Effect of Microstructure on mechanical and Charpy impact properties offerrite-martensite dual phase API X52 pipeline Steel

Öz

The microstructural changes that occur during intercritical annealing treatment at 780°C of API X52 steel have been investigated. Three treatments were developed to produce dual phase (DP) microstructure: Intermediate Quenching Treatment/Air (IQ/A), Intermediate Quenching Treatment/Water (IQ/W) and Step Quenching Treatment (SQ).The IQ/W resulted in the formation of fine and fibrous martensite morphology uniformly distributed in the ferrite matrix. However, the IQ/A treatment showed a spherical network of martensite along the ferrite/ferrite grain boundaries. The SQ yielded blockly and banded martensite and ferrite morphology. The experimental results show that API X52 (DP) steel with finely dispersed microstructures (IQ/W) have higher Charpy impact properties and lower ductile–brittle transition temperature (DBTT)than (DP) steel with banded microstructures.A carefully conducted comparison of fracture surfaces of the representative specimens obtained after IQ and SQ treatments has been studied.

Anahtar Kelimeler

• Intercritical annealing,Dual-phase steel

Kaynakça

1. [1] R.O. Rocha, T.M.F. Melo, E.V. Pereloma, D.B. Santos, Microstructural evolution at the initial stages of continuous annealing cold rolled dual phases steel, Materials Science and Engineering: A, 391 ( 2005) 296-304.DOI:10.1016/j.msea.2004.08.081.
2. [2] M. Nishiyama, K. Park, N. Nakada, T. Tsuchiyama, Effect of the martensite distribution on the strain hardening and ductile fracture behaviors in dual-phase steel, Materials Science and Engineering: A, 604 (2014) 135-141.DOI:10.1016/j.msea.2014.02.058.
3. [3] A. Bag, K.K Ray, E.S. Dwarakadasa, Influence of martensite content and morphology on tensile and impact properties of high-martensite dual-phase steels, Metallurgical Transaction A 30 (1999) 1193–1202. DOI:10.1007/s11661-999-0269-4.
4. [4] H. Seyedrezai, A.K. Pilkey, J.D. Boyd, Effect of pre-ic annealing treatments on the final microstructure and work hardening behavior of a dual-phase steel, Materials Science and Engineering: A, 594 (2014) 178-188. DOI:10.1016/j.msea.2013.11.034.