Comparison of different resin-modified glass ionomer cements of water sorption and microleakage values used in pediatric dentistry

Yıl 2013, Cilt: 23 Sayı: 1, 43 - 49, 01.01.2013

Öz

Purpose: The purpose of this in vitro study was to evaluate the amount of water sorption and microleakage of resin-modified glass ionomer cements used in the treatment of primary teeth. Material and Methods: For evaluate scores of microleakage of 4 different materials were used noncarious 60 extracted primary molar teeth. Teeth were randomly divided into 4 groups (n=15). Standard class II preparations (3x3x2 mm) were made in mesial and distal surfaces. All cavities were restored using one of four material (Photac–Fil Quick, Ionolux, Fuji II LC and Riva). After all teeth were subjected to thermocycling for 250 cycles, teeth were cut mesio-distal direction from the center of the restoration and scores of microleakage were determined using a microscope. For evaluate water sorption of materials were prepared 10 specimens of each material with 5 mm diameter and 2 mm thick. These specimens were stored in a desiccator for 1 hour at 23 ± 2º C and then 24 hours 37±1º and the weight of each sample was measured by sensitive balance. The specimens were stored in an incubator which contains distilled water at 37 ± 1º C’ for one week. Then the specimens were weighed again. Data were analyzed statistically by Analysis of Variance and Tukey HSD test. Results: Gingival leakage of Photac-Fil Quick and Riva specimens were found to be statistically higher than in other materials (p<0.05). Riva showed the highest water sorption value after 7 days (p<0.05). Conclusion: If the resin-modified glass ionomer cement can use in the treatment of primary teeth, the use of Fuji II LC with the lowest values of water sorption and microleakage may be prefer.

Kaynakça

  • Wilson AD, Kent BE. A new translucent for dentistry. The glass ionomer cement. Br Dent J 1972;132:133-5.
  • Yap AU, Pek YS, Cheang P. Physico-mechanical properties of a fast-set highly viscous GIC restorative. J Oral Rehabil 2003;30:1-8.
  • Rosenstiel SF, Land MF, Crispin MJ. Dental luting agents: A review of the current literature. J Prosthet Dent 1998;80:280-301.
  • Yap A, Lee CM. Water sorption and solubility of resin-modified polyalkenoate cements. J Oral Rehabil 1997;24:310-4.
  • Nicholson JW, McLean JW. A preliminary report on the effect of storage in water on the properties of commercial light-cured glass-ionomer cements. Br Dent J 1992;173:98-101.
  • Mitra SB, Kedrowski BL. Long-term mechanical properties of glass ionomers. Dent Mater 1994;10:78-82.
  • Mitra SB. Adhesion to dentin and physical properties of a light-cured glass ionomer liner/base. J Dent Res 1991;70:72-4.
  • Uno S, Finger WJ, Fritz U. Long-term mechanical characteristics of resin-modified glass ionomer restorative materials. Dent Mater 1996;12:64-69.
  • Hinoura K, Onose H, Masutani S, Matsuzaki T, Moore BK. Volumetric change of light cured glass ionomer in water. J Dent Res 1993; 72:222, Abstr. No.9
  • Iwami Y, Yamamoto H, Sato W, Kawai K, Torii M, Ebisu S. Weight change of various lightcured restorative materials after water immersion. Oper Dent 1998;23:132-7.
  • Braden M. recent advances in dental materials. In: Yap A, Lee CM. Water sorption and solubility of resin-modified polyalkenoate cements. J Oral Rehabil 1997;24:310-4.
  • Arias VG, Campos IT, Pimenta LAF. Microleakage study of three adhesive sistems. Braz Dent 2004;15:194-8.
  • Hondrum SO. Storage stability of dental luting agents. J Prosthet Dent 1999;81:464-8.
  • Küçükeşmen C, Küçükeçmen Ç, Öztaş DD, Kaplan R. Farklı Tiplerdeki Geleneksel Ve Rezin-Modifiye Cam İyonomer Simanların Su Emilimi Ve Suda Çözünürlüğü. AÜ. Diş Hek. Fak. Derg. 2005;32: 25
  • Kanchanavasita W, Anstice HM, Pearson GJ. Water sorption characteristics of resin-modified glass- ionomer cements. Biomaterials 1997;18: 343Cattani-Lorente MA, Dupuis V, Payan J, Moya F, Meyer JM Effect of water on the physical properties of resin-modified glass ionomer cements. Dent Mater. 1999 ;15:71-8.
  • Nicholson JW. The physics of water sorption by resin-modified glass ionomer dental cements. J Mater Sci Mater Med. 1997 ;8:691-5.
  • Meyer JM, Cattani-Lorente MA, Dupuis V. Compomers: between glass-ionomer cements and composites. Biomat 1998;19:529-39.
  • Iwami Y, Yamamoto H, Sato W, Kawai K, Torii M, Ebisu S. Weight change of various lightcured restorative materials after water immersion. Oper Dent 1998;23:132-7.
  • Carvalho RM, Pereira JC, Yoshiyama M, Pashley DH. A review of polymerization contraction: The influence of stress development versus stress relief. Oper Dent 1996;21:17-24.
  • Condon JR, Ferracane JL. Assessing the effect of composite formulation on polymerization stress. JADA 2000;131:497-503.
  • Öztürk AN, Usumez A, Öztürk B, Usumez S. Influence of different light source on microleakage of class V composite resin restoration. J Oral Rehabil 2004;31:500-4.
  • Hanks GT, Wataha JC, Parsel RR. Permeability of biological and synthetic molecules through dentine. J Oral Rehabil 1994;21:475-87.
  • Ferrari M, Garcia-Godoy F. Sealing ability of new generation adhesive restorative materials placed on vital teeth. Am J Dent 2002;15:117-28.
  • Çelik Ç, Özel Y, Karabulut E. Kavite dezenfektanı uygulamasının farklı dentin adeziv sistemlerin mikrosızıntısına etkisi. Atatürk Üniv Diş Hek Fak Derg 2007;17: 7-12.
  • İrie M, Suzuki K. Marginal sealof resin-modified glass ionomers and compomers:Effect of delaying polishing procedure after one day storage. Oper Dent 2000:25;488-96.
  • İrie M, Suzuki K. Water storage effect on the marginal seal of resin modified glass ionomer restorations Oper Dent 1999;24;272-8. Masih S, Thomas AM, Koshy G, Joshi JL. Comparative evaluation of the microleakage of two modified glass ionomer cements on primary molars. An in vivo study. J Indian Soc Pedod Prev Dent. 2011;29:135-9.
  • Oba AA, Aras Ş. Fuji II LC ve F 2000’in mikrosızıntı özelliklerinin süt dişinde in vitro koşullarda karşılaştırılması. G.Ü. Dişhek Fak Derg. 2003; 20: 23Brackett WW, Gunnin TD, Gilpatric RO, Browning WD. Microleakage of Class V compomer and lightcured glass ionomer restorations.J Prosthet Dent 1998;79:261-3. Yazışma Adresi: Yrd. Doç. Dr. Mustafa Erhan Sarı
  • Ondokuz Mayıs Üniversitesi Diş Hekimliği Fakültesi Pedodonti Anabilim Dalı, Samsun Fax:03624576032 Tel:03624405418
  • Email: dterhansari@hotmail.com

Çocuk diş hekimliğinde kullanılan farklı rezin modifiye cam iyonomer simanların su emilimi ve mikrosızıntı değerlerinin karşılaştırılması

Yıl 2013, Cilt: 23 Sayı: 1, 43 - 49, 01.01.2013

Öz

Amaç: Bu in-vitro çalışmanın amacı, süt dişlerinin tedavisinde kullanılan rezin modifiye cam iyonomer simanların su emilimi ve mikrosızıntı miktarlarını değerlendirmektir. Gereç ve Yöntem: 4 farklı rezin modifiye cam ionomer simanın mikrosızıntı değerlerinin değerlendirilmesi amacıyla çekilmiş çürüksüz 60 süt azı dişi kullanıldı. Dişler rastgele 4 gruba ayrıldı (n=15). Mezial ve distal yüzeylere standart sınıf II kaviteler (3x3x2 mm) açıldı. Kaviteler dört materyalden biriyle restore edildi (Photac–Fil Quick, Ionolux, Fuji II LC ve Riva). 250 tur termal siklus işleminin ardından dişler restorasyon merkezinden mesio-distal yönde kesildi ve mikrosızıntı seviyeleri mikroskopla belirlendi. Materyallerin su emiliminin değerlendirilmesi amacıyla 5 mm çapında 2 mm yüksekliğinde 10’ar adet örnek hazırlandı. Örnekler desikatör içerisine yerleştirilerek 1 saat 23 ± 2º C’de, daha sonra 24 saat 37 ± 1º C’de bekletildi ve bu süre sonunda her örneğin ağırlığı hassas terazi ile ölçüldü. Aynı örnekler daha sonra distile suda 37 ± 1º C’de bir hafta bekletildikten sonra tekrar tartıldı. Elde edilen veriler Varyans analizi ve Tukey HSD testi ile istatistiksel olarak değerlendirildi. Bulgular: Photac–Fil Quick ve Riva örneklerinde gingival bölgedeki mikrosızıntının istatistiksel olarak diğer materyallere göre daha fazla olduğu tespit edildi (p<0,05). 7 gün sonra en yüksek su emilimi değerini Riva gösterdi (p<0,05). Sonuç: Süt dişlerinin tedavisinde rezin modifiye cam iyonomer simanlar kullanılacaksa en düşük su emilimi ve mikro sızıntı değerlerine sahip Fuji II LC kullanılması tercih edilebilir.

Kaynakça

  • Wilson AD, Kent BE. A new translucent for dentistry. The glass ionomer cement. Br Dent J 1972;132:133-5.
  • Yap AU, Pek YS, Cheang P. Physico-mechanical properties of a fast-set highly viscous GIC restorative. J Oral Rehabil 2003;30:1-8.
  • Rosenstiel SF, Land MF, Crispin MJ. Dental luting agents: A review of the current literature. J Prosthet Dent 1998;80:280-301.
  • Yap A, Lee CM. Water sorption and solubility of resin-modified polyalkenoate cements. J Oral Rehabil 1997;24:310-4.
  • Nicholson JW, McLean JW. A preliminary report on the effect of storage in water on the properties of commercial light-cured glass-ionomer cements. Br Dent J 1992;173:98-101.
  • Mitra SB, Kedrowski BL. Long-term mechanical properties of glass ionomers. Dent Mater 1994;10:78-82.
  • Mitra SB. Adhesion to dentin and physical properties of a light-cured glass ionomer liner/base. J Dent Res 1991;70:72-4.
  • Uno S, Finger WJ, Fritz U. Long-term mechanical characteristics of resin-modified glass ionomer restorative materials. Dent Mater 1996;12:64-69.
  • Hinoura K, Onose H, Masutani S, Matsuzaki T, Moore BK. Volumetric change of light cured glass ionomer in water. J Dent Res 1993; 72:222, Abstr. No.9
  • Iwami Y, Yamamoto H, Sato W, Kawai K, Torii M, Ebisu S. Weight change of various lightcured restorative materials after water immersion. Oper Dent 1998;23:132-7.
  • Braden M. recent advances in dental materials. In: Yap A, Lee CM. Water sorption and solubility of resin-modified polyalkenoate cements. J Oral Rehabil 1997;24:310-4.
  • Arias VG, Campos IT, Pimenta LAF. Microleakage study of three adhesive sistems. Braz Dent 2004;15:194-8.
  • Hondrum SO. Storage stability of dental luting agents. J Prosthet Dent 1999;81:464-8.
  • Küçükeşmen C, Küçükeçmen Ç, Öztaş DD, Kaplan R. Farklı Tiplerdeki Geleneksel Ve Rezin-Modifiye Cam İyonomer Simanların Su Emilimi Ve Suda Çözünürlüğü. AÜ. Diş Hek. Fak. Derg. 2005;32: 25
  • Kanchanavasita W, Anstice HM, Pearson GJ. Water sorption characteristics of resin-modified glass- ionomer cements. Biomaterials 1997;18: 343Cattani-Lorente MA, Dupuis V, Payan J, Moya F, Meyer JM Effect of water on the physical properties of resin-modified glass ionomer cements. Dent Mater. 1999 ;15:71-8.
  • Nicholson JW. The physics of water sorption by resin-modified glass ionomer dental cements. J Mater Sci Mater Med. 1997 ;8:691-5.
  • Meyer JM, Cattani-Lorente MA, Dupuis V. Compomers: between glass-ionomer cements and composites. Biomat 1998;19:529-39.
  • Iwami Y, Yamamoto H, Sato W, Kawai K, Torii M, Ebisu S. Weight change of various lightcured restorative materials after water immersion. Oper Dent 1998;23:132-7.
  • Carvalho RM, Pereira JC, Yoshiyama M, Pashley DH. A review of polymerization contraction: The influence of stress development versus stress relief. Oper Dent 1996;21:17-24.
  • Condon JR, Ferracane JL. Assessing the effect of composite formulation on polymerization stress. JADA 2000;131:497-503.
  • Öztürk AN, Usumez A, Öztürk B, Usumez S. Influence of different light source on microleakage of class V composite resin restoration. J Oral Rehabil 2004;31:500-4.
  • Hanks GT, Wataha JC, Parsel RR. Permeability of biological and synthetic molecules through dentine. J Oral Rehabil 1994;21:475-87.
  • Ferrari M, Garcia-Godoy F. Sealing ability of new generation adhesive restorative materials placed on vital teeth. Am J Dent 2002;15:117-28.
  • Çelik Ç, Özel Y, Karabulut E. Kavite dezenfektanı uygulamasının farklı dentin adeziv sistemlerin mikrosızıntısına etkisi. Atatürk Üniv Diş Hek Fak Derg 2007;17: 7-12.
  • İrie M, Suzuki K. Marginal sealof resin-modified glass ionomers and compomers:Effect of delaying polishing procedure after one day storage. Oper Dent 2000:25;488-96.
  • İrie M, Suzuki K. Water storage effect on the marginal seal of resin modified glass ionomer restorations Oper Dent 1999;24;272-8. Masih S, Thomas AM, Koshy G, Joshi JL. Comparative evaluation of the microleakage of two modified glass ionomer cements on primary molars. An in vivo study. J Indian Soc Pedod Prev Dent. 2011;29:135-9.
  • Oba AA, Aras Ş. Fuji II LC ve F 2000’in mikrosızıntı özelliklerinin süt dişinde in vitro koşullarda karşılaştırılması. G.Ü. Dişhek Fak Derg. 2003; 20: 23Brackett WW, Gunnin TD, Gilpatric RO, Browning WD. Microleakage of Class V compomer and lightcured glass ionomer restorations.J Prosthet Dent 1998;79:261-3. Yazışma Adresi: Yrd. Doç. Dr. Mustafa Erhan Sarı
  • Ondokuz Mayıs Üniversitesi Diş Hekimliği Fakültesi Pedodonti Anabilim Dalı, Samsun Fax:03624576032 Tel:03624405418
  • Email: dterhansari@hotmail.com
Toplam 29 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Makaleler
Yazarlar

Yrd. Doç. Dr. Mustafa Erhan Sarı Bu kişi benim

Ar. Gör. Dt. Bilal Özmen Bu kişi benim

Yayımlanma Tarihi 1 Ocak 2013
Yayımlandığı Sayı Yıl 2013 Cilt: 23 Sayı: 1

Kaynak Göster

APA Sarı, Y. D. D. M. E., & Özmen, A. G. D. B. (2013). Çocuk diş hekimliğinde kullanılan farklı rezin modifiye cam iyonomer simanların su emilimi ve mikrosızıntı değerlerinin karşılaştırılması. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi, 23(1), 43-49.
AMA Sarı YDDME, Özmen AGDB. Çocuk diş hekimliğinde kullanılan farklı rezin modifiye cam iyonomer simanların su emilimi ve mikrosızıntı değerlerinin karşılaştırılması. Ata Diş Hek Fak Derg. Ocak 2013;23(1):43-49.
Chicago Sarı, Yrd. Doç. Dr. Mustafa Erhan, ve Ar. Gör. Dt. Bilal Özmen. “Çocuk Diş hekimliğinde kullanılan Farklı Rezin Modifiye Cam Iyonomer simanların Su Emilimi Ve mikrosızıntı değerlerinin karşılaştırılması”. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 23, sy. 1 (Ocak 2013): 43-49.
EndNote Sarı YDDME, Özmen AGDB (01 Ocak 2013) Çocuk diş hekimliğinde kullanılan farklı rezin modifiye cam iyonomer simanların su emilimi ve mikrosızıntı değerlerinin karşılaştırılması. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 23 1 43–49.
IEEE Y. D. D. M. E. Sarı ve A. G. D. B. Özmen, “Çocuk diş hekimliğinde kullanılan farklı rezin modifiye cam iyonomer simanların su emilimi ve mikrosızıntı değerlerinin karşılaştırılması”, Ata Diş Hek Fak Derg, c. 23, sy. 1, ss. 43–49, 2013.
ISNAD Sarı, Yrd. Doç. Dr. Mustafa Erhan - Özmen, Ar. Gör. Dt. Bilal. “Çocuk Diş hekimliğinde kullanılan Farklı Rezin Modifiye Cam Iyonomer simanların Su Emilimi Ve mikrosızıntı değerlerinin karşılaştırılması”. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi 23/1 (Ocak 2013), 43-49.
JAMA Sarı YDDME, Özmen AGDB. Çocuk diş hekimliğinde kullanılan farklı rezin modifiye cam iyonomer simanların su emilimi ve mikrosızıntı değerlerinin karşılaştırılması. Ata Diş Hek Fak Derg. 2013;23:43–49.
MLA Sarı, Yrd. Doç. Dr. Mustafa Erhan ve Ar. Gör. Dt. Bilal Özmen. “Çocuk Diş hekimliğinde kullanılan Farklı Rezin Modifiye Cam Iyonomer simanların Su Emilimi Ve mikrosızıntı değerlerinin karşılaştırılması”. Atatürk Üniversitesi Diş Hekimliği Fakültesi Dergisi, c. 23, sy. 1, 2013, ss. 43-49.
Vancouver Sarı YDDME, Özmen AGDB. Çocuk diş hekimliğinde kullanılan farklı rezin modifiye cam iyonomer simanların su emilimi ve mikrosızıntı değerlerinin karşılaştırılması. Ata Diş Hek Fak Derg. 2013;23(1):43-9.

Bu eser Creative Commons Alıntı-GayriTicari-Türetilemez 4.0 Uluslararası Lisansı ile lisanslanmıştır. Tıklayınız.