Effect of Acrylic/Polyester Fiber Addition on Mortar Mechanical and Insulation Properties

Yıl 2024, Cilt: 5 Sayı: 2, 43 - 57, 18.12.2024

Hakan Sarıkaya , Murat Yatkın

Öz

In this study, the compressive strength, flexural strength, thermal insulation, and microstructural properties of mortar samples containing an acrylic/polyester fiber mixture were analyzed. To this end, eight different mortar mixtures were prepared, incorporating 0%, 0.5%, 1%, and 1.5% acrylic/polyester fiber mixture by weight. In four of the mortar mixtures, 100% cement was used as the binder material, while in the other four mixtures, fly ash was preferred as a substitute for cement at a rate of 50% by weight. The effects of all prepared mortar samples on both mechanical and insulation properties were investigated in detail. According to the experimental results, it was observed that as the fiber content ratio increased, the compressive strengths decreased, while the flexural strengths and insulation values increased

Anahtar Kelimeler

Acrylic/Polyester fiber, Compressive strength, Flexural strength

Akrilik/Polyester Lif İlavesinin Harç Mekanik Ve Yalıtım Özeliklerine Etkisi

Öz

Bu çalışmada, akrilik/polyester lif karışımı içeren harç numunelerinin basınç dayanımı, eğilme dayanımı, ısı yalıtımı ve mikro yapı özellikleri analiz edilmiştir. Bu amaçla, harç numunelerine ağırlıkça %0, %0.5, %1 ve %1.5 akrilik/polyester lif karışımı içeren 8 farklı harç karışımları hazırlanmıştır. 4 farklı harç karışımında bağlayıcı malzeme içeriğinde %100 çimento kullanılırken, diğer 4 farklı karışımda ise bağlayıcı malzeme içeriğinde çimento yerine ağırlıkça %50 oranında da uçucu kül tercih edilmiştir. Hazırlanan tüm harç numunelerinin hem mekanik hem de yalıtım özellikleri üzerindeki etkileri ayrıntılı olarak araştırılmıştır. Deney sonuçlarına göre, lif katkı oranı arttıkça basınç dayanımlarının düştüğü, eğilme dayanımlarının ve yalıtım değerlerinin arttığı görülmüştür.

Anahtar Kelimeler

Akrilik/Polyester lifi, Basınç dayanımı, Eğilme dayanımı

Kaynakça

• Khan, M., McNally, C. A. (2023). Holistic review on the contribution of civil engineers for driving sustainable concrete construction in the built environment. Developments in the Built Environment, 16100273.
• Bostancı, L. (2022). Atık cam tozu içeren alkali-aktive edilmiş cüruf harçlarının mekanik, por yapısı, termal yalıtkanlık ve mikro yapı özellikleri. Politeknik Dergisi, 25(1): 75-87.
• Poletanovic, B., Katalin Kopecsko, K., Merta, I. (2024). Fibre hornification improves the long-term properties of hemp fibre-reinforced fly ash-based geopolymer mortar. Construction and Building Materials, 446, 137957.
• Ünal, M.T., Şimşek O. (2022) Çimento Harçlarında Optimum Uçucu Kül ve PVA Lif Oranının Belirlenmesi. Politeknik Dergisi, 25(2) : 477-489.
• Falkner, H., Huang, Z., Teutsch, M., (1995). Comparative Study of Plain and Steel Fibre Reinforced Concrete Graund Slab, Concrete International, 45-5.
• Craig, R. J. Parr, J. A. Germain, E. Mosquera, V. Kamilares, S. (1986). Fiber Reinforced Beams in Torsio , ACI Journal.
• Şimşek, S. 1997). Lifli Beton Üzerine Bir Çalışma, Gazi Üniversitesi Fen Bilimleri Enstitüsü, Ankara, Haziran.
• Korkut, F., Türkmenoğlu, Z.F. Taymuş, R.B., Güler, S. (2017). Çelik ve Sentetik Liflerin Kendiliğinden Yerleşen Betonların Taze Ve Mekanik Özellikleri Üzerine Etkisi, ÖHÜ Müh. Bilim. Derg. / OHU J. Eng. Sci., 6(2): 560- 570.
• Yılmaz, A. (2020). Advanced Composite Materials. Journal of Materials Science.
• Smith, B., & Jones, C. (2019). Reinforcement of Concrete with Synthetic Fibers. Construction Materials Journal.
• Doe, J. (2021). Durability of Fiber-Reinforced Concrete. International Journal of Civil Engineering
• TS EN 197-1, Çimento- Bölüm 1: Genel Çimentolar Bileşim, Özellikler ve Uygunluk Kriterleri, Türk Standartları Enstitüsü, Ankara.
• TS EN 12390-3, Beton - Sertleşmiş beton deneyleri - Bölüm 3: Deney numunelerinin basınç dayanımının tayini, Türk Standartları Enstitüsü, Ankara.
• TS EN 12390-5, Beton - Sertleşmiş beton deneyleri - Bölüm 5: Deney numunelerinin eğilme dayanımının tayini, Türk Standartları Enstitüsü, Ankara.
• ASTM C1113/C1113-09 (2009) Standard test method for thermal conductivity of refractories by hot wire (Platinum Resistance Thermometer Technique). ASTM International, West Conshohocken, PA
• TS EN 12390-3, Beton- Sertleşmiş Beton Deneyleri- Bölüm 3: Deney Numunelerinde Basınç Dayanımı Tayini”, Türk Standartları Enstitüsü, Ankara.
• TS EN 12390-4, Beton- Sertleşmiş Beton Deneyleri- Bölüm 4: Basınç Dayanımı- Deney Makinalarının Özellikleri”, Türk Standartları Enstitüsü, Ankara.
• TS EN 12390-5, Beton- Sertleşmiş Beton Deneyleri- Bölüm 5: Deney Numunelerinin Eğilme Dayanımı Tayini”, Türk Standartları Enstitüsü, Ankara.