COATING OF POLYETHYLENE TEREPHTHALATE NONWOVEN FABRICS WITH INDIUM ZINC OXIDE SOLUTIONS AT LOW TEMPERATURE BY SOL-GEL PROCESS

Year 2010, Volume: 17 Issue: 79, 2 - 6, 01.08.2010

Abstract

In this study, the polyethylene terephthalate (PET) nonwoven fabric was firstly coated with indium zinc oxide solution at low temperature by sol-gel process. The electrical resistivity values of the fabrics coated with indium zinc oxide (IZO) was measured by using four-point probe method before and after washing test. The surface morphology and structural properties of the fabric samples were investigated by scanning electron microscopy (SEM) and X-ray diffractometer, respectively. Moreover, the effect of coating layer numbers as three and six layers on electrical properties of the coated fabric samples was figured out. It was determined that the electrical resistivity values of the fabric samples coated by six layers were 89 .

SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI

Year 2010, Volume: 17 Issue: 79, 2 - 6, 01.08.2010

Abstract

Bu çalışmada polietilen tereftalat (PET) dokusuz yüzey kumaş literatürde ilk defa olarak indiyum çinko oksit sol çözeltisi ile düşük sıcaklıkta sol-jel yöntemiyle kaplanmıştır. İndiyum çinko oksit (IZO) ile kaplanan kumaşların elektriksel direnç değerleri dört nokta prob yöntemi kullanarak yıkamadan önce ve sonra ölçülmüştür. Kumaş örneklerinin yüzey morfolojisi ve yapısal özellikleri sırasıyla tarama elektron mikroskobu (SEM) ve X-ışınları difraktometresi (XRD) kullanarak incelenmiştir. Ayrıca 3 kat ve 6 kat olmak üzere kaplama kat sayısının artırılmasının kaplanan kumaşların elektriksel özellikleri üzerine etkisi araştırılmıştır. 6 kat kaplanan kumaşların elektriksel direnç değerinin 89 k ğu bulunmuştur.

There are 0 citations in total.

Details

Primary Language Turkish
Subjects Engineering
Journal Section Articles
Authors

Xuyuan Tao This is me

Vladan Koncar This is me

Claude Dufour This is me

Publication Date August 1, 2010
Published in Issue Year 2010 Volume: 17 Issue: 79

Cite

APA Tao, X., Koncar, V., & Dufour, C. (2010). SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI. Tekstil Ve Mühendis, 17(79), 2-6.
AMA Tao X, Koncar V, Dufour C. SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI. Tekstil ve Mühendis. August 2010;17(79):2-6.
Chicago Tao, Xuyuan, Vladan Koncar, and Claude Dufour. “SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI”. Tekstil Ve Mühendis 17, no. 79 (August 2010): 2-6.
EndNote Tao X, Koncar V, Dufour C (August 1, 2010) SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI. Tekstil ve Mühendis 17 79 2–6.
IEEE X. Tao, V. Koncar, and C. Dufour, “SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI”, Tekstil ve Mühendis, vol. 17, no. 79, pp. 2–6, 2010.
ISNAD Tao, Xuyuan et al. “SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI”. Tekstil ve Mühendis 17/79 (August 2010), 2-6.
JAMA Tao X, Koncar V, Dufour C. SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI. Tekstil ve Mühendis. 2010;17:2–6.
MLA Tao, Xuyuan et al. “SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI”. Tekstil Ve Mühendis, vol. 17, no. 79, 2010, pp. 2-6.
Vancouver Tao X, Koncar V, Dufour C. SOL-JEL YÖNTEMİ İLE DÜŞÜK SICAKLIKTA POLİETİLEN TEREFTALAT DOKUSUZ YÜZEY KUMAŞLARIN İNDİYUM ÇİNKO OKSİT ÇÖZELTİLER İLE KAPLANMASI. Tekstil ve Mühendis. 2010;17(79):2-6.