Investigation of the Microstructure and Mold Life of Borided AISI 5630 Bims Mold

Öz

In this study, boriding was investigated on the surface of 5630 steel bims mold by using pack cementation diffusion method. For this purpose, a mixture of Al2O3, B4C and FeW and 10% NaBF4 was used as coating powder, and the AISI 5630 steel surface, which was the substrate material, was coated with the pack cementation diffusion method at 1000 °C for 4 hours and at 950 °C for 4 hours. The successfully obtained coated samples were sectioned and their coating morphologies, thicknesses and microhardness were examined. The phase structures formed on the coating surface were obtained by the X-Ray Diffraction method (XRD) and the Fe2B layer assessed by optical microscope and micro-hardness testing. As a result of the study, the lowest coating thickness was obtained on the sample coated at 950 °C for 4 hours. Although the highest coating thickness was obtained on the sample coated at 1000 °C for 4 hours. As a result of the microhardness analysis, it was observed that the hardness of the coating layer was approximately 5 times higher (2416 HV) than the substrate material.

Anahtar Kelimeler

• Bims Mold
• Boriding
• Pack cementation

Kaynakça

1. [1] Toklu, K., “Pomza taşından üretilen bims blok kalitesinin artırılma olanaklarının araştırılması”, Yüksek Lisans Tezi, İstanbul Üniversitesi, Fen Bilimleri Enstitüsü, İstanbul, 2009.
2. [2] Ömer A., “Bor Madeninin Stratejil Açıdan İncelenmesi”, Yüksek Lisans, Tezi, Dumlupınar Üniversitesi, Sosyal Bilimler Enstitüsü, Kütahya, 2004.
3. [3] Gündüz, L., Hafif beton olarak pomza, I. Isparta Pomza, 1998.
4. [4] Gündüz L., Şapcı N. Ve Davraz M., “Pomza madenciliği, endüstrisi ve türkiye açısından önemi (gelişen yeni bir sektör)”, Türkiye 19. Madencilik Kongresi ve Fuarı, IMCET2005, İzmir, Türkiye, 9 - 12 Haziran 2005, ss.397- 408
5. [5] Çevikbaş, A., İlgün,F., “Türkiye pomza yataklarının jeolojisi ve ekonomisi”, I. Isparta Pomza Sempozyumu, Isparta: SDÜ,1997, s13-18
6. [6] Yiğitbaşıoğlu, H., “Türkiye için önemli bir maden: bor.” Coğrafi Bilimler Dergisi, 2004, 2(2), 13-25. https://doi.org/10.1501/Cogbil_0000000046
7. [7] Yücel, A., “Dünyadaki başlıca bor yatakları, üretimi, pazarlaması ve Türkiye’nin önemi”, Hacettepe Üniversitesi, 2010.
8. [8] Arzum ULUKÖY, Ahmet Çetin CAN. Çeliklerin Borlanması. Journal Of Engıneerıng Scıences. 2006 : 12 : 2 : 189-198

9. [9] Çalık, A., Delikanlı, K., Uzun. A., “Ç1035 Çeliğin Borlama Özelliklerinin İncelenmesi” Il.Uluslararası Bor Sempozyumu, Eskişehir, 2004