Reducing of Zirconium Silicate Quantity in Opaque White Sanitary Ware Glaze

Yıl 2017, Cilt: 4 Sayı: 1, 1 - 8, 28.06.2017

Ahmet Emrah Kaplan Gülfem Binal

Öz

 As expensive and common material the zircon (ZrSiO4
) contributes opacity to sanitaryware white opaque
glazes and promotes whiteness of glaze surface by its high optical refractive index. The high optical refractive index of
zirconium silicate is necessary to obtain acceptible white camouflage influence to cover the dark beige color of the soft
porcelain sanitaryware body. As known, as an opacifier the zircon has highest cost level in sanitaryware glaze recipes.
There are many studies on decrease of usage percentage of zirconium silicate in opaque glaze recipes. The calsined
caolin adapted alternative glaze recipes have been tried to obtain acceptible opaque sanitary glaze avoid high recipe
cost in this study. Alternative recipe combinations have been tried to provide lower cost sanitary opaque glaze of R2ORO-(ZrO2
)-B2O3-Al2O3-SiO2 glass and ceramic systems. As a result, the notable zircon usage reduction has been
achieved without any technical spesification lost or obstacle in industrial bases.

Anahtar Kelimeler

Zirconium Silicate, Opaque White Glaze, Sanitaryware, Calsined Caolin

Vitrifiye Seramik Beyaz Opak Sırlarda Zirkonyum Silikat Miktarının Azaltılması

Öz

Vitrifiye seramik beyaz opak sırlarında opasite sağlayıcı olarak yaygın ve pahalı bir hammadde olan zirkonyum
silikat (ZrSiO4
) kırınım indisinin yüksek olması sayesinde sırın opaklığını artırarak daha beyaz görünmesini
sağlamaktadır. Yüksek kırınım indisinin sağladığı örtücülük genelde koyu bej renkteki yarı porselen vitrifiye bünye
rengini kamufle edebilmek için gereklidir. Vitrifiye seramik opak sırlarının maliyetini arttıran en baskın unsur
zirkonyum silikattır. Opak sır reçetelerinde zirkonyum silikat oranını düĢürmek üzerine seramik pek çok çalıĢmalar
vardır. Bu çalıĢmada R2O-RO-(ZrO2
)-B2O3
-Al2O3
-SiO2 kristal sır sistemine kalsine kaolin eklenerek yüksek reçete
maliyetini düĢürmek amaçlanmıĢtır. Sonuç olarak endüstriyel anlamda herhangi bir kullanım engeli veya teknik
özellik kaybı olmaksızın kayda değer oranda zirkon kullanım tasarrufu sağlanmıştır. 

Anahtar Kelimeler

Zirkonyum silikat, Opak beyaz sır, Seramik sağlık gereçleri, Kalsine kaolin

Kaynakça

• Domenico Fortuna, „Sanitaryware‟, Faenza Editrice, 2000 Italy.
• Tezi, Anadolu Üniversitesi Fen Bilimleri Enstitüsü Seramik Mühendisliği Anabilim Dalı, Eskişehir, 2009.
• Eppler, R. A. , “Glazes for high-fire bodies”, Ceram. Engineering Science. Proc. 2000.
• Synders, E. The Developments of Zircon as a Superor Opacifier, Tshwane University of Technology, Department of Chemical and Metallurgical Engineering, January 2007.
• Pekkan K. , Karasu, B. ve Önal, H. Ş. , “Zirkonsuz Opak Firit ve Firit Bazlı Hızlı Tek Pişirim Duvar Karosu Sırı Üretimi ve Karakterizasyonu”, IV. Uluslararası Katılımlı Seramik, Cam, Emaye, Sır ve Boya Semineri SERES 2007 Bildiriler Kitabı, 2007.
• Karasu, B., Dölekçekiç, E., Taşpınar, B., Cömert, M., Özdemir, H., Zirkonla Opaklaştırılmış Yer Karolarında Zirkon Kullanımını Azaltıcı Önlemler, Tübitak Seramik Araştırma Merkezi (SAM), P/1999-7, 1999.
• Karasu, B., Pekkan, K., “R2O-RO-(ZrO2)-B2O3-Al2O3-SiO2 Cam Seramik Sistemlerinden Hızlı Pişirim Duvar Karosu Opak Sırı Olarak Faydalanılması”, Afyon Kocatepe Üniversitesi, Fen Bilimleri Dergisi, 2009.
• Berns, R.S., Billmeyer and Saltzman's principles of color technology, J. Wiley/New York, 2000.
• Özcan, A., “Kağıt Yüzey Pürüzlülüğünün L* a * b * değerleri üzerine etkisinin belirlenmesi” , İstanbul Ticaret Üniversitesi Fen Bilimleri Dergisi, cilt.7, sayı. 14, pp.53-61, İstanbul, 2008.
• Eppler, R. A. , “Glazes for high-fire bodies”, Ceram. Engineering Science. Proc. 2000.