AN INVESTIGATION INTO THE USE OF CLAY BEARING DIATOMITES OF KUTAHYA ALAYUNT REGION IN CEMENT PRODUCTION1

Öz

In this research, the use of clay bearing diatomites from Kütahya-Alayunt region in cement

production as puzzolanic materials was investigated. Cements were produced by adding

clay bearing dioatomites to the cement body by 5%, 10%, and 20% and grinding them

together with clinker materials. After the tests, it was found that 10% and 20% clayed

diatomite addition could be used in 42.5- class cement production. İf the strength of

portland cement clinker was about 50 N/mm2. By utilizing this material, less clinker4 produced at 1450 oC will be needed which means lower emission rates causing

environmental pollutions and a special type of cement can be obtained by using diatomite for lower specific gravity, heat and noise insulation

Anahtar Kelimeler

• Cement,Clinker,Diatomite,Puzzolans

KÜTAHYA-ALAYUNT BÖLGESİ KİLLİ DİYATOMİTLERİN ÇİMENTO ÜRETİMİNDE KULLANILABİLİRLİĞİNİN ARAŞTIRILMASI

Öz

Bu çalışmada, Kütahya–Alayunt bölgesi killi diyatomitlerinin katkılı çimento üretiminde puzolanik malzeme olarak kullanılabilirliği araştırılmıştır. Çimento bileşimine % 5, %10 ve %20 oranlarında katılan killi diyatomit, klinker ile birlikte öğütülerek çimentolar elde edilmiştir. Deneyler sonucunda % 10 ve % 20 killi diyatomit katkısının portland çimentosu klinkerinin dayanım değerlerinin 50 N/mm2 civarında olduğu taktirde 42,5 sınıfı çimento üretiminde kullanılabileceği tespit edilmiştir. Bu malzemenin kullanımı ile hem 1450 oC’de üretilen klinker kullanımı azaltılarak çevreye daha az emisyon verilecek hemde diyatomitin düşük özgül ağırlığı ile ısı ve ses izolasyonu yapabilmesi nedeni ile özel bir çimento tipi oluşturabilecektir.

Anahtar Kelimeler

• Diyatomit,Puzolan,Klinker,Çimento

Kaynakça

1. [1] Köktürk, U. 1997. “Endüstriyel Hammaddeler” Dokuz Eylül Üniversitesi Müh-Mim.Fak. Yayın No:205, İzmir, 64-68.
2. [2] M. G. Stamatakis, D. Fragoulis, G. Csirik, I. Bedelean and S. Pedersen. 2003 “Theinfluence of biogenic micro-silica-rich rocks on the properties of blendedcements” Cement and Concrete Composites, Volume 25, Issue 2, Pages 177-184
3. [3] D. Fragoulis, M. G. Stamatakis, D. Papageorgiou and E. Chaniotakis. 2005 “Thephysical and mechanical properties of composite cements manufactured withcalcareous and clayey Greek diatomite mixtures” Cement and Concrete Composites,Volume 27, Issue 2, Pages 205-209
4. [4] D. Fragoulis, M. G. Stamatakis, E. Chaniotakis and G. Columbus. 2004“Characterization of lightweight aggregates produced with clayey diatomite rocksoriginating from Greece” Materials Characterization, Volume 53, Issues 2-4, Pages307-316
5. [5] Aruntaş, H.Y., Albayrak, M., Saka, H.A., Tokyay, M., 1998 “Ankara-Kızılcahamamve Çankırı-Çerkeş yöresi diatomitlerinin özelliklerinin belirlenmesi” Turkey Journalof Engineering and Environmental Science, 22, TÜBİTAK, 337-343.
6. [6] Bentli, İ., 2002 “Kütahya-Alayunt diatomit cevherinin zenginleştirilmesi araştırılması”.4.Endüstriyel Hammaddeler Sempozyumu, TMMOB Maden Mühendisleri Odası,Eds: Köse, İzmir, 121-126,
7. [7] Bentli, İ., Ediz, N., Tatar, İ., 2004. “Beneficiation of Kutahya-Alayunt diatomite bycalcination” 10th International Mineral Processing Symposium, Ed: İpekoğlu, İzmir,183-189.
8. [8] Ediz, N., Tatar, İ., Bentli, İ., 2005. The use of raw and calcined diatomite in art-tilebodies. Turkey 19th International Mining Congress, Eds: Onur&Tanrıverdi,IMCET2005, 259-262.

9. [9] F.M. Lea, 1976 “The Chemistry of Cement and Concrete”, 3rd ed., Edward Arnold,Ltd. London, Reprinted in, p. 727. TS EN 196-1 Çimento Deney Metotları- Bölüm 1: Dayanım TS EN 196-2 Çimento Deney Metotları- Bölüm 2: Çimentonun Kimyasal Analizi TS EN 196-3 Çimento Deney Metotları- Bölüm 3: Priz Süresi ve Hacim GenleşmeTayini TS EN 196-6 Çimento Deney Metotları-Bölüm 6 :İncelik Tayini TS EN 196-7 Çimento Deney Metotları- Çimentodan NumuneAlma ve HazırlamaMetotları