Synthesis of Ti-TiAl3 Composite by Resistive Sintering

Abstract

In the present work, Ti-TiAl₃ metallic-intermetallic in situ composites were synthesized by one step resistive sintering method. Process time had been completed in 90 second using 1.5-1.7 Volt and 2000 Amper direct current. Ti and Al elemental powders were mixed by the stoichiometric ratio corresponding to the TiAl₃ intermetallic phases' with molar proportion of 1:3. We aimed to obtain some residual ductile Ti phase as well as the TiAl₃ major phase in structure. XRD analyses detected the only phases in the composite were Ti and TiAl₃. TiAl₂ phase also detected as trace peak in the XRD Chart. SEM examinations showed a dense microstructure with low amount of porosity. The relative density of the sample measured according to Archimedes’ principle was 98,7%, and the microhardness of the sample was about 455±20 HV.

Keywords

• Synthesis of Ti-TiAl3 Composite by Resistive Sintering,Ti-Al intermetallics

Kaynakça

1. [1] M. H. Erdoğan, M. İpek, G. F. Ç. Efe, S. Zeytin, C. Bindal, "Toz Metalurjisi Yöntemi ile Niyobyum Aluminid Üretimi ve Karakterizasyonu," in 14.th International Materials Symposium, IMSF 2012, Pamukkale University, Denizli, Turkey.
2. [2] J. Cao, J. Feng, Z. Li, Effect of reaction heat on reactive joining of TiAl intermetallics using Ti–Al–C interlayers, Scripta Materialia. 57, 421, (2007). DOI: 10.1016/j.scriptamat.2007.04.048.
3. [3] N. Cinca, C. R. C. Lima, J. M. Guilemany, An overview of intermetallics research and application: Status of thermal spray coatings, Journal of Materials Research and Technology. 2, 75, (2013). DOI: 10.1016/j.jmrt.2013.03.013.
4. [4] W. Chen, H. Xiao, Z. Fu, S. Fang, D. Zhu, Reactive hot pressing and mechanical properties of TiAl3/Ti3AlC2/Al2O3 in situ composite, Materials & Design. 49, 929, (2013). DOI: 10.1016/j.matdes.2013.02.053.
5. [5] R. Orrù, R. Licheri, A. M. Locci, A. Cincotti, G. Cao, Consolidation/synthesis of materials by electric current activated/assisted sintering, Materials Science and Engineering: R: Reports. 63, 127, (2009). DOI: 10.1016/j.mser.2008.09.003.
6. [6] T. Yener, S. Okumus, S. Zeytin, In Situ Formation of Ti-TiAl 3 Metallic-Intermetallic Composite by Electric Current Activated Sintering Method, Acta Physica Polonica A. 127, 917, (2015). DOI: 10.12693/APhysPolA.127.917.
7. [7] T. Yener, S. Zeytin, Synthesis And Characterization Of Metallic-Intermetallic Ti-TiAl3, Nb-Ti-TiAl3 Composites Produced With Electric-Current-Activated Sintering (ECAS), Materiali in tehnologije. 48, 847, (2014). DOI: UDK 66.017:621.762.5.
8. [8] T. Yener, S. C. Yener, and S. Zeytin, “Electromagnetic-shielding effectiveness and fracture behavior of laminated (Ni–NiAl3) composites,” Mater. Tehnol., vol. 50, no. 6, pp. 899–902, 2016.

9. [9] T. D. Huy, H. Fujiwara, R. Yoshida, D. T. Binh, H. Miyamoto, Microstructure and Mechanical Properties of TiAl3/Al2O3 in situ Composite by Combustion Process, Materials Transactions. 55, 1091, (2014). DOI: 10.2320/matertrans.Y-M2014823.