Çeşitli içeceklere maruz bırakılan kompozit rezinlerin ağartıcı diş macunu ile fırçalandıkdan

Abstract

Aim: The aim of this study was the microroughness evaluation of composite resin samples which are exposed to various types of drinks after brushing with whitening toothpaste. Material and Method: As acidic drinks coke, orange juice, sport drink, green tea, apple tea, green tea + lemon tea; as resin restorative materials Tetric, Premise and Filtek Z – 250; as whitening toothpaste Plus White were used during the study. 28 samples were prepared as 5 mm in diameter and 2 mm in thickness from every material. For three composite resin groups; we had 84 samples, totally. Every sample was immersed within the asidic drinks at room temperature for 3h/ day during 1 week. The control group samples were stored at % 0,9 isotonic sodium chloride without subjecting to any cycling. This process was repeated for 7 days, by renewing the used asidic drinks every day. The samples were brushed every day with brushing machine, after removing asidic drinks. After the samples were dried at the end of 7 days, surface roughness was measured by using (Surftest 211.Mitutoyo, Japan) profilometer equipment. Results: When surface roughness values of all materials has been examined, no significant difference has been actuarially observed among the roughness values of the composite samples kept into 0.9% isotonic sodium chloride (p>0.05); whereas, it has been determined that sports drink significantly causes more roughness than the other drinks in composite resin samples (p<0.05). It has been determined that, actuarially, Premise samples kept into sports drink are significantly more rough than Tetric and Filtek Z-250 (p<0.05). Conclusion: After being subjected to acidic beverages brushing with whitening toothpastes, composite resin samples were observed to cause microroughness.

Keywords

• Surface roughness, esthetics restorative materials, acidic drinks, whitening toothpaste

Çeşitli içeceklere maruz bırakılan kompozit rezinlerin ağartıcı diş macunu ile fırçalandıkdan

Abstract

Amaç: Bu çalışmanın amacı, çeşitli tipteki içeceklere maruz bırakılan kompozit rezin örneklerinin ağartıcı diş macunu ile fırçalandıktan sonra mikropürüzlülüğünün değerlendirilmesidir. Gereç ve Yöntem: Çalışmada; asitli içecek olarak kola, portakal suyu, sporcu içeceği, yeşil çay, elma çayı, yeşil çay + limon çayı; dolgu materyalleri olarak Tetric, Premise (Dentin) ve Filtek Z – 250; diş macunu olarak Plus White kullanıldı. Her bir materyalden 5 mm çapında ve 2 mm kalınlığında 28 adet örnek hazırlandı. Üç kompozit rezin grubu için toplamda 84 örnek elde edildi. Her bir örnek oda sıcaklığında 24 saatte 3 saat olacak şekilde asidik içecekler içinde bekletildi. Kontrol grubundaki örnekler ise döngüye tabi tutulmaksızın % 0,9 izotonik sodyum klorür içerisinde saklandı. Bu işlem 7 gün boyunca, çalışmada kullanılan asidik içecekler her gün yenilenerek tekrarlandı. Örnekler her gün asidik içecekler içinden çıkartıldıktan sonra fırçalama makinesiyle fırçalandı. 7 gün sonunda örnekler kurutulduktan sonra profilometre (Surftest 211.Mitutoyo, Japonya) cihazı kullanılarak yüzey pürüzlülüğü ölçüldü. Sürekli değişkenler bakımından dağılımların normalliği Shapiro-Wilk testi ile grup varyanslarının homojenliği ise Levene testi ile kontrol edildi. Bulgular: Bütün materyallerin yüzey pürüzlülük değerlerine bakıldığında % 0.9 izotonik sodyum klorür içerisinde bekletilen kompozit rezin örneklerinin pürüzlülük değerleri arasında istatistiksel olarak anlamlı bir farklılık gözlenmezken (p>0.05); sporcu içeceğinin kompozit rezin örneklerinde diğer içeceklere göre anlamlı derecede daha fazla pürüzlülüğe neden olduğu belirlendi (p<0.05). Sporcu içeceğinde bekletilen Premise örneklerinin ise Tetric ve Filtek Z-250 örneklerine göre istatistiksel olarak anlamlı derecede daha fazla pürüzlü olduğu belirlendi (p<0.05). Sonuç: Asitli içeceklere maruz bırakıldıktan sonra ağartıcı özellikteki diş macunu ile fırçalamanın kompozit rezin örneklerinde mikropürüzlülüğe neden olduğu gözlenmiştir.

Keywords

• Yüzey pürüzlülüğü, estetik restoratif materyaller, asitli içecekler, ağartıcı diş macunu

References

1. Grippo JO, Simring M, Schreiner S. Attrition, abrasion, corrosion and abfraction revisited: a new perspective on tooth surface lesions. J Am Dental Ass 2004; 135: 1109–18.
2. Wongkhantee S, Patanapiradej V, Maneenut C, Tantbirojn D. Effect of acidic food and drinks on surface hardness of enamel, dentine, and toothcoloured filling materials. J Dent 2006; 34: 214Lussy A, Jaeggi T, Jaeggi-Scharer S. Prediction of the erosive potential of some beverages. Caries Res 1995; 29: 349-54.
3. Zero DT. Etiology of dental erosion - extrinsic factors. Eur J Oral Sci 1996;104:162-77.
4. Edwards M, Creanor SL, Foye RH, Gilmour WH. Buffering capacities of soft drinks: the potential influence on dental erosion. J Oral Rehabil 1999; 26: 923-27.
5. Beiraghi S, Atkins S, Rosen S, Wilson S, Odom J, Beck M. Effect of calcium lactate in erosion and S. mutans in rats when added to Coca-Cola. Pediatr Dent 1989; 11: 312-5.
6. Geurtsen W., Leyhausen G. and Garcia Godoy F.: Effect of storage media on the fluoride release and surface microhardness of four polyacid-modified composite resins (“compomers”). Dent Mater 1999; 15: 196-201.
7. Wu W. and Mc Kinney J.E.: Influence of chemicals on wear of dental composites. J Dent Res 1982; 61: 1180-3.
8. Vieira A, Lugtenborg M, Ruben JL, Huysmans MC. Brushing abrasion of eroded bovine enamel pretreated with topical fluorides. Caries Res. 2006; 40: 224-30.

9. Nomoto R, McCabe JF. A simple acid erosion test for dental water-based cements. Dent Mater 2001; 17: 53–9.
10. Czarnecka B, Limanowska-Shaw H, Nicholson JW. Buffering and ion-release by a glass-ionomer cement under near-neutral and acidic conditions. Biomaterials 2002; 23: 2783–8.
11. Mante MO, Saleh N, Tanna NK, Mante FK. Softening patterns of light cured glass ionomer cements. Dent Mater 1999;15:303–9.
12. Lussi A, Jaeggi T, Zero D. The role of diet in the aetiology of dental erosion. Caries Res 2004; 38: 34–
13. McKenzie MA, Linden RWA, Nicholson JW. The physical properties of conventional and resinmodified glass-ionomer dental cements stored in saliva, proprietary acidic beverages, saline and water. Biomaterials 2003;24:4063–9.
14. Dodds M, Peggy P, Rodriguez D. The effect of some Mexican citric acid snacks on vitro tooth enamel erosion. Pediatr Dent 1997;19:339-40.
15. Maupome G, Diez de Bonilla J, Torres-Villasenor G, Andrade- Delgado LC, Castaño VM. In vitro quantitative assessment of enamel microhardness after exposure to eroding immersion in cola drink. Caries Res 1998;32:148-53.
16. West NX, Hughes JA, Addy M. Erosion of dentine and enamel in vitro by dietary acids: the effect of temperature, acid character, concentration and exposure time. J Oral Rehabil 2000;27:875-80.
17. Barbour ME, Finke M, Parker DM, Hughes JA, Allen GC, Addy M. The relationship between softening and erosion caused by soft drinks at a range of temperatures. J Dent 2006;34:207-13.
18. Goldstein G.R. and Lerner T.: The effect of toothbrushing on a hybrid composite resin. J Prosthet Dent 1991;66: 498-500.
19. Zero D.T.: Etiology of dental erosion-extrinsic factors, Eur J Oral Sci 1996;104: 162-77.
20. Wictorin L.: Effect of toothbrushing on acrylic resin veneering material. Acta Odontol Scand 1972;30: 383-3
21. Hallgren A., Oliveby A. and Twetman S.: Caries associated microflora in plaque from orthodontic appliances retained with glass ionomer cement. Scand J Dent Res 1992;100: 140- 3.
22. Toledano M., De La Torre F.J. and Osorio R.: Evaluation of two polishing methods for resin composites, Am J Dent 1994;7:328-30.
23. Shintani H., Satou J., Satou N., Hatashihara H. and Inoue T.: Effects of various finishing methods on staining and accumulation of Streptococcus mutans HS-6 on composite resins, Dent Mater 1985;1: 225-7.
24. Özel E, Gökçe K. Spor İçecekleri ve Dental Erozyon. Atatürk Üniv Diş Hek Fak Derg 2006; 16: 14Sarı ME, Koyutürk AE, Çankaya S. Günlük Tüketilen Yiyecek ve içeceklerin Mine ve Dolgu Materyallerinin Yüzey Sertliği Ve Pürüzlülüğüne Etkisi. Atatürk Üniv. Dis Hek. Fak. 2010;20(3):1531
25. Attin T., Buchalla W., Trett A. and Hellwig E.: Toothbrushing abrasion of polyacidmodified composites in neutral and acidic buffer solutions, J Prosthet Dent 1988;80:148-50.
26. Min JH, Kwon HK, Kim BI. The addition of nanosized hydroxyapatite to a sports drink to inhibit dental erosion: in vitro study using bovine enamel. J Dent. 2011; 39:629-35.
27. Tanoue N., Matsumura H., Atsuta M. Wear and surface roughness of current prosthetic composites after toothbrush/dentifrice abrasion. J Prosthet Dent 2000; 84: 93- 97.
28. Johnson WW, Dhuru VB, Brantley WA. Composite microfiller content and its effect on fracture toughness and diamaterial tensile strength. Dent Mater 1993; 9: 95- 8.
29. Önal B. Restoratif diş hekimliğinde maddeler ve uygulamaları, Bornova- İzmir, 2004, 4-9, 66-98.
30. Summit JB, Robbins JW, Hilton TJ, Schwartz RS. Fundamentalis of Operative Dentistry A Contemporary Approach 2006; 1: 289-339. Yazışma Adresi: Dt. Hanife KAMAK Gazi Üniversitesi
31. Diş Hekimliği Fakültesi Diş Hastalıkları ve Tedavisi ABD Tel: [phone]
32. Email: [e-mail]