The Effect of Peptizing Agent Concentration on Processing and Properties of Alumina Based Catalyst Support

Abstract

Gamma alumina (γ-Al2O3) has drawn attention as a support material for heterogeneous catalysts extensively used in the oil and gas industry due to its superior properties. Boehmite (AlOOH) is an industrially accepted and well-known precursor to produce gamma alumina-based support. The process additions such as nitric acid (HNO3) are commonly used in shaping process of alumina to control textural, mechanical and structural properties of final catalyst support. In this work, gamma alumina precursor boehmite was peptized by nitric acid at molar ratio of HNO3/AlOOH ranging from 0 to 0.054. With addition of nitric acid, extrusion paste showed higher plasticity up to 0.017 mole of HNO3/AlOOH. The addition of more than this point led to an inhomogenity of extrusion paste caused by hard and brittle structure caused by the formation of aluminum nitrate salts. Also, higher mechanical strength was observed for samples peptized with lower nitric acid concentration because of effective deagglomeration by peptization. The pore size of catalyst support pellets increased up to an acid/ boehmite molar ratio of 0.017 by peptizing of boehmite. However, beyond this point pore size decreased due to dissolution of boehmite.

Keywords

• Catalyst Support
• Gamma Alumina
• Peptizing
• Extrusion

References

1. [1] A. Glotov, E. Karakhanov, “Heterogeneous Catalysts for Petrochemical Synthesis and Oil Refining,” Catalysts, vol. 11, no. 5, pp.602, 2021.
2. [2] E. Vitz. (2022, Dec. 11). Heterogeneous Catalysis [Online]. Available: 18.12: Heterogeneous Catalysis- Chemistry LibreTexts
3. [3] Y. Pan, X. Shen, L. Yao, A. Bentalib, Z. Peng, “Active sites in heterogeneous catalytic reaction on metal and metal oxide: theory and practice,” Catalysts, vol. 8, no. 10, pp. 78, 2018.
4. [4] A. Hagemeyer, A.F. Volpe, Encyclopedia of Condensed Matter Physics. Academic Press, 2005.
5. [5] K. Y. Paranjpe, “Alpha, Beta and Gamma alumina as catalyst,” Pharma Innov, vol. 6, no. 11, pp. 236-238, 2017.
6. [6] P. Alphonse, M. Courty, “Structure and thermal behavior of nanocrystalline boehmite,” Thermochimica acta, vol. 425, no. 1-2, pp. 75-89, 2005.
7. [7] C. Kozicki, C. Carlson. (2022, Dec. 11). Why Agglomerate Powder? [Online]. Available: Why Agglomerate Powder? (feeco.com)
8. [8] M. Al-Ani, M. Al-Dahhan, “Effect of catalyst shape on pressure drop and liquid holdup in a pilot plant trickle bed reactor,” Fuel, vol. 284, pp. 118860, 2021.

9. [9] K. P. de Jong, Synthesis of solid catalysts. John Wiley & Sons, 2009.
10. [10] S. Devyatkov, N. V. Kuzichkin, D. Murzin, “On comprehensive understanding of catalyst shaping by Extrusion,” Chemistry Today, vol. 33, no. 6, pp. 57-64, 2015
11. [11] J. A. Schwarz, C. I. Contescu, Surfaces of nanoparticles and porous materials. CRC press, 1999.
12. [12] M. Dronova, “Study of concentrated boehmite suspensions containing anisotropic colloidal particles: phase diagram, structure and rheology-Application to membrane separation processes,” Ph.D. dissertation, Sorbonne Université, 2021.
13. [13] N. van Garderen, F. J. Clemens, C. G. Aneziris, T. Graule, “Improved γ-alumina support based pseudo-boehmite shaped by micro-extrusion process for oxygen carrier support application,” Ceramics International, vol. 38, no. 7, pp. 5481-5492, 2012.
14. [14] G. T. Whiting, S. Chung, D. Stosic, A. D. Chowdhury, L. van der Wal, D. Fu, J. Zecevic, A. Travert, K. Houben, M. Baldus, B. M. Weckhuysen, “Multiscale mechanistic insights of shaped catalyst body formulations and their impact on catalytic properties,” ACS Catalysis, vol. 9, no. 6, pp. 4792-4803, 2019.
15. [15] W. C. Cheng, R. G. Donnelly, “Surfactants in acid-peptized catalyst compositions,” U.S. Patent 4705767, November 10 1987.
16. [16] K. W. Jun, Y. J. Lee, S. M. Kim, J. Y. Kim, “Method of preparing boehmite and gamma-alumina with high surface area,” U. S. 11886367, September 5 2012.
17. [17] F. Karouia, M. Boualleg, M. Digne, P. Alphonse, “The impact of nanocrystallite size and shape on phase transformation: Application to the boehmite/alumina transformation,” Advanced Powder Technology, vol. 27, no. 4, pp. 1814-1820, 2016.
18. [18] S. Lowell, J. E. Shields, Powder Surface Area and Porosity: Second Edition. Chapman and Hall, 1984.
19. [19] J. M. Drouin, T. Chopin, P. Nortier, H. Van Damme, “Rheology and structure of peptized boehmite pastes,” Journal of colloid and interface science, vol. 125, no. 1, pp. 314-326, 1988.
20. [20] Sasol. (2022, Dec. 11). High Purity Aluminas [Online]. Available: https://products.sasol.com/pic/products/home/categories/high-purity-aluminas/index.html
21. [21] S. Lamouri, M. Hamidouche, N. Bouaouadja, H. Belhouchet, V. Garnier, G. Fantozzi, J. F. Trelkat, “Control of the γ-alumina to α-alumina phase transformation for an optimized alumina densification,” Boletín de la Sociedad Española de cerámica y vidrio, vol. 56, no. 2, pp. 47-54, 2017.
22. [22] K. Wefers, C. Misra, “Oxides and hydroxides of aluminum,” Alcoa Technical Paper, no. 19, 1987.
23. [23] L. Sharifi, M. Beyhaghi, T. Ebadzadeh, E. Ghasemi, “Microwave-assisted sol–gel synthesis of alpha alumina nanopowder and study of the rheological behavior,” Ceramics International, vol. 39, no. 2, pp. 1227-1232, 2013.
24. [24] Y. V. Vatutina, K. A. Nadeina, O. V. Klimov, M. O. Kazakov, I. G. Danilova, S. V. Cherepanova, A. S. Noskov, “Peptization of alumina by ammonia to adjust catalytic properties of NiMo/B-Al2O3 hydrotreating catalysts,” Catalysis Today, no. 375, pp. 377-392, 2021.
25. [25] V. Y. Tregubenko, I. E. Udras, V. A. Drozdov, A. S. Belyi, “Effect of pseudoboehmite peptization by organic acids on texture characteristics of obtained aluminum oxides,” Russian journal of applied chemistry, vol. 84, pp. 9-16, 2011.