Heat treatment effect of hexagonal boron nitride reinforced electroless nickel coatings

Öz

In this study, surfaces of 1050 aluminium alloy were coated with hexagonal boron nitride (h-BN) reinforced electroless nickel-phosphorus (Ni-P) composite coating and the effect of heat treatment on the coating structure for 1 hour at 400°C was investigated. Composite coatings were performed in solutions which consist of three different compositions (1, 5 and 10 g/L) of h-BN. A scanning electron microscope (SEM), X-ray spectroscopy (EDS) and X-ray diffraction (XRD) analysis were performed on the composite coatings. Additionally, surface roughness and hardness were measured and finally, electrochemical corrosion experiments were conducted in 3.5% sodium chloride (NaCl) solution. The heat treatment process has identified a transition from amorphous structure to crystalline in the nickel matrix. The result of heat treatment, hardness values increased and the highest value of hardness (1015 ± 41 HV_0.05) was achieved with the specimen coated in 10 g/L h-BN solution. In the electrochemical experiments, a reduction in corrosion resistance of the composite coatings was determined the result of heat treatment. 

Anahtar Kelimeler

• 1050 aluminium alloy,Electroless nickel composite coating,Corrosion,h-BN,Heat treatment.

Hekzagonal bor nitrür takviyeli akımsız nikel kaplamanın özelliklerine ısıl işlemin etkisi

Öz

Bu çalışmada, 1050 alüminyum alaşım yüzeyine hekzagonal bor nitrür (h-BN) ilaveli akımsız nikel-fosfor (Ni-P) kompozit kaplama uygulanmış ve 400°C’de 1 saat süreyle yapılan ısıl işlemin kaplama yapısına etkisi incelenmiştir. Kompozit kaplamalar, üç farklı miktarda (1, 5 ve 10 g/L) h-BN içeren çözeltide yapılmıştır. Kaplamalara, Taramalı Elektron Mikroskobu (SEM), X-ışını spektroskopisi (EDS), X-ışını kırınımı (XRD) analizleri yapılmıştır. Bunlara ilaveten yüzey pürüzlülükleri, sertlikleri ölçülmüş ve %3,5 sodyum klorür (NaCl) çözeltisi içinde elektrokimyasal korozyon deneyleri yapılmıştır. Amorf yapıdaki nikel matrisin ısıl işlem ile kristalin yapıya dönüştüğü tespit edilmiştir. Isıl işlem sonucu sertlik değerleri artmış ve en yüksek sertlik değerine (1015 ± 41 HV_0,05), 10 g/L h-BN içerikli çözeltide yapılan kaplamada ulaşılmıştır. Elektrokimyasal deneylerde ise ısıl işlemin kompozit kaplamaların korozyon direncini azalttığı belirlenmiştir. 

Anahtar Kelimeler

• 1050 alüminyum alaşımı,Akımsız nikel kompozit kaplama,h-BN,Isıl işlem,Korozyon

Kaynakça

1. [1] Roy M., Surface Engineering for Enhanced Performance against Wear, Springer, New York, 2013.
2. [2] Sha W., Wu X., Keong K. G., Electroless Copper and Nickel-Phosphorus Plating: Processing, Characterisation and Modelling, Woodhead Publishing Limited, Cambridge, 2011.
3. [3] Sudagar J., Lian J., Sha W., Electroless nickel, alloy, composite and nano coatings - A critical review, J. Alloys Compd., 571, 183-204, 2013.
4. [4] 4. Agarwala R. C., Agarwala V., Electroless alloy/composite coatings : A review, Sadhana, 475, 93, 2003.
5. [5] Kocabaş M., Ön işlemli akımsız nikel ve bor nitrür takviyeli akımsız nikel kaplanmış anodize alüminyum yüzeylerin özellikleri, Doktora Tezi, Yıldız Teknik Üniversitesi Fen Bilimleri Enstitüsü, İstanbul, 2017.
6. [6] Rabizadeh T., Allahkaram S. R., Corrosion resistance enhancement of Ni-P electroless coatings by incorporation of nano-SiO2 particles, Mater. Des., 32 (1), 133-8, 2011.
7. [7] Wang H. L., Liu L. Y., Dou Y., Zhang W. Z., Jiang W. F., Preparation and corrosion resistance of electroless Ni-P/SiC functionally gradient coatings on AZ91D magnesium alloy, Appl. Surf. Sci., 286, 319-27, 2013.
8. [8] Islam M., Azhar M. R., Khalid Y., Khan R., Abdo H. S., Dar M. A., Electroless Ni-P/SiC nanocomposite coatings with small amounts of SiC nanoparticles for superior corrosion resistance and hardness, J. Mater. Eng. Perform., 24 (12), 4835-43. 2015.

9. [9] Islam M., Azhar M. R., Fredj N., Burleigh T. D., Oloyede O. R., Almajid A. A., Influence of SiO2 nanoparticles on hardness and corrosion resistance of electroless Ni-P coatings, Surf. Coat. Technol., 261, 141-8, 2015.
10. [10] Dong D., Chen X. H., Xiao W. T., Yang G. B., Zhang P. Y., Preparation and properties of electroless Ni-P-SiO2 composite coatings, Appl. Surf. Sci., 255 (15), 7051–5, 2009.
11. [11] Lee C. K., Chang C. S., Tan A. H., Yang C. Y., Lee S. L., Preparation of electroless nickel-phosphorous-TiO2 composite coating for improvement of wear and stress corrosion cracking resistance of AA7075 in 3.5% NaCl, Key Eng. Mater., 74-79, 656-657, 2015.
12. [12] Tamilarasan T. R., Rajendran R., Siva Shankar M., Sanjith U., Rajagopal G., Sudagar J., Wear and scratch behaviour of electroless Ni-P-nano-TiO2: Effect of surfactants, Wear, 346-347, 148-57, 2016.
13. [13] Balaraju J. N., Kalavati., Rajam K. S., Influence of particle size on the microstructure, hardness and corrosion resistance of electroless Ni-P-Al2O3 composite coatings, Surf. Coat. Technol., 200 (12-13), 3933-41, 2006.
14. [14] Alirezaei S., Vaghefi S. M., Urgen M., Saatchi A., Kazmanli K., Evaluation of structure and mechanical properties of Ni-P-Al2O3 nanocomposite coatings, J. Compos. Mater., 47, 3323-9, 2012.
15. [15] Leon O. A., Staia M. H., Hintermann H. E., Influence of the heat treatment on the tribological behavior of a Ni-P-BN(h) autocatalytic composite coating, Surf. Coat. Technol., 120-121, 641-5, 1999.
16. [16] Leon O. A., Staia M. H., Hintermann H. E., Deposition of Ni-P-BN (h) composite autocatalytic coatings, Surf. Coat. Technol., 108-109, 461-5, 1998.
17. [17] Leon O. A., Staia M. H., Hintermann H. E., Wear mechanism of Ni-P-BN(h) composite autocatalytic coatings. Surf. Coat. Technol., 200 (5–6), 1825-9, 2005.
18. [18] Leon O. A., Staia M. H., Hintermann H. E., High temperature wear of an electroless Ni-P-BN (h) composite coating, Surf. Coat. Technol., 164, 578-84, 2003.
19. [19] Farrokhzad M. A., High temperature oxidation behaviour of autocatalytic Ni-P-BN (h) coatings. Surf. Coat. Technol., 309, 390-400, 2017.
20. [20] Hsu C-I., Wang G-L. L. Ger M-D., Hou K-H., Corrosion Behaviour of Electroless Deposited Ni–P/BN(h) Composite Coating. Int. J. Electrochem. Sci., 11, 4352-61, 2016.
21. [21] Hsu C-II., Hou K-H., Ger M-D., Wang G-L. L., The effect of incorporated self-lubricated BN(h) particles on the tribological properties of Ni-P/BN(h) composite coatings, Appl. Surf. Sci., 357, 1727-35, 2015.
22. [22] Kocabaş M., Örnek C., Curioni M., Cansever N., Nickel fluoride as a surface activation agent for electroless nickel coating of anodized AA1050 aluminum alloy, Surf. Coat. Technol., 364, 231-8, 2019.
23. [23] Vitry V., Kanta A. F., Delaunois F., Application of nitriding to electroless nickel-boron coatings: Chemical and structural effects; mechanical characterization; corrosion resistance, Mater Des., 39, 269-78, 2012.
24. [24] Wu Y., Shen B., Liu L., Hu W., The tribological behaviour of electroless Ni-P-Gr-SiC composite, Wear, 261 (2), 201-7, 2006.
25. [25] Yin Z., Chen F., Effect of nickel immersion pretreatment on the corrosion performance of electroless deposited Ni-P alloys on aluminium, Surf. Coatings Technol., 228, 34-40, 2013.
26. [26] Alishahi M., Monirvaghefi S. M., Saatchi A., Hosseini S. M., The effect of carbon nanotubes on the corrosion and tribological behavior of electroless Ni-P-CNT composite coating, Appl. Surf. Sci., 258 (7), 2439-46, 2012.