RELATIONSHIP BETWEEN CRYSTALLINE STRUCTURE AND OPTICAL PROPERTIES OF WHEAT (Triticum aestevum L.) STRAW SODA-OXYGEN PULP

Yıl 2003, Cilt: 4 Sayı: 1, 14 - 20, 19.03.2011

Esat Gümüşkaya , Zehra Serin Sedat Ondaral , Derya Ustaömer

Öz

In this study;
pulp was produced with soda-oxygen process by using wheat (Triticum
aestevum L.) straw as raw material and this pulp
bleached with hypocholoride (H) and peroxyde (P) stages. It was found that
crystalline properties of unbleached and bleached pulp samples increased by
removing amorphous components. In addition, paper sheets made from unbleached
and bleached soda-oxygen pulp and determined their optical properties.
Consequently; while crystalline properties of pulp samples was rising with HP
bleaching, it was determined that optical properties of paper sheets improved
with bleaching.

Anahtar Kelimeler

Soda-oxygen pulping , cellulose , crystallinity , wheat straw , x-ray

BUĞDAY (Triticum aestevum L.) SAPI SODA-OKSİJEN KAĞIT HAMURUNUN KİMYASAL VE KRİSTAL YAPISI İLE OPTİK ÖZELLKLERİ ARASINDAKİ İLİŞKİLER

Öz

Buğday (Triticum aestevum L.) sapından soda-oksijen  yöntemiyle elde edilen kagıt hamurları hipoklorit (H) ve peroksit (P) ile iki kademeli ağartma işlemine tabi tutulmuştur. Pişirme ve ağartma işlemleri boyunca amorf yapılı bileşenlerin hammadde ve kağıt hamuru bünyesinden uzaklaştırılmasıyla birlikte kristalen yapı özelliklerinde artış olduğu tespit edilmiştir. Ayrıca, pişirme ve ağartma işlemleri sırasında her bir kademeden alınan kagıt hamuru örneklerinden elde edilen kağıt safihalarının optik özellikleri belirlenmiştir. Sonuç olarak; soda-oksijen yöntemiyle elde edilen kağıt hamurlarının HP kademeleri ile ağartıldığında kristalen özelliklerinin artmasına bağlı olarak optik özelliklerinin geliştiği tespit edilmiştir.

Anahtar Kelimeler

Soda-oksijen pisirmesi , selüloz , kristallik derecesi , bugday samanı , x-ısını