TiO2 FILMS WITH VARIOUS CRYSTAL STRUCTURES FOR SINGLE AND BILAYER PHOTOANODES OF DYE-SENSITIZED SOLAR CELLS

Yıl 2018, Cilt: 6 Sayı: 2, 235 - 242, 01.06.2018

Nursev Erdogan Jongee Park Abdullah Ozturk

Öz

Phase pure and composite TiO2nanopowders exhibiting various crystal structures (anatase, rutile and brookite) are used as photoanode in dye-sensitized solar cells. The nanopowders are deposited in paste form onto a conducting oxide glass using doctor blade method in single layer and bilayers. The highest solar efficiency achieved by the single layer photoanode composed of > 99 wt % anatase crystals was 2.86 %. The solar efficiency of 4.93 % has been harvested via bilayer photoanode built by applying a layer consisting 55 wt % anatase and 45 wt % rutile phase nanoparticles on top of the layer composed of a mixture of > 99 wt % anatase crystals. The improved photovoltaic performance is attributed to anatase dominated bottom layer which facilitates electron charge generation with high surface area and charge transport by proper crystal structure as well as synergistic effect of binary phase content of the photoanodes. The porous structure of top layer enhances diffusion of the I−/I3− electrolyte in the bilayer TiO2 photoanode.

Anahtar Kelimeler

Titanium dioxide, Dye-sensitized solar cells, Bilayer photoanode, Nanoparticles

Kaynakça

• Small Spacecraft Technology State of the Art, Mission Design Division, Ames Research Center, Moffett Field, California, 2015, NASA/TP–2015–216648/REV1.
• Jean J, Brown PR, Jaffo RL, Buonassisi T, Bulovié V. Pathways for solar photovoltaics, Energy and Environ Sci 2015; 4.
• O’Regan B, Gratzel M. A low-cost, high efficiency solar cell based on dye-sensitized colloidal TiO2 films. Nature 1991; 353: p.737.
• Ye M, Wen X, Wang M, Locozzia J, Zhang N, Lin C, Lin Z. Recent advances in dye-sensitized solar cells: from photoanodes, sensitizers and electrolytes to counter electrodes. Materials Today 2015; 18: 3.
• Li G, Richter CP, Milot RL, Cai L, Schmuttenmaer CA, Crabtree RH, Brudvig GW, Batista VS. Synergistic effect between anatase and rutile TiO2 nanoparticles in dye-sensitized solar cells. Dalton Trans., 2009; p.10078.
• Lekphet W, Ke TC, Su C, Li WR. Morphology control studies of TiO2 microstructures via surfactant-assisted hydrothermal process for dye-sensitized solar cell applications. Applied Surface Science 2016; 382: p. 15.
• Shen Z, Wang G, Tian H, Sunarso J, Liu L, Liu J, Liu S. Bi-layer photoanode films of hierarchical carbon-doped brookite-rutile TiO2 composite and anatase TiO2 beads for efficient dye-sensitized solar cells. Electrochimica Acta 2016; 216: p. 429.
• Liu G, Yan X, Chen Z, Wang X, Wang L, Lu GQ, Cheng HM. Synthesis of rutile–anatase core–shell structured TiO2 for photocatalysis. J Mater Chem 2009; 19: p.6590.
• Erdogan N, Ozturk A, Park J. Hydrothermal synthesis of 3D TiO2 nanostructures using nitric acid: characterization and evolution mechanism. Ceram Int 2016; 42: p. 5985.
• Ito S, Chen P, Comte P, Nazeeruddin MK, Liska P, Péchy P, Grätzel M. Fabrication of screen-printing pastes from TiO2 powders for dye-sensitised solar cells. Prog Photovolt 2007; Res. Appl; 15: 603.
• Yu H, Pan J, Bai Y, Zong X, Li X, Wang L. Hydrothermal Synthesis of a Crystalline Rutile TiO2 Nanorod Based Network for Efficient Dye-Sensitized Solar Cells. Chem Eur J 2013; 19: p.13569.
• Kambe S, Nakade S, Wada Y, Kitamura T, Yanagida S. Effects of crystal structure, size, shape and surface structural differences on photo-induced electron transport in TiO2 mesoporous electrodes. J Mater Chem 2002; 12: p.723
• Wang Q, Moser, JE, Grätzel M. Electrochemical Impedance Spectroscopic Analysis of Dye-Sensitized Solar Cells. J Phys Chem B 2005; 109: p.14945.