This work has studied the influence of colemanite waste (CW), tincal waste (TW) and
Borax penta-hydrate waste (BW) on the physical properties of brick. Waste were replaced
by clay in amounts 5, 10, and 20 wt % of sample. Physical and mechanical properties of
the brick were investigated through a number of tests. It has been established that TW and
BW replacement considerably increases compressive strength of the brick. However CW
replacement has negative effects on the compressive strength. The results obtained were
compared with the Turkish Standards , and in general, were found to be within the limit. As
a result, TW and BW samples may be used in the production of brick.
Compressive Strength Shrinkage Tincal Ore Waste Water Absorption Brick
Bu çalışmada colemanit atığı, tincal atığı ve borakspentahidrat atıklarının tuğlanın fiziksel
özelliklerine etkisi çalışılmıştır. Atıklar 5%, %10 ve %20 oranında kil ile yer değiştirilerek
tuğlanın fiziksel ve mekanik özellikleri bir takım testlerle araştırılmıştır. Tincal ve
borakspentahidrat atıklarının tuğlanın basınç dayanımını artırdığı ve colemanit atığının
basınç dayanımı üzerine negatif etki yaptığı bulunmuştur. Elde edilen sonuçlar Türk
standartları Enstitüsünde belirtilen değerlerle karşılaştırılmış ve genelde standartlarla uyum
gösterdiği bulunmuştur. Sonuç olarak tincal ve borakspentahidrat atıkları tuğla üretiminde
kullanılabilir.