Recycling and Characterization of Metallic Chips Using Powder Metallurgy

Öz

In this study, a new metal matrix composite material was produced by sintering from cast iron and bronze shavings made by recycling melting method. In the production of metal matrix composite material, 90% CuSn10 as a matrix material and 10% GGG40 cast iron as a reinforcement material were used. The chips having the same dimensions were mixed in a homogeneous mixture and pre-formed under a pressure of 1146 MPa and then sintered at 875 °C. The mechanical properties and porosity of the produced materials are characterized and the mechanical properties are compared with the mechanical properties of the bronze material in bulk state. According to the results, the mechanical properties of the material produced by the sintering method are very close to that of the bronze material in the bulk state.

Anahtar Kelimeler

• recycling,metal chips,sintering

Kaynakça

1. [1] S. Szezepanik, T. Sleboda, The influence of the hot deformation and heat treatment on the properties of P/M AI-Cu composites, Journal of Materials Processing Technology 60 (1996) 729-733
2. [2] W. Chmura, J. Gronostajski, Mechanical and tribological properties of aluminium-base composites produced by there cycling of chips, Journal of Materials Processing Technology 106 (2000) 23±27http://dx.doi.org/10.1016/S0924-0136 (00)00632-4
3. [3] J. Gronostajski, H.Marciniak, A. MatuszakNew methods of aluminium and aluminium-alloy chips recycling, Journal of Materials Processing Technology106 (2000) 34±39 http://dx.doi.org/10.1016/S0924-0136 (00)00634-8
4. [4] Shuyan Wua, ZeshengJi, Tielei Zhanga, Microstructure and mechanical properties of AZ31B magnesium alloy recycled by solid-state process from different size chips, Journal of Materials Processing Technology 209 (2009) 5319–5324
5. [5] J. Gronostajski, A. Matuszak, The recycling of metals by plastic deformation: an example of recycling of aluminium and its alloys chips, Journal of Materials Processing Technology 92±93 (1999) 35±41 http://dx.doi.org/10.1016/S0924-0136 (99)00166-1
6. [6] Mohamed Ibrahim Abdel Aal, Eun Yoo Yoon, Hyoung Seop Kim, Recycling of AlSi8Cu3 alloy chips via high pressure torsion, Materials Science & Engineering A, 560(2013) 121–128
7. [7] Maoliang Hu, Zesheng Ji, Xiaoyu Chen, Zhenkao Zhang Effect Of Chip Size On Mechanical Property And Microstructure Of Az91d Magnesium Alloy Prepared By Solid State Recycling, Materials Characterization 59(2008), 385–389.