The Determination of Some Physical and Mechanical Characterictics of Olive Wood (Olea Europaea)

Year 2014, Volume: 10 Issue: 2, 29 - 35, 29.01.2017

Gonca Düzkale İbrahim Bektaş Hasan Hüseyin Tunç Yasin Doğanlar

Abstract

In this study, some mechanical and physical properties of Olea europaea grown in Kahramanmaraş, Turkey were determined. Physical properties, such as air-dried density, oven-dried density, volumetric shrinkage, swelling and mechanical properties, such as compression strength, impact bending strength, modulus of rupture, modulus of elasticity were determined.

According to the test results, the air-dried density of 0.86 g/cm3, oven-dried density of 0.76 g/cm3, volumetric shrinkage of 9.7 %, volumetric swelling of 10.2 %, compression strength of 53.17 N/mm2, impact bending strength 0.30 kgm/cm2, modulus of rupture of 64.39 N/mm2 and modulus of elasticity of 4444 N/mm2 were found.

Keywords

Olive wood, Physical properties

Zeytin Ağacı (Olea Europaea) Odunun Bazı Fiziksel ve Mekanik Özelliklerinin Belirlenmesi

Abstract

Bu çalışmada, Kahramanmaraş’ta yetişen Zeytin ağacı odununun hava kurusu yoğunluk, tam kuru yoğunluk, daralma ve genişleme miktarları, basınç direnci, dinamik eğilme direnci, statik eğilme direnci ve elastikiyet modülü değerleri belirlenmiştir.

Test sonuçlarına göre, hava kuru yoğunluk 0.86 g/cm3, tam kuru yoğunluk 0.76 g/cm3, hacimsel daralma % 9,7 ve genişleme miktarı % 10.2, basınç direnci 53.17 N/mm2, dinamik eğilme direnci 0.30 kgm/cm2, statik eğilme direnci 64.39 N/mm2 ve elastikiyet modülü değerleri 4444 N/mm2 bulunmuştur.

Keywords

Zeytin odunu, Fiziksel özellikler, Mekanik özellikler

References

• Anonim a, 2014, http://www.wikipedia.org/wiki/zeytin, erişim:25.06.2013,
• Anonim b, 2014, http://www.wood-database.com/lumber-identification/hardwoods/olive, erişim:13.02.2014,
• Arno, J 1988. Olea europea – Olive. In A Guide to Useful Woods of the World, Flynn Jr., J.H., Editor. King Philip Publishing Co., Portland, Maine,
• Bektaş, İ 1997. Kızılçam (Pinus Brutia ten.) Odununun Teknolojik Özellikleri ve Yörelere Göre Değişimi, Doktora Tezi, İstanbul Üniversitesi, Fen bilimleri Enstitüsü, İstanbul,
• Bozkurt, Y., Göker, Y 1987. Fiziksel ve Mekanik Ağaç Teknolojisi Kitabı, İstanbul Üniversitesi Orman Fakültesi Yayınları, Yayın No: 388,
• Bozkurt, Y., Göker, Y 1996. Fiziksel ve Mekanik Ağaç Teknolojisi, İÜ, Orman Fakültesi Yayınları, Üniversite Yayın No:3944, İstanbul,
• Efe, H., Çağatay, K 2011. Çeşitli Masif Ağaç Malzemelerin Bazı Fiziksel ve Mekanik Özelliklerinin Belirlenmesi, Politeknik Dergisi, Cilt :14, sayı:1, s:55-61,
• Erdocia, X., Prado, R. Corcuera, M. A., Labidi, J 2014. Effect of Different Organosolv Treatments on The Structure Andproperties of Olive Tree Pruning Lignin, Journal of Industrial and Engineering Chemistry, 20: 1103–1108,
• Garcia-Maravera, A., Rodriguezb, M.L., Serrano-Bernardoa, F., Diazc, Zamorano, L.F 2015. Factors Affecting The Quality of Pellets Made from Residual Biomass of Olive Trees, Fuel Processing Technology, 129:1–7,
• Govorčin, S., Sinković, T., Sedlar, T 2010. Dimensional Stability of Olive (Olea europaea L.) and Teak (Tectona grandis L.), Drvna Industrıja, 61 (3) 169-173.