The effect of different sintering temperatures on microstructure and hardness in Al-7Si%10B4C composite material production

Öz

In this study, Al-7Si%10B₄C metal matrix composite material was produced by adding 10 wt. % B₄C in weight into the Al-%7Si powder mixture, using powder metallurgy method. The prepared powder mixtures were subjected to cold press under a pressure of 450 MPa and sintered for 60 minutes at different sintering temperatures (550°C, 570°C and 590°C) in an argon gas atmosphere. Microstructures of Al7Si%10B₄C composite materials produced at different sintering temperatures were characterized by SEM+EDS, X-ray diffraction (XRD) and hardness measurements. As a result of the study, it was observed that Al_3,21Si_0,47 in matrix phase and AlB₁₂, AlB₁₀, phase and compounds between matrix and reinforcement were formed by increasing the sintering temperature. Furthermore, it was determined that there is a significant increase in hardness values due to the increase in temperature values.

Anahtar Kelimeler

• Al-Si,B4C,MMC,Powder Metallurgy

Al-7Si%10B4C kompozit malzeme üretiminde farklı sinterleme sıcaklıklarının mikroyapı ve sertlik üzerine etkisi

Öz

Bu çalışmada, Al-7Si%10B₄C metal matrisli kompozit malzeme, Al-%7Si toz karışımı içerisine ağırlıkça %10 oranında B₄C ilave edilerek toz metalurjisi yöntemi kullanılarak üretilmiştir. Hazırlanan toz karışımları, 450 MPa basınç altında soğuk presleme işlemine tabi tutulmuş ve argon gazı atmosferinde farklı sinterleme sıcaklıklarında (550 ^oC, 570 ^oC ve 590 ^oC) 60 dakika süre ile sinterlenmiştir. Farklı sinterleme sıcaklıklarında üretilen Al7Si%10B₄C kompozit malzemelerin mikro yapıları, SEM+EDS, X-ışını kırınımı (XRD) ve sertlik ölçümü ile karakterize edilmiştir. Çalışma sonucunda, sinterleme sıcaklığının artması ile matris fazında Al_3,21Si_0,47 ve matris-takviye arasında ise AlB₁₂, AlB₁₀, faz ve bileşikleri oluştuğu görülmüştür. Ayrıca sıcaklık değerlerindeki artışa bağlı olarak sertlik değerlerinde görülür bir artış olduğu belirlenmiştir.

Anahtar Kelimeler

• Al-Si,B4C,MMK,Toz Metalurjisi

Kaynakça

1. [1] Cerit A. A., Karamis M. B., Nair F., Yıldızlı K., Effect of reinforcement particle size and volume fraction on wear behaviour of metal matrix composites, Journal of Balkan Tribological Association, 12 (4), 482-489, 2008.
2. [2] Jiang L., Wen H., Yang H., Hu T., Topping T., Zhang D., Schoenung J. M., Influence of length-scales on spatial distribution and interfacial characteristics of B4C in a nanostructured Al matrix, Acta Materialia, 89, 327-343, 2015.
3. [3] Li M., Ma K., Jiang L., Yang H., Lavernia E. J., Zhang L., Schoenung J. M., Synthesis and mechanical behavior of nanostructured Al 5083/n-TiB2 metal matrix composites, Materials Science and Engineering: A, 656, 241-248, 2016.
4. [4] Casati R., Vedani M., Metal matrix composites reinforced by nano-particles a review, Metals, 4(1), 65-83, (2014).
5. [5] Sharifi E. M., Karimzadeh F., Enayati M. H., Fabrication and evaluation of mechanical and tribological properties of boron carbide reinforced aluminum matrix nanocomposites, Materials & Design, 32(6), 3263-3271, 2011.
6. [6] Alumınıja V. H. K. N. O., Wear behaviour of B4C reinforced hybrid aluminum-matrix composites, Materiali in tehnologije, 49(1), 9-13. 2015.
7. [7] Çolak N , Turhan H ., Toz Metalurjisi Yöntemi ile Üretilen Al-Si/B4C Kompozit Malzemenin Mikroyapı ve Mekanik Özelliklerinin Araştırılması, Fırat Üniversitesi Mühendislik Bilimleri Dergisi, 28 (2), 259-266., 2016.
8. [8] Toptan F., Kilicarslan A., Karaaslan A., Cigdem M., Kerti I., Processing and microstructural characterisation of AA 1070 and AA 6063 matrix B4Cp reinforced composites, Materials & Design, 31, 87-91, 2010.

9. [9] Mohanty R. M., Balasubramanian K., Seshadri S. K., Boron carbide-reinforced alumnium 1100 matrix composites: fabrication and properties, Materials Science and Engineering: A, 498 (1-2), 42-52, 2008.
10. [10] Topçu I., Gülsoy H. O., Kadıoğlu N., Güllüoğlu A. N., Processing and mechanical properties of B4C reinforced Al matrix composites, Journal of Alloys and Compounds, 482 (1-2), 516-521, 2009.
11. [11] Lü P., Yue X. Y., Yu L., Ru H. Q., Effect of in situ synthesized TiB2 on the reaction between B4C and Al in a vacuum infiltrated B4C–TiB2–Al composite, Journal of materials science, 44 (13), 3483-3487, 2009.
12. [12] Ghasali E., Alizadeh M., Ebadzadeh T., hossein Pakseresht A., Rahbari A., Investigation on microstructural and mechanical properties of B4C–aluminum matrix composites prepared by microwave sintering. Journal of Materials Research and Technology, 4 (4), 411-415, 2015.
13. [13] Hu H. M., Lavernia E. J., Harrigan W. C., Kajuch J., Nutt S. R., Microstructural investigation on B4C/Al-7093 composite, Materials Science and Engineering: A, 297(1-2), 94-104, 2001.
14. [14] Jung J., Kang S., Advances in Manufacturing Boron Carbide‐Aluminum Composites, Journal of the American Ceramic Society, 87(1), 47-54, 2004.
15. [15] Frage N., Levin L., Frumin N., Gelbstein M., Dariel M. P., Manufacturing B4C–(Al, Si) composite materials by metal alloy infiltration, Journal of materials processing technology, 143, 486-490, 2003.
16. [16] Gomez L., Busquets-Mataix D., Amigo V., Salvador M. D., Analysis of boron carbide aluminum matrix composites. Journal of composite materials, 43(9), 987-995, 2009.
17. [17] Halverson D. C., Pyzik A. J., Aksay I. A., Snowden W. E., Processing of Boron Carbide‐Aluminum Composites. Journal of the American Ceramic Society, 72 (5), 775-780, 1989.
18. [18] Viala J. C., Bouix J., Gonzalez G., Esnouf C., Chemical reactivity of aluminium with boron carbide. Journal of Materials Science, 32(17), 4559-4573, 1997.
19. [19] Kumdalı F., Alüminyum Matrisli B4C Takviyeli Kompozitlerin Toz Metalurjisi Yöntemi İle Üretimi, Yüksek Lisans Tezi, Yıldız Teknik Üniversitesi Fen Bilimleri Enstitüsü, İstanbul, 2008.
20. [20] Alp E., Karaçay E., Cabbar H. C., Düşük sıcaklıkta bor karbür üretimi ve karakterizasyonu, Journal of the Faculty of Engineering & Architecture of Gazi University, 28 (2), 2013.
21. [21].Güler M., Alüminyum alaşımlarında inklüzyon çeşitleri ve önleyici faaliyetler, Metalurji, 184 (07), 36-42, 2017.
22. [22] Pyzik A. J., Beaman D. R., Al‐B‐C Phase Development and Effects on Mechanical Properties of B4C/Al‐Derived Composites, Journal of the American Ceramic Society, 78 (2), 305-312, 1995.