USE OF HEMATITE MINERAL AS FILLER IN ASPHALT CONCRETE

Öz

In order to increase the strength of bituminous hot mixes (HMA) under heavy axle loads and to reduce their high costs, the search for an alternative to the pavement material is increasing day by day. In this study, the usability of hematite mineral as filler material in HMA was investigated. For this purpose, the optimum bitumen amount (OBA) was calculated by preparing mixtures with limestone aggregate at the rates of 3.5%, 4%, 4.5%, 5%, 5.5% and 6%. OBA was determined by applying the same procedure for HMA, which is formed by replacing limestone filler with hematite. In the continuation of the study, HMA samples containing both limestone filler material and hematite filler material were prepared with their own OBA values, and their performance properties were evaluated by Marshall stability (MS) test. Practical specific gravity value (Dp), void volume value (Vh), voids in mineral aggregate (VMA), voids filled with bitumen (Vf), MS and flow values of samples containing hematite filler material were compared with the sample containing limestone filler and the specification limit values and as a result, it was concluded that hematite can be used as filler material in HMA.

Anahtar Kelimeler

• Hot mix asphalt
• hematite mineral
• Marshall stability

HEMATİT MİNERALİNİN ASFALT BETONDA FİLLER OLARAK KULLANIMI

Öz

Bitümlü sıcak karışımların (BSK) ağır dingil yükleri altındaki dayanımını artırmak aynı zamanda yüksek maliyetini düşürebilmek için kaplama malzemesine alternatif arayışı her geçen gün artmaktadır. Bu çalışmada, hematit mineralinin BSK’da filler malzemesi olarak kullanılabilirliği araştırılmıştır. Bu amaçla %3.5, %4, %4.5, %5, %5.5 ve %6 oranlarında kireçtaşı agrega ile karışımlar hazırlanarak optimum bitüm miktarı (OBM) hesaplanmıştır. Kireçtaşı fillerin hematit ile yer değiştirilmesiyle oluşan BSK için de aynı prosedür uygulanarak OBM belirlenmiştir. Çalışmanın devamında hem kireçtaşı filler içeren BSK hem de hematit filler içeren BSK numuneleri kendi OBM değerleriyle hazırlanmış, Marshall stabilite (MS) deneyi ile performans özellikleri değerlendirilmiştir. Hematit filler içeren numunelerin pratik özgül ağırlık değeri (Dp), boşluk yüzdesi (Vh), agregalar arası boşluk yüzdesi (VMA), bitümle dolu boşluk yüzdesi (Vf), MS ve akma değeri kireçtaşı filler içeren numuneyle ve şartname sınır değerleri ile karşılaştırılmış ve hematitin BSK’da filler malzeme olarak kullanılabileceği sonucuna varılmıştır.

Anahtar Kelimeler

• Bitümlü sıcak karışım
• Hematit minerali
• Marshall stabilitesi

Kaynakça

1. Acar, S.O., Tapkın, S., 1998. Portland Çimentosu Kullanılarak Hazırlanan Marshall Numunelerinin Özelliklerinin İncelenmesi, Asfalt’98, 2. Ulusal Asfalt Sempozyumu, Ankara, 95-104.
2. Ahmedzade, P., Sengoz, B., 2009. Evaluation of Steel Slag Coarse Aggregate in Hot Mix Asphalt Concrete. Journal of Hazardous Materials, 165, 300-305.
3. Al-Hdabi, A., 2016. Laboratory Investigation on The Properties of Asphalt Concrete Mixture with Rice Husk Ash as Filler. Construction and Building Materials, 126, 544-551.
4. Asthana, G., Choudhary, J., Kumar, B., Gupta, A., 2020. Experimental Investigation of Waste Glass Powder as Filler in Asphalt Concrete Mixes. In Recent Developments in Waste Management: Select Proceedings of Recycle, Springer Singapore, 261-270.
5. ASTM C 127-88. 1992. Test Method for Specific Gravity and Adsorption of Coarse Aggregate. USA: Annual Book of ASTM Standards.
6. ASTM C 128-88. 1992. Test Method for Specific Gravity and Adsorption of Fine Aggregate. USA: Annual Book of ASTM Standards.
7. ASTM C 131-96. 1996. Standard Test Method for Resistance to Abrasion of Small Size Coarse Aggregate by Use of The Los Angeles Machine. Annual Book of ASTM Standards.
8. ASTM D5. 1992. Standard Test Method for Penetration of Bituminous Materials. Annual Book of ASTM Standards USA.

9. ASTM D36. 1992. Standard Test Method for Softening Point of Bitumen (Ring-and-Ball Apparatus), Annual Book of ASTM Standards USA.
10. ASTM D70. 1992. Standard Test Method for Density of Semi-Solid Bituminous Materials (Pycnometer Method). Annual Book of ASTM Standards USA.
11. Chen, M.Z., Lin, J.T., Wu, S.P., Liu, C.H., 2011. Utilization of Recycled Brick Powder as Alternative Filler in Asphalt Mixture. Construction and Building Materials, 25, (4), 1532-1536.
12. Islam, S.S., Ransinchung, G.D., Choudhary, J., 2021. Analyzing the Effect of Waste Jarosite as an Alternative Filler on the Engineering Properties of Asphalt Mixes. Construction and Building Materials, 270, 121466.
13. Gedik, A., Selcuk, S., Lav, A.H., 2021. Investigation of Recycled Fluorescent Lamps Waste as Mineral Filler in Highway Construction: A Case of Asphaltic Pavement Layers. Resources, Conservation and Recycling, 168, 105290.
14. Kaplan, A.N., 2021. Agrega ve Reçine Tipinin Polimer Betonun Performansı Üzerine Etkileri. Süleyman Demirel Üniversitesi, Fen Bilimleri Enstitüsü, Doktora Tezi, 216s., Isparta.
15. Karayolları Genel Müdürlüğü. 2013. Karayolları Teknik Şartnamesi. Ankara.
16. Maden Teknik Arama Genel Müdürlüğü, 2017. Dünyada ve Türkiye’de Demir. Fizibilite Etütleri Daire Başkanlığı, Eylül.
17. Modarres, A., Rahmanzadeh, M., Ayar, P., 2015. Effect of Coal Waste Powder in Hot Mix Asphalt Compared to Conventional Fillers: Mix Mechanical Properties and Environmental Impacts. Journal of Cleaner Production, 91, 262-268.
18. Morova, H.V., 2022. Eticol-43 Bor Mineralinin Asfalt Betonda Filler Olarak Kullanımı. Uluslararası Sürdürülebilir Mühendislik ve Teknoloji Dergisi, 6, (2), 85-92.
19. Önal, M.A., Karaca, S., 1990. Asfalt Betonu ve Diğer Karışım Tipleri İçin Karışım Dizayn Metotları. Karayolları Genel Müdürlüğü Teknik Araştırma Dairesi Başkanlığı, Ankara.
20. Pasandín, A. R., Pérez, I., Ramírez, A., Cano, M.M., 2016. Moisture Damage Resistance of Hot-Mix Asphalt Made with Paper Industry Wastes as Filler. Journal of Cleaner Production, 112, 853-862.
21. Serin, S., Önal, Y., Kayadelen, C., Morova, N. 2023. Utilization of Recyclable Concrete and Ceramic Waste as Filling Material in Hot Mix Asphalt. Periodica Polytechnica Civil Engineering, 67, (3), 846-854.
22. Shishehboran, M., Ziari, H., Korayem, A.H., Hajiloo, M., 2021. Environmental and Mechanical Impacts of Waste Incinerated Acidic Sludge Ash as Filler in Hot Mix Asphalt. Case Studies in Construction Materials, 14, E00504.
23. Uzun, İ., Terzi, S., 2012. Evaluation of Andesite Waste as Mineral Filler in Asphaltic Concrete Mixture. Construction And Building Materials, 31, 284-288.
24. Zhang, J., Sun, C., Li, P., Liang, M., Jiang, H., Yao, Z., 2019. Experimental Study on Rheological Properties and Moisture Susceptibility of Asphalt Mastic Containing Red Mud Waste as a Filler Substitute. Construction and Building Materials, 211, 159-166.