:26.
• 18.Ertaş E, Güler AU, Yücel AC, Köprülü H, Güler E. Color stability of resin composites after immersion in different drinks. Dent Mater J. 2006;25:371.
• 19.Dietschi D, Campanile G, Holz J, Meyer JM. Comparison of the color stability of ten new-generation composites: an in vitro study. Dent Mater 1994; 10: 353–62.
• 20.Tuncdemir AR, Güven ME. Effects of fibers on color and translucency changes of bulk-fill and anterior composites after accelerated aging. Biomed Res Int. 2018;2018:2908696.
• 21.Turgut S, Bağış B, Bağış YH, Korkmaz FM, Tüzüner T, Baygın Ö. Restoratif materyallerin translüsensi özelliklerinin değerlendirilmesi. AÜ Diş Hek Fak Derg. 2011;38:18–20.
• 22. Ryan EA, Tam LE, McComb D. Comparative translu- cency of esthetic composite resin restorative materi- als. J Can Dent Assoc. 2010;76:a84.
• 23. Yu B, Lee YK. Influence of color parameters of resin composites on their translucency. Dent Mater. 2008;24:1236-42.
• 24. Yu B, Lee YK. Translucency of varied brand and shade of resin composites. Am J Dent. 2008;21:229-32.
• 25. Ghinea R, Pérez MM, Herrera LJ, Rivas MJ, Yebra A, Pa- ravina RD. Color difference thresholds in dental cera- mics. J Dent. 2010;38:57-64.
• 26. Piccoli YB, Lima VP, Basso GR, Salgado VE, Lima GS, Moraes RR. Optical stability of high-translucency resin-based composites. Oper Dent. 2019;44:536–44.
• 27. Heffernan MJ, Aquilino SA, Diaz-Arnold AM, Haselton DR, Stanford CM, Vargas MA. Relative translucency of six all-ceramic systems. Part I: core materials. J Prosthet Dent. 2002;88:4-9.
• 28. Azzopardi N, Moharamzadeh K, Wood DJ, Martin N, van Noort R. Effect of resin matrix composition on the translucency of experimental dental composite resins. Dent Mater. 2009;25:1564-8.
• 29. Lu H, Powers JM. Color stability of resin cements after accelerated aging. Am J Dent. 2004;17:354–8.
• 30. Morsy A, Gamal W, Riad M. Color matching of a sing- le shade structurally colored universal resin composite with the surrounding hard dental tissues. EDJ. 2020;66:2721–7.
• 31. Nikaido T, Kunzelmann KH, Chen H, Ogata M, Hara- da N, Yamaguchi S, et al. Evaluation of thermal cycling and mechanical loading on bond strength of a self-etching primer system to dentin. Dent Mater. 2002;18:269-75.
• 32. Koyuturk AE, Kusgoz A, Ulker M, Yeşilyurt C. Effects of mechanical and thermal aging on microleakage of different fissure sealants. Dent Mater J. 2008;27:795– 801.