Investigation of The Weldability of Aluminum Alloys with Mig Welding Method

Yıl 2021, Cilt: 4 Sayı: 1, 42 - 52, 30.06.2021

Ali Yürük , Yakup Kaya , Nizamettin Kahraman

Öz

In this study, the effect of welding parameters on mechanical and microstructural properties of aluminum alloys was investigated in gas metal arc welding (GMAW). 5754 AlMg alloys were used as base metals. Welding was performed at different welding voltaj and welding speeds and then tensile tests, hardness measurements, notch impact tests and bending tests were performed to determine the mechanical properties of welded joints. In addition, microstructural examinations were also done.

Anahtar Kelimeler

5754 AlMg Alloy, MIG Welding, Welding speed

Alüminyum Alaşımlarının MIG Kaynak Yöntemi ile Kaynak Edilebilirliğinin İncelenmesi

Öz

Bu çalışmada alüminyum alaşımlarının kaynak bölgesinin mekanik ve mikroyapı özelliklerine, MIG kaynak parametrelerinin etkileri incelenmiştir. Çalışmada kolay temin edilebilmesi sebebiyle 5000 serisi alüminyum ve alaşımları kullanılmıştır. Kaynak uygulaması farklı kaynak gerilimi ve kaynak hızlarında gerçekleştirilmiş ve daha sonra kaynaklı birleştirmelerin mekanik özelliklerini belirlemek için çekme deneyi, sertlik ölçümleri, çentik darbe deneyi ve eğme deneyleri yapılmıştır. Ayrıca mikroyapıda meydana gelen değişiklikleri belirlemek için de mikroyapı çalışmaları yapılmıştır.

Anahtar Kelimeler

5754 Alüminyum Alaşımı, MIG Kaynak Yöntemi, Kaynak Hızı