The Evaluation Of Components Of Framework Prosthesis Made İn Different Prosthodontics Laboratories By XRF-Spectroscopy

Öz

In dental laboratories, the alloy which remains from the first cast is often reused and other restorations are made with the new alloy addition. The repeated process of casting can change the chemical components and and micro-structures of alloys. In this study, the components of framework samples which were made in six different dental laboratories which work with our faculty were evaluated by use of XRF spectroscopy. Duplicated models obtained from the measurement taken from the lower jaw of a partial toothless patient, by having been sent to six different laboratories, framework prothesis was prepared and by XRF spectroscopy current components were determined. Components of prothesis prepared in laboratories when compared to orginal component it has been determined that in all framework prothesis chrome rate has decreased and some elements were lost.

Anahtar Kelimeler

• Framework prosthesis, metal alloys, repeated casting, XRF spectroscopy

Farklı Protez Laboratuvarlarında Hazırlanan İskelet Protezlerin Bileşimlerinin XRF Spektroskopisi İle Değerlendirilmesi

Öz

Protez laboratuvarlarında, ilk dökümden artan alaşımlar sıklıkla yeniden kullanılmakta ve yeni alaşım ilavesi ile başka restorasyonlar oluşturulmaktadır. Tekrarlanan döküm işlemi, alaşımların kimyasal bileşimlerini ve mikro-yapılarını değiştirebilmektedir. Bu çalışmada, fakültemizle çalışmakta olan altı farklı protez laboratuvarında hazırlatılan iskelet örneklerin bileşimleri XRF spektroskopisi ile değerlendirilmiştir. Kısmi dişsiz bir hastanın alt çenesinden alınan ölçüden elde edilen dublikat modeller altı farklı laboratuvara gönderilerek iskelet protezler hazırlatılmış ve XRF spektroskopisi ile mevcut bileşimler belirlenmiştir. Laboratuvarlar tarafından hazırlanan protezlerin bileşimleri orijinal bileşim ile karşılaştırıldığında; bütün iskelet protezlerde krom oranının azaldığı, bazı elementlerin ise kaybolduğu saptanmıştır.

Anahtar Kelimeler

• İskelet protez, metal alaşımları, tekrarlanan döküm, XRF spektroskopisi.

Kaynakça

1. Açıkgöz O. Dişhekimliğinde Maddeler Bilgisi. Erzurum, 1996. p. 195-198.
2. O’Brien WJ. Dental Materials: Properties and Selections. Quintessence Publishing Co, Chicago, 19 p. 363-7. Baran İ, Nalçacı R. Dişhekimliğinde kullanılan materyaller ve alerjik reaksiyonlar. Atatürk Üniv Diş Hek Fak Derg 2007;Suppl.:26-32.
3. Moffa JP, Lugassy AA, Guckes AD, Gettleman L. An evaluation of nonprecious alloys for use with porcelain veneers. Part I. Physical properties. J Prosthet Dent 1973;30 4 Pt 1:424-31.
4. Zaimoğlu A, Can G, Ersoy AE, Aksu L. Diş Hekimliğinde Maddeler Bilgisi. Ankara Üniv. Basımevi, Ankara, Bölüm 1993. p. 19.
5. Jochen DG, Caputo AA, Matyas J. Reuse of silverpalladium ceramic metal. J Prosthet Dent 1991; 65: 588Reisbick MH, Brantley WA. Mechanical property and microstructural variations for recast low-gold alloy. Int J Prosthodont 1995; 8: 346-50.
6. Ayad MF. Compositional stability and marginal accuracy of complete cast crowns made with asreceived and recast type III gold alloy. J Prosthet Dent 2002; 87: 162-6.
7. Lopes MB, Consani S, Sinhoreti MAC, CorrerSobrinho L. Influence of recasting palladium-silver alloy on the fit of crowns with different marginal configurations. J Prosthet Dent 2005; 94: 430-4.
8. Viennot S, Lissac M, Malquarti G, Dalard F, Grosgogeat B. Influence of casting procedures on the corrosion resistance of clinical dental alloys containing palladium. Acta Biomaterialia 2006; 2: 321Peraire M, Martinez-Gomis J, Anglada JM, Bizar J, Salsench J, Gil FJ. Effects of recasting on the chemical composition, microstructure, microhardness, and ion release of 3 dental casting alloys and titanium. Int J Prosthodont 2007; 20: 286Al-Hiyasat AS, Darmani H. The effects of recasting on the cytotoxicity of base metal alloys. J Prosthet Dent 2005; 93: 158-63.

9. Hesby DA, Kobes P, Garver DG, Pelleu GB. Physical properties of a repeatedly used nonprecious metal alloy. J Prosthet Dent 1980; 44: 291-3.
10. Nelson DR, Palik JF, Morris HF, Comella MC. Recasting a nickel-chromium alloy. J Prosthet Dent 1986; 55: 122-7.
11. Özdemir S, Arıkan A. Effects of recasting on the amount of corrosion products released from two Ni-Cr base metal alloys. Eur J Prosthodont Rest Dent 1998; 6: 149-53.
12. Nalbant D, Yaluğ S, Gürbüz R. Tekrarlanan dökümün tek parça bölümlü protez alaşımının mekanik özelliklerine etkisi. GÜ Dişhek Fak Derg 2002; 19: 9-14.
13. Leinfelder KF, Lemons JE. Clinical Restorative Materials and Techniques. Lea and Febiger, Philadelphia, Chapters 4 1988: p.119-121,136, 270.
14. Mei Y, Ma MX, Nie ZR. The element determination of six samples of petal powders by using XRF spectrometry. Guang Pu Xue Yu Guang Pu Fen Xi 2012;32:1969-71.
15. Dharmar S, Rathnasamy J, Swaminathan TN. Radiographic and metallographic evaluation of porosity defect and grain structure of cast chromium cobalt removable partial dentures. J Prosthet Dent 1993; 69: 369-73.
16. Kotake M, Wakabayaski N, Ai M, Yoneyama T, Hamanaka H. Fatique resistance of titanium-nickel alloy cast clasps. Int J Prosthodont 1997; 10: 547
17. Lassila L V J, Vallittu P K. Effect of water and artificial saliva on the low cycle fatique resistance of cobalt-chromium dental alloy 1998; 80: 708-13.
18. Karaağaçlıoğlu L, Hasanreisoğlu U, Akören AC, Keskin Y. Kıymetsiz metal alaşımlarında tekrarlanan dökümlerin alaşımın bileşimine etkisi. A Ü Diş Hek Fak Derg 1991; 18: 179-83.
19. Asgar K, Arfaei AH. Castability of crown and bridge alloys. J Prosthet Dent. 1985; 54(1): 60-3.
20. Baran GR. The metallurgy of Ni-Cr alloys for fixed prosthodontics. J Prosthet Dent 1983; 50: 113-6.
21. Kelly CR, Rose TC. Nonprecious alloys for use in fixed prosthodontics. J Prosthet Dent 1983; 49: 363Horasawa N, Marek M. The effect of recasting on corrosion of a silver palladium alloy. Dent Mater 2004; 20: 352-7.
22. Tuccillo JJ, Lichtenberger H, Nielsen JP. Composition stability of gold base dental alloys for different melting techniques. J Dent Res 1974; 53: 1127Powers JM, Sakaguchi RL. Craig’ s Restorative Dental Materials. 12th ed. St. Louis: CV Mosby Co; 200 p. 57-70, 133-5, 363- 93.
23. Henrique GEP, Consani S, Almeida Rollo J.MD, Silva FA. Soldering and remelting influence on fatique strength of cobalt-chromium alloy. J Prosthet Dent 1997;78:146-52.
24. Craig RG, Powers JM, Wataha JC. Dental Materials Properties and Manipulation. 8th ed. St. Louis: CV Mosby Co; 2004. p. 27, 238, 47.
25. Aksoy G, Örgev V, Bıçakçı A. Farklı eritme yöntemlerinin yeni baz metal alaşımları ile bunlara değişik oranlarda artık alaşım karıştırılmış olanlarının yüzey niteliği ve sertlikleri üzerindeki etkilerinin karşılaştırılması. Ege Diş Hek Fak Derg 1995;16:144-51.
26. Özdemir Doğan D, Özdemir AK, Polat NT, Dal U, Gümüş C, Akkurt İ. Prevalence of respiratory abnormalities and pneumoconiosis in dental laboratory technicians. Tüberküloz ve Toraks Derg 2010; 58: 135-1.
27. Strandman E, Lockwandt P. Equipment for standardizing casting of Co-Cr alloys in dentistry. Odont Revy 1975;27:145-154.
28. Philips WR. Elements of dental materials. Chapter: 8, WB Sounders Company, 1977.
29. Wataha JC. Alloys for prosthodontic restorations. J Prosthet Dent 2002; 87: 351-63.
30. Kurtulmuş S, Aydın K. Tekrarlanan döküm işleminin dental alaşımların mekanik özelliklerine etkisi. Cumhuriyet Üniv Diş Hek Fak Derg 2008; 11: 126Yazışma Adresi: Prof. Dr. Zeynep YEŞİL DUYMUŞ
31. Recep Tayyip Erdoğan Üniversitesi Diş Hekimliği Fakültesi Protetik Diş Tedavisi Ana Bilim Dalı Rize e mail: [e-mail]