THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD
Öz
In this study, the effects of high welding speed on microstructure and mechanical property of dissimilar welded components (AISI 430 ferritic stainless steel and AISI 304 austenitic stainless steel) by CO2 laser welding was carried out. Laser beam welding experiments were carried out under argon and helium atmospheres at 2250 W constant heat input and 100-200-300 cm/min. welding speeds. The microstructures of the welded joints and the heat affected zones (HAZ) were examined by optical microscopy, SEM, EDS and X-Ray analysis. The tensile strength of the welded joints was measured. The result of this study indicated that; the width of welding zone became much thinner depending on the increased welding speed. Tensile strength values also confirmed this result. The best properties were observed at the specimens welded under helium atmosphere, at 100 cm/min welding speed.
Anahtar Kelimeler
Ayrıntılar
Birincil Dil
Türkçe
Konular
-
Bölüm
-
Yayımlanma Tarihi
1 Mart 2010
Gönderilme Tarihi
8 Ağustos 2014
Kabul Tarihi
-
Yayımlandığı Sayı
Yıl 2010 Cilt: 5 Sayı: 2
APA
Çalıgülü, U., Taşkın, M., & Dikbaş, H. (2010). THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD. Technological Applied Sciences, 5(2), 160-177. https://doi.org/10.12739/10.12739
AMA
1.Çalıgülü U, Taşkın M, Dikbaş H. THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD. Technological Applied Sciences. 2010;5(2):160-177. doi:10.12739/10.12739
Chicago
Çalıgülü, Uğur, Mustafa Taşkın, ve Halil Dikbaş. 2010. “THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD”. Technological Applied Sciences 5 (2): 160-77. https://doi.org/10.12739/10.12739.
EndNote
Çalıgülü U, Taşkın M, Dikbaş H (01 Mart 2010) THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD. Technological Applied Sciences 5 2 160–177.
IEEE
[1]U. Çalıgülü, M. Taşkın, ve H. Dikbaş, “THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD”, Technological Applied Sciences, c. 5, sy 2, ss. 160–177, Mar. 2010, doi: 10.12739/10.12739.
ISNAD
Çalıgülü, Uğur - Taşkın, Mustafa - Dikbaş, Halil. “THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD”. Technological Applied Sciences 5/2 (01 Mart 2010): 160-177. https://doi.org/10.12739/10.12739.
JAMA
1.Çalıgülü U, Taşkın M, Dikbaş H. THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD. Technological Applied Sciences. 2010;5:160–177.
MLA
Çalıgülü, Uğur, vd. “THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD”. Technological Applied Sciences, c. 5, sy 2, Mart 2010, ss. 160-77, doi:10.12739/10.12739.
Vancouver
1.Uğur Çalıgülü, Mustafa Taşkın, Halil Dikbaş. THE EFFECTS OF HIGH WELDING SPEED ON MICROSTRUCTURE AND MECHANICAL PROPERTY OF DISSIMILAR WELDED COMPONENTS (AISI 430–AISI 304) BY CO2 LBW METHOD. Technological Applied Sciences. 01 Mart 2010;5(2):160-77. doi:10.12739/10.12739