A COMPARATIVE STUDY ON THE STRESS INTENSITY FACTOR OF CARBON EPOXY COMPOSITE PLATES HAVING CENTRAL HOLES

Year 2000, Volume: 6 Issue: 2, 109 - 112, 01.02.2000

M. Hüsnü Dirikolu Alaattin Aktaş

https://izlik.org/JA93AA63PR

Abstract

In this paper, a comparative study regarding the determination of stress intensity factors (SIF) for non-standard thin composite plates is presented. Carbon-Epoxy composite plates are considered for the study. Unnotched specimens and specimens containing either 4, 6, or 8 mm dia. holes are prepared and then tested. Based on the experimental data thus obtained, two analytical approaches and a finite element fracture analysis tool called FRANC have been used to compare the critical SIF values for this composite material.

Keywords

Stress intensity factor , Fracture , Crack , Composite , Carbon epoxy

DELİKLİ KARBON-EPOKSİ PLAKALARIN GERİLME ŞİDDETİ FAKTÖRLERİ ÜZERİNDE KARŞILAŞTIRMALI BİR ÇALIŞMA

https://izlik.org/JA93AA63PR

Abstract

Makalede standart olmayan ince kompozit levhaların gerilme şiddeti faktörlerinin (GŞF) hesaplanmasıyla ilgili karşılaştırmalı bir çalışma sunulmaktadır. Çalışmada Karbon-Epoksi kompozit levhalar kullanılmıştır. Çentiksiz ve üzerinde 4, 6 veya 8 mm çapında delik bulunan deney numuneleri hazırlanıp test edilmiştir. Elde edilen deney sonuçlarına dayanarak, iki analitik yaklaşım ve FRANC-sonlu elemanlar programı kullanılarak kompozitin kritik GŞF'leri hesaplanıp karşılaştırmalar yapılmıştır.

Keywords

Gerilme şiddeti faktörü , Kırılma , Çatlak , Kompozit , Karbon epoksi