Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi ve Karakterizasyonu

Derya Farisoğulları; Nilay Kantarcı Güler; Faruk Karadağ; Ahmet Ekicibil; Bekir Özçelik

doi:10.21605/cukurovaummfd.316752

Research Article

Production, Characterization and Effect of Te Doping on FeSe-11 Compounds

Year 2016, Volume: 31 Issue: ÖS2, 175 - 180, 15.10.2016

Derya Farisoğulları Nilay Kantarcı Güler Faruk Karadağ Ahmet Ekicibil Bekir Özçelik

https://doi.org/10.21605/cukurovaummfd.316752

Abstract

In this work, FeTe0.7Se0.3 single crystals have been synthesized by using the self-flux method, in order to understand effect of Te doping in the Fe-chalcogenides. For this purpose, the physical properties of sample have been investigated by Scanning Electron Microscopy (SEM), Energy dispersive x-ray (EDX) spectroscopy, X-ray diffraction (XRD) and magnetic techniques. The XRD results show that the sample has tetragonal structure, with some impurity peaks. SEM results demonstrate that the sample is distributed in a terrace-like formation. EDX results indicate that the distribution of Fe, Te and Se on the surface of the sample is homogenous. According to χ-1-T measurement, antiferromagnetic interaction is observed. In addition, M-H curves show nearly paramagnetic behavior for the sample measured.

Keywords

Fe-based superconductivity, Self-flux method, XRD, SEM, Magnetism

References

1. Onnes, H.K., 1911. The superconductivity of mercury, Commun. Phys. Lab. Univ. Leiden, p. 122–124.
2. Marouchkine, A., 2004. Room-Temperature Superconductivity, Cambridge International Science Publishing, Cambridge, UK, p. 82-93.
3. Bednorz, J.G., Muller, K.A., 1986. Possible High Tc Superconductivity in the Ba-La-Cu-O System, Z. Phys. B vol. 64, p. 189-193.
4. Dai, P., Chakoumakos, B.C., Sun, G.F., Wong, K.W., Xin, Y., Lu, D.F., 1995. Synthesis and Neutron Powder Diffraction Study of the Superconductor HgBa2Ca2Cu3O8+δ by Tl Substitution, Physica C: Superconductivity. 243, p. 201–206.
5. Monteverdea, M., Núñez-Regueiroa, M., Achab, C., Lokshinc, K.A., Pavlovc, D.A., Putilinc, S.N., Antipovc, E.V., 2004. Fluorinated Hg-1223 under Pressure: the Ultimate Tc of the Cuprates?, Physica C: Superconductivity. 408-410, p. 23-24.
6. Kamihara, Y., Watanabe, T., Hirano, M., Hosono, H., 2008. Iron-based Layered Superconductor La[O1-xFx]FeAs (x= 0.05-0.12) with Tc=26 K, J. Am. Chem. Soc. 130, p. 3296-3297.
7. Rotter, M., Tegel, M., Johrendt, D., 2008. Superconductivity at 38 K in the Iron Arsenide (Ba1-xKx)Fe2As2 Phys. Rev. Lett., 101, p. 1–4.
8. Chu, C.W., Chen, F., Gooch, M., Guloy, A.M., Lorenz, B., Lv, B., Sasmal, K., Tang, Z.J, Tapp, J.H., Xue, Y.Y., 2009. The Synthesis and Characterization of LiFeAs and NaFeAs, Physica C: Superconductivity, 469, p. 326-331.
9. Hsu, F.C., Luo, J.Y., Yeh, K.W., Chen, T.K., Huang, T.W., Wu, P.M., Lee, Y.C., Huang, Y.L., Chu, Y.Y., Yan, D.C., Wu, M.K., 2008. Superconductivity in the PbO-type Structure Alpha-FeSe, Proc. Natl Acad. Sci., 105, p. 14262–14264.
10. Zhu, X., Han, F., Mu, G., Zeng, B., Cheng, P., Shen, B., Wen, H., 2009. Sr3Sc2Fe2As2O5 as a Possible Parent Compound for FeAs-based Superconductors, Phys. Rev. B 79, 024516.
11. Wu, Z.F., Wang, Z.H., Tao, J., Qiu, L., Yang, S.G., Wen, H.H., 2016. Flux Pinning and Relaxation in FeSe0.5Te0.5 Single Crystals, Supercond. Sci. Technol., 29, 035006 (6pp).
12. Medvedev, S., McQueen, T.M., Troyan, I.A., Palasyuk, T., Eremets, M.I., Cava, R.J., Naghavi, S., Casper, F., Ksenofontov, V., Wortmann, G., Felser, C., 2009. Electronic and Magnetic Phase Diagram of Bold Italic Beta-Fe1.01Se with Superconductivity at 36.7 K under Pressure, Nat. Mater., 8, p. 630–633.

Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi ve Karakterizasyonu

Year 2016, Volume: 31 Issue: ÖS2, 175 - 180, 15.10.2016

Derya Farisoğulları Nilay Kantarcı Güler Faruk Karadağ Ahmet Ekicibil Bekir Özçelik

https://doi.org/10.21605/cukurovaummfd.316752

Abstract

Bu çalışma kapsamında, Fe-kalkojenlerin fiziksel mekanizmasını daha iyi irdelemek için FeTe0.7Se0.3 tek kristali self-flux metodu kullanılarak sentezlendi. Bu bağlamda, hazırlanan numunenin fiziksel özellikleri, Taramalı Elektron Mikroskopu (SEM), Enerji Saçılımlı X-ışını Spektroskopi (EDX), X-Işını Kırınımı (XRD) ve manyetik teknikleri kullanılarak incelendi. Numune, XRD sonucunda tetragonal kristal yapı ile birlikte bazı safsızlık piklerinin de varlığını sergilemektedir. SEM sonucu, numunenin terasa benzer bir oluşum olduğunu göstermektedir. EDS sonucu, Fe, Te ve Se elementlerinin numune yüzeyinde homojen olarak dağıldığını göstermektedir. χ-1-T ölçümlerine göre, numunede antiferromanyetik etkileşmeler gözlemlenmektedir. Buna ek olarak, M-H grafiklerinde ise neredeyse paramanyetik davranışın olduğunu göstermektedir.

Keywords

Fe-tabanlı süperiletkenler, Self-flux metodu, XRD, SEM, Manyetizma

References

1. Onnes, H.K., 1911. The superconductivity of mercury, Commun. Phys. Lab. Univ. Leiden, p. 122–124.
2. Marouchkine, A., 2004. Room-Temperature Superconductivity, Cambridge International Science Publishing, Cambridge, UK, p. 82-93.
3. Bednorz, J.G., Muller, K.A., 1986. Possible High Tc Superconductivity in the Ba-La-Cu-O System, Z. Phys. B vol. 64, p. 189-193.
4. Dai, P., Chakoumakos, B.C., Sun, G.F., Wong, K.W., Xin, Y., Lu, D.F., 1995. Synthesis and Neutron Powder Diffraction Study of the Superconductor HgBa2Ca2Cu3O8+δ by Tl Substitution, Physica C: Superconductivity. 243, p. 201–206.
5. Monteverdea, M., Núñez-Regueiroa, M., Achab, C., Lokshinc, K.A., Pavlovc, D.A., Putilinc, S.N., Antipovc, E.V., 2004. Fluorinated Hg-1223 under Pressure: the Ultimate Tc of the Cuprates?, Physica C: Superconductivity. 408-410, p. 23-24.
6. Kamihara, Y., Watanabe, T., Hirano, M., Hosono, H., 2008. Iron-based Layered Superconductor La[O1-xFx]FeAs (x= 0.05-0.12) with Tc=26 K, J. Am. Chem. Soc. 130, p. 3296-3297.
7. Rotter, M., Tegel, M., Johrendt, D., 2008. Superconductivity at 38 K in the Iron Arsenide (Ba1-xKx)Fe2As2 Phys. Rev. Lett., 101, p. 1–4.
8. Chu, C.W., Chen, F., Gooch, M., Guloy, A.M., Lorenz, B., Lv, B., Sasmal, K., Tang, Z.J, Tapp, J.H., Xue, Y.Y., 2009. The Synthesis and Characterization of LiFeAs and NaFeAs, Physica C: Superconductivity, 469, p. 326-331.
9. Hsu, F.C., Luo, J.Y., Yeh, K.W., Chen, T.K., Huang, T.W., Wu, P.M., Lee, Y.C., Huang, Y.L., Chu, Y.Y., Yan, D.C., Wu, M.K., 2008. Superconductivity in the PbO-type Structure Alpha-FeSe, Proc. Natl Acad. Sci., 105, p. 14262–14264.
10. Zhu, X., Han, F., Mu, G., Zeng, B., Cheng, P., Shen, B., Wen, H., 2009. Sr3Sc2Fe2As2O5 as a Possible Parent Compound for FeAs-based Superconductors, Phys. Rev. B 79, 024516.
11. Wu, Z.F., Wang, Z.H., Tao, J., Qiu, L., Yang, S.G., Wen, H.H., 2016. Flux Pinning and Relaxation in FeSe0.5Te0.5 Single Crystals, Supercond. Sci. Technol., 29, 035006 (6pp).
12. Medvedev, S., McQueen, T.M., Troyan, I.A., Palasyuk, T., Eremets, M.I., Cava, R.J., Naghavi, S., Casper, F., Ksenofontov, V., Wortmann, G., Felser, C., 2009. Electronic and Magnetic Phase Diagram of Bold Italic Beta-Fe1.01Se with Superconductivity at 36.7 K under Pressure, Nat. Mater., 8, p. 630–633.

There are 12 citations in total.

Details

Journal Section	Articles
Authors	Derya Farisoğulları This is me Nilay Kantarcı Güler This is me Faruk Karadağ This is me Ahmet Ekicibil This is me Bekir Özçelik This is me
Publication Date	October 15, 2016
Published in Issue	Year 2016 Volume: 31 Issue: ÖS2

Cite

APA	Farisoğulları, D., Kantarcı Güler, N., Karadağ, F., Ekicibil, A., et al. (2016). Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi ve Karakterizasyonu. Çukurova Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi, 31(ÖS2), 175-180. https://doi.org/10.21605/cukurovaummfd.316752
AMA	Farisoğulları D, Kantarcı Güler N, Karadağ F, Ekicibil A, Özçelik B. Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi ve Karakterizasyonu. cukurovaummfd. September 2016;31(ÖS2):175-180. doi:10.21605/cukurovaummfd.316752
Chicago	Farisoğulları, Derya, Nilay Kantarcı Güler, Faruk Karadağ, Ahmet Ekicibil, and Bekir Özçelik. “Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi Ve Karakterizasyonu”. Çukurova Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi 31, no. ÖS2 (September 2016): 175-80. https://doi.org/10.21605/cukurovaummfd.316752.
EndNote	Farisoğulları D, Kantarcı Güler N, Karadağ F, Ekicibil A, Özçelik B (September 1, 2016) Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi ve Karakterizasyonu. Çukurova Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi 31 ÖS2 175–180.
IEEE	D. Farisoğulları, N. Kantarcı Güler, F. Karadağ, A. Ekicibil, and B. Özçelik, “Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi ve Karakterizasyonu”, cukurovaummfd, vol. 31, no. ÖS2, pp. 175–180, 2016, doi: 10.21605/cukurovaummfd.316752.
ISNAD	Farisoğulları, Derya et al. “Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi Ve Karakterizasyonu”. Çukurova Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi 31/ÖS2 (September 2016), 175-180. https://doi.org/10.21605/cukurovaummfd.316752.
JAMA	Farisoğulları D, Kantarcı Güler N, Karadağ F, Ekicibil A, Özçelik B. Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi ve Karakterizasyonu. cukurovaummfd. 2016;31:175–180.
MLA	Farisoğulları, Derya et al. “Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi Ve Karakterizasyonu”. Çukurova Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi, vol. 31, no. ÖS2, 2016, pp. 175-80, doi:10.21605/cukurovaummfd.316752.
Vancouver	Farisoğulları D, Kantarcı Güler N, Karadağ F, Ekicibil A, Özçelik B. Te Katkısının FeSe-11 Bileşiklerine Etkisi, Üretimi ve Karakterizasyonu. cukurovaummfd. 2016;31(ÖS2):175-80.