Effect of Different Fillers and Concentrations on the Flexural Strength of Heat-Polymerized PMMA Denture Base Resin

Öz

Objective: The aim of the current study was to evaluate the effect of different nanofillers and their corresponding concentrations on the flexural strength of heat-polymerized PMMA denture base resin. Methods: A total of 110 PMMA specimens were produced according to ISO standards and divided into 11 groups (n = 10). PMMA was reinforced with titanium-dioxide (TiO₂), silicon-dioxide (SiO₂), graphitic carbon nitride (g-C₃N₄), multiwalled carbon nanotubes (MWCNTs), and cellulose nanofibrils (CNFs) at concentrations of 1 wt% and 2 wt%, while unreinforced PMMA served as the control group. A three-point bending assessment was utilized to measure the flexural strength. The results were put through analysis employing one-way ANOVA alongside Tukey's HSD post-hoc evaluations (α=.05). Results: Significant differences in flexural strength were observed among the groups (p<.05). The lowest mean flexural strength values were recorded for g-C₃N₄ (2%) (68.54 MPa) and MWCNTs (2%) (68.99 MPa). Within the TiO₂ groups, the 1% concentration (83.21 MPa) showed higher flexural strength than the 2% concentration (78.72 MPa), while CNF-reinforced PMMA demonstrated the highest flexural strength overall, with CNF (1%) demonstrating the maximum value (134.66 MPa), followed by CNF (2%) (129.94 MPa). Each experimental cohort surpassed the critical flexural strength standard specified by ISO 20795-1. Conclusions: The integration of nanofillers significantly affected the flexural strength of PMMA denture base resin. The reinforcing effect was strongly dependent on filler type and concentration. Among the tested materials, cellulose nanofibrils at 1 wt% provided the most effective reinforcement, whereas higher concentrations of several nanofillers adversely affected flexural strength.

Anahtar Kelimeler

• Polymethyl methacrylate
• denture bases
• nanoparticles
• flexural strength
• titanium dioxide.

Destekleyen Kurum

Atatürk University

Etik Beyan

Ethical approval of the study was received from the Committee for Ethics Research at the University of Atatürk (Date: 04/02/2026, Number: 05).

Farklı Nanodoldurucuların ve Konsantrasyonlarının Isıyla Polimerize Edilmiş PMMA Protez Kaide Rezininin Eğilme Dayanımına Etkisi

Öz

Amaç: Bu çalışmanın amacı, farklı nanodoldurucuların ve konsantrasyonlarının ısı ile polimerize edilmiş polimetil metakrilat (PMMA) protez kaide materyallerinin eğilme dayanımı üzerindeki etkisini değerlendirmektir. Yöntemler: Toplam 110 adet PMMA numunesi ISO standartlarına göre üretildi ve 11 gruba (n = 10) ayrıldı. PMMA, %1 ve %2 ağırlık konsantrasyonlarında titanyum dioksit (TiO₂), silicon dioksit (SiO₂), grafit karbon nitrit (g-C₃N₄), çok duvarlı karbon nanotüpler (MWCNT) ve selüloz nanofibriller (CNF) ile takviye edildi; takviyesiz PMMA ise kontrol grubu olarak kullanıldı. Eğilme dayanımı, üç nokta eğilme testi kullanılarak ölçüldü. Veriler tek yönlü ANOVA ve Tukey HSD post-hoc testleri kullanılarak analiz edildi (α=.05). Bulgular: Gruplar arasında eğilme dayanımında önemli farklılıklar gözlemlendi (p<.05). En düşük ortalama eğilme dayanımı değerleri g-C₃N₄ (%2) ve MWCNT'ler (%2) için kaydedildi. TiO₂ için, %1'lik grup %2'lik gruba göre daha yüksek eğilme dayanımı gösterdi. CNF takviyeli PMMA en yüksek eğilme dayanımını sergiledi; CNF (%1) maksimum değeri gösterirken, onu CNF (%2) izledi. Tüm gruplar ISO 20795-1 tarafından belirtilen minimum eğilme dayanımı gereksinimini aştı. Sonuç: Nanodoldurucuların eklenmesi, PMMA protez kaide materyallerinin eğilme dayanımını önemli ölçüde etkilemiştir. Güçlendirme etkisi, dolgu maddesinin türüne ve konsantrasyonuna büyük ölçüde bağlıydı. Test edilen malzemeler arasında, %1 ağırlık oranındaki selüloz nanofibriller en etkili güçlendirmeyi sağlarken, çeşitli nanodoldurucuların daha yüksek konsantrasyonları eğilme dayanımını olumsuz etkilemiştir.

Anahtar Kelimeler

• Polimetil metakrilat
• protez kaideleri
• nanodoldurucular
• eğilme dayanımı
• titanyum dioksit.

Destekleyen Kurum

Atatürk Üniversitesi

Etik Beyan

Çalışmanın etik onayı Atatürk Üniversitesi Araştırma Etik Kurulu'ndan alınmıştır (Tarih: 04/02/2026, Sayı: 05)

Kaynakça

1. Agnihotri, R., Gaur, S., & Albin, S. (2020). Nanometals in dentistry: Applications and toxicological implications—a systematic review. Biological Trace Element Research, 197, 70–88. https://doi.org/10.1007/s12011-019-01986-y
2. Aldegheishem, A., Aldeeb, M., Al-Ahdal, K., Helmi, M., & Alsagob, E. I. (2021). Influence of reinforcing agents on the mechanical properties of denture base resin: A systematic review. Polymers, 13(18), 3083. https://doi.org/10.3390/polym13183083
3. Altarazi, A., Haider, J., Alhotan, A., Silikas, N., & Devlin, H. (2023). 3D printed denture base material: The effect of incorporating TiO₂ nanoparticles and artificial ageing on the physical and mechanical properties. Dental Materials, 39(12), 1122–1136. https://doi.org/10.1016/j.dental.2023.10.005
4. Alzayyat, S. T., Almutiri, G. A., Aljandan, J. K., Algarzai, R. M., Khan, S. Q., Akhtar, S., Matin, A., & Gad, M. M. (2021). Antifungal efficacy and physical properties of poly(methyl methacrylate) denture base material reinforced with SiO₂ nanoparticles. Journal of Prosthodontics, 30(6), 500–508. https://doi.org/10.1111/jopr.13271
5. Ata, S. O., Akay, C., & Mumcu, E. (2023). The effects of metal nanoparticles incorporation on the mechanical properties of denture base acrylic resin. European Oral Research, 57(1), 36. https://doi.org/10.26650/eor.20231079531
6. Bacali, C., Badea, M., Moldovan, M., Sarosi, C., Nastase, V., Baldea, I., Chiorean, R. S., & Constantiniuc, M. (2019). The influence of graphene in improvement of physico-mechanical properties in PMMA denture base resins. Materials, 12(14), 2335. https://doi.org/10.3390/ma12142335
7. Cevik, P., & Yildirim-Bicer, A. Z. (2018). The effect of silica and prepolymer nanoparticles on the mechanical properties of denture base acrylic resin. Journal of Prosthodontics, 27(8), 763–770. https://doi.org/10.1111/jopr.12573
8. Chen, S., Yang, J., Jia, Y. G., Lu, B., & Ren, L. (2018). A study of 3D-printable reinforced composite resin: PMMA modified with silver nanoparticles loaded cellulose nanocrystal. Materials, 11(12), 2444. https://doi.org/10.3390/ma11122444

9. Di Carlo, S., De Angelis, F., Brauner, E., Pranno, N., Tassi, G., Senatore, M., & Bossù, M. (2020). Flexural strength and elastic modulus evaluation of structures made by conventional PMMA and PMMA reinforced with graphene. European Review for Medical and Pharmacological Sciences, 24(10), 5201–5208. https://doi.org/10.26355/eurrev_202005_21301
10. Gad, M. M., Abualsaud, R., Al-Thobity, A. M., Almaskin, D. F., Alzaher, Z. A., Abushowmi, T. H., Qaw, M. S., Akhtar, S., & Al-Harbi, F. A. (2020). Effect of SiO₂ nanoparticles addition on the flexural strength of repaired acrylic denture base. European Journal of Dentistry, 14(1), 19–23. https://doi.org/10.1055/s-0039-1701076
11. International Organization for Standardization. (2013). Dentistry—Base polymers—Part 1: Denture base polymers (ISO 20795-1:2013). https://www.iso.org/standard/62277.html
12. Karci, M., Demir, N., & Yazman, S. (2019). Evaluation of Flexural Strength of Different Denture Base Materials Reinforced with Different Nanoparticles. Journal of prosthodontics: official journal of the American College of Prosthodontists, 28(5), 572–579. https://doi.org/10.1111/jopr.12974
13. Kawaguchi, T., Lassila, L. V. J., Baba, H., Tashiro, S., Hamanaka, I., Takahashi, Y., & Vallittu, P. K. (2020). Effect of cellulose nanofiber content on flexural properties of a model, thermoplastic, injection-molded, polymethyl methacrylate denture base material. Journal of the Mechanical Behavior of Biomedical Materials, 102, 103513. https://doi.org/10.1016/j.jmbbm.2019.103513
14. Lee, J. H., Jo, J. K., Kim, D. A., Patel, K. D., Kim, H. W., & Lee, H. H. (2018). Nano-graphene oxide incorporated into PMMA resin to prevent microbial adhesion. Dental Materials, 34(4), e63–e72. https://doi.org/10.1016/j.dental.2018.01.019
15. Mohamed, P. A., Fahmy, A. E., & El Shabrawy, S. M. (2023). Three-dimensionally printed denture base resins modified by nanoglass particles and carbon nanotubes. The Journal of Prosthetic Dentistry, 130(5), 797.e1–797.e9. https://doi.org/10.1016/j.prosdent.2023.08.007
16. Morones, J. R., Elechiguerra, J. L., Camacho, A., Holt, K., Kouri, J. B., Ramírez, J. T., & Yacaman, M. J. (2005). The bactericidal effect of silver nanoparticles. Nanotechnology, 16(10), 2346–2353. https://doi.org/10.1088/0957-4484/16/10/059
17. Shahkar, L., Malek Khachatourian, A., & Nemati, A. (2024). Fabrication and characterization of PMMA denture base nanocomposite reinforced with hydroxyapatite and multi-walled carbon nanotubes. Diamond and Related Materials, 147, 111377. https://doi.org/10.1016/j.diamond.2024.111377
18. Sodagar, A., Bahador, A., Khalil, S., Saffar Shahroudi, A., & Zaman Kassaee, M. (2013). The effect of TiO₂ and SiO₂ nanoparticles on flexural strength of poly(methyl methacrylate) acrylic resins. Journal of Prosthodontic Research, 57(1), 15–19. https://doi.org/10.1016/j.jpor.2012.05.001
19. Vikram, S., & Chander, N. G. (2020). Effect of zinc oxide nanoparticles on the flexural strength of polymethyl methacrylate denture base resin. European Oral Research, 54(1), 31–35. https://doi.org/10.26650/eor.20200063
20. Wang, R., Tao, J., Yu, B., & Dai, L. (2014). Characterization of multiwalled carbon nanotube–polymethyl methacrylate composite resins as denture base materials. The Journal of Prosthetic Dentistry, 111(4), 318–326. https://doi.org/10.1016/j.prosdent.2013.07.017