Effects of Different Wood Preservatives on The Some Physical Properties of Wood Species Used in Furniture and Building Industry

Öz

This study aims to determine the combustion, density values of Fagus and Pinus sylvestris’ woods impregranted with Ammonium tetra fluoro borate (1 - 3 %) and the mixture of cement and borax (6 % – 9 %) according to ASTM-D 1413-76 standards. In the combustion test carried out according to ASTM-D 160-50, the combustion resulted from flame, the self-combustion and the combustion as glowing processes were completed and the amount of lux, combustion duration, decomposition and ash were determined. According to experimental results, it is determined that Fogus’ wood has the highest retention (42,43 kg/m3) in the mixture of cement and borax 9 %, combustion tempature (587 o C) in the mixture of cement and borax 6 % , the value of lux (267 lux) in the the combustion as glowing and Pinus sylvestris’ wood has the longest combustion duration (29,03 min.) Ammonium tetrafluoro borate 1%, the most weight loss (94 %).

Anahtar Kelimeler

• Pinus brutia pine
• beech wood
• boron compounds
• combustion of wood
• impregnation
• density

Çeşitli Emprenye Maddelerinin Mobilya ve Yapı Endüstrisinde Kullanılan Odun Türlerinin Bazı Fiziksel Özellikleri Üzerine Etkileri

Öz

Bu çalışmada, amonyum tetra flu borat (% 1 - % 3) ve çimento + boraks (% 6 - % 9) ile ASTM-D 1413–76 esaslarına göre emprenye edilen Doğu Kayını (Fagus Orientalis Lipsky) ve Sarıçam (Pinus Sylvestris L.) odunlarının yanma ve yoğunluk değerlerinin belirlenmesi amaçlanmıştır. ASTM D 160–50 standardına göre yapılan yanma deneyinde alev kaynaklı yanma (AKY), kendi kendine yanma (KKY), kor halinde yanma (KHY) işlemi yapılmış olup; ışık yoğunluk değeri, yanma süresi, dağılma ve kül miktarı belirlenmiştir. Deney sonuçlarına göre en yüksek retensiyon kayın odunu %9 çimento+boraks karışımında (42,43 kg/m3), en yüksek yanma sıcaklığı kayın odunu %6 çimento+boraks karışımında (587°C), ışık yoğunluk değeri KHY’ da kayın odunu %9 çimento+boraks karışımında (267 Lüks), en uzun yanma süresi sarıçam odunu %1 amonyum tetra flu boratta (29.03 dk), en çok ağırlık kaybı sarıçam odunu kontrol örneğinde (% 94) tespit edilmiştir.

Anahtar Kelimeler

• Sarıçam
• kayın
• borlu bileşikler
• odunda yanma
• emprenye
• yoğunluk

Kaynakça

1. ASTM D 1413–76 (1976) Standartd Methods of Testing Preservatives by Laboratory Soilblock Cultures, Annual Book of Astm Standarts, USA Wood
2. ASTM 160–50 (1975) Standart Test Method for Combustible Properties of Terated Wood by the Crib Test, USA
3. Atılgan A, Peker H, Tan H, Bakır D (2011) Çevre Dostu Borlu Bileşiklerin Mobilya Olanakları, Artvin Çoruh Üniversitesi Orman Fakültesi Dergisi, 12 (2):126– 138 Kullanım
4. Atar M, Keskin H, Yavuzcan HG (2004) Varnish Layer Hardness of Oriental Beech (Fagus orientalis Lipsky) Wood as Effected by İmpregnation and Clor Bleaching, J. Coatings Technol. 1: 498–504
5. Baysal E (1994) Çeşitli Borlu ve Wr Bileşiklerin Kızılcam Odununun Bazı Fiziksel Özelliklerine Etkisi, K.T.Ü. Fen Bil. Enstitüsü, Yüksek Lisans Tezi, Trabzon
6. Baysal E, Şimşek H, Toker H, Çolak M, Yiğitbaşı ON (2006) Borlu Bileşiklerle Muamele Edilmiş Ağaç Malzemede Higroskopisite Seviyelerinin Belirlenmesi, III. Uluslararası Bor Sempozyumu, Ankara, 45–51
7. Baysal E (2003) Yanmayı Geciktirici Kimyasal Maddeler ve Bitkisel Sepi Maddeleri ile Muamele Edilen Doğu Kayını ( Fagus orientalis Lipsky) Odununun Yanma Özellikleri, Fırat Üniversitesi, Fen ve Mühendislik Bilimleri Dergisi, 15(1), 123–134
8. Hafızoğlu H, Yalınkılıç MK, Yıldız ÜC, Baysal E, Peker H, Demirci Z (1994) Türkiye Bor Kaynaklarının Odun Koruma (Emprenye) Endüstrisinde Değerlendirilme İmkânları, Tübitak- Tarım ve Ormancılık Araştırma Grubu Projesi Kod No: TOAG- 875, Trabzon Chin-Mu T, Wang Incombustibility of Fire Retardant Coated Wood Panels Quart. J. Expt. Forest NTU, 5: 49–55 YL (1991)

9. Goldstein IS (1973) Degradation And Protecüon of Wood From Thermal Attcak, in:Wood Deterioration and Its Prevention by Preservative Treatments (D.D. Nicholas,Ed.) Syracuse Univ., New York, Press, Vol:I, 307-339
10. Hafors B (1990) The Role of the Wasa in the Development of PEG Preservation Method in: Archaelogical Wood Properties, Preservation Series: 225: 195–217
11. Kayacık H (1968) Orman ve Park Ağaçlarının Özel Sistematiği, III. cilt, Angiospermae İstanbul Üniversitesi, Y No: 1360, Orm. Fak. Yayın No: 134 tohumlar), Fire Rretardant Treatments on Wood Stentgh: A Rewiew, Wood and Fiber Science, 22 (1): 113–131
12. Peker H, Atar M, Uysal B (1999) Ağaç Malzemede Yanmayı Geciktirici ve Su İtici Kimyasal Maddelerin Eğilme Direncine Üniversitesi, Fen ve Mühendislik BilimleriDergisi, 5(1): 975–983
13. Örs Y, Atar M, Peker H (1999) Bazı Emprenye Maddelerinin Sarıçam ve Doğu Yoğunluklarına Etkileri, Tübitak, Doğa Türk Tarım ve Ormancılık Dergisi, 23 (5): 1169–1179 Odunlarının
14. Örs Y, Sönmez A, Uysal B (1999) Çeşitli Kimyasal Malzemenin Yanmaya Dayanıklılığı Üzerine Etkileri, Türk Tarım ve Ormancılık Dergisi, 23(2):43–48
15. Örs Y, Atar M, Peker H (1999) Çeşitli Emprenye ve Üst Yüzey İşlem Maddelerinin Sarıçam ve Kestane Odununun Etkileri, Tübitak Doğa Türk Tarım ve Ormancılık Dergisi, 23 (5): 541–549
16. Örs Y, Atar M, Peker H (1999) Okaliptüs (Eucalyptus Camaldulensis Dehn.) Odunun Pamukkale Üni. Müh. Bil. Dergisi, 5 (2–3): 1195–1201 Özellikleri,
17. Örs Y, Atar M, Peker H (1999) Sarıçam Odunun Yanma Özeliklerine Bazı Borlu Bileşiklerin ve Su İtici Maddelerin Etkileri, Türk Tarım ve Ormancılık Dergisi, 3 (5): 501–509
18. Qu H, Wu W, Wu H, Xie J, Xu J (2011) Study on the Effects of Flame Retardants Decomposition of Wood by TG–MS, Journal of Thermal Analysis and Calorimetry, 103: 935–942 Thermal
19. Sönmez A, Atar M, Peker H (2001) Çeşitli Maddeler ile Emprenye Edilmiş Melez Kavak Odununun Yanma Özellikleri, Gazi Üniversitesi, Fen Bilimleri Enstitüsü Dergisi, 15 (1): 23-35
20. Temiz A, Gezer ED, Yildiz UC, Yildiz S (2008) Combustion Properties of Alder (Alnus glutinosa L.) Gaertn. Subsp Barbata (CA Mey) Yalt.) and Southern Pine (Pinus sylvestrisL.) Wood Compounds, Building Materials, 22, 11, 2165–2169
21. Toker H (2007) Borlu Bileşiklerin Ağaç Malzemenin Bazı Fiziksel Mekanik ve Biyolojik Özelliklerine Etkilerinin Belirlenmesi, Gazi Üniversitesi Fen Bilimleri Enstitüsü, Doktora Tezi, Eylül, Ankara
22. TS 2471 (1976) Odunda Fiziksel ve Mekaniksel Deneyler için Rutubet Miktarı Tayini, TSE, Ankara
23. TS 345 (1974) Ahşap Emprenye Maddelerinin Etkilerinin Muayene Metotları, TSE, Ankara
24. TS 1476 (1984) Odunda Fiziksel ve Mekaniksel Özelliklerinin Tayini İçin Homojen Meşcerelerden Numune Ağacı ve Laboratuar Numunesi Alınması, TSE, Ankara
25. TS 2471 (1976) Odunda Fiziksel ve Mekaniksel Deneyler İçin Rutubet Miktarı Tayini TSE, Ankara
26. TS 2472 (1976) Odunda, Fiziksel ve Mekaniksel Deneyler için Birim Hacim Ağırlığı Tayini, TSE, Ankara
27. Uysal B, Özçiftçi A (2004) The Effects of İmpregnation Combustion Properties of Laminated Wood Material. Combustion Science & Technology, 176(1): 117–133
28. Williams LH (1990) Potential Benefits of Diffusible Preservatives for Wood Protecüon : An Analysis with Emphasis on Building Protecüon, In: First International Conferance on Wood Protection with Diffusible Preservatives, Hamel, Forest Products Research Society, 29-35
29. Yalınkılıç MK, Baysal B, Demirci Z (1997) Bazı Borlu Bileşiklerin ve Su İtici Maddelerin Kızılçam Odunun Yanma Özellikleri Üzerine Etkileri, Doğa Türk Tarım ve Ormancılık Dergisi, 21 (3): 423–431
30. Yalınkılıç MK, Demirci Z, Baysal E (1996) Çeşitli Duglas (Mirb.) Franco) OdunununYanma Özellikleri Pamukkale Üniversitesi, Mühendislik Bilimleri Dergisi, 4 (1–2): 613–624
31. Yalınkılıç MK, Baysal E, Demirci Z, Peker H (1996) Sarıçam, Kayın, Ladin ve Kızılağaç Odunlarının Çeşitli Kimyasal Maddelerle Emprenye Edilebilme Özellikleri, Pamukkale Üniversitesi, Mühendislik Bilimleri Dergisi, 2 (2):147–156 .