Perlit Esaslı Geopolimer Kompozitlere Kür Süresi Ve Sıcaklığın Etkisi

Inorderto minimize the CO₂emissionandenergyconsumption, which are disadvantageous during the cement production,perlit-basedcompositeswasproduced in thisstudy. Tothis and, ground perlite was activated with sodiumhydroxide and perlite-based cementless cubic composites with dimensions of 50 × 50 × 50 mm were produced. The produced samples were cured for 24 and 48 hours curing time at 90 ºC and 110 ºC curing temperature. The best curing time was determined according to NaOH molarity of the solution and curing temperature. The best compressive strength was determined as 46.76 MPa in perlite-based composites having 15,5 solution molarity, 24 hours curing time and at 110 ºC curing temperature.

Çimento üretimi esnasında dezavantaj olan CO₂ emisyonu ve yüksek enerji tüketimini en aza indirilmesi amacı ile bu çalışmada perlit içeren geopolimer kompozitler üretilmiştir. Bu amaçla öğütülmüş perlit, sodyum hidroksit ile aktive edilerek, 50×50×50 mm boyutlarında çimentosuz perlit esaslı kompozit küp numuneler üretilmiştir. Üretilen numuneler 24 ve 48 saat kür süresinde ve 90 ºC ve 110 ºC derece kür sıcaklığında olgunlaştırılmıştır. Karışımlar için en iyi kür süresi, Na alkali oranı ve kür sıcaklığına bağlı olarak en yüksek basınç dayanımları belirlenmiştir. En iyi basınç dayanımı %16 Na alkali oranında, 24 saat kür süresinde ve 110 ºC kür sıcaklığında 46,76 MPa olarak bulunmuştur.