Investigation of the Effect of Impact Test Temperatures on the Compression After Impact Behavior of Composite Plates

Öz

The purpose of this study is to determine the effect of impact test temperature and plate material on the compressive strength of composite sheets after impact. Single-material 3-layer plates such as biaxial glass fiber/epoxy, carbon fiber/epoxy and kevlar fiber/epoxy were prepared for the tests. Compression after impact “CAI” tests were carried out on specimens exposed to 50 J impact at different temperatures (-20 ⁰C, 20 ⁰C and 60 ⁰C). Tests were performed on the INSTRON 1114 test machine using the Boeing test apparatus prepared according to the ASTM D7137 standard and load cell. The effect of this force on the damage was investigated by applying the compression force with the apparatus, which can make small adjustments according to the thickness and width of the samples. Using the information obtained from the load cell, a force-displacement curve was created for each sample and the maximum force that the samples could bear was obtained. Damage observation was made to understand the damage mechanism. Test results show that temperature changes affect compression behavior after impact in all samples. It has been observed that the plate material has an effect on the extent of the damage.

Anahtar Kelimeler

• Compression after impact strength
• Composite laminates
• Biaxial glass fiber
• Biaxial kevlar fiber
• Biaxial carbon fiber

Darbe Test Sıcaklıklarının Kompozit Levhaların Darbe Sonrası Bası Davranışına Etkisinin İncelenmesi

Öz

Bu çalışmanın amacı darbe testi sıcaklığının ve levha malzemesinin, kompozit levhaların darbe sonrası bası dayanımına etkisini tespit etmektir. Testler için her biri 3 tabakalı olan biaxial cam elyaf/epoksi, karbon elyaf/epoksi ve kevlar elyaf/epoksi plakalar hazırlanmıştır. Farklı sıcaklıklarda (-20 ⁰C, 20 ⁰C ve 60 ⁰C’de) 50 J’lük darbe uygulanmış olan numunelere sıkıştırma (Darbe sonrası bası “CAI”) testleri yapılmıştır. Testler INSTRON 1114 test makinesinde, ASTM D7137 standardına göre hazırlanan Boeing test aparatı ve yük hücresi kullanılarak uygulanmıştır. Numunelerin kalınlık ve genişliğine göre küçük ayarlamalar yapılabilen aparat ile numuneler üzerine bası uygulanarak hasar üzerindeki etkisi incelenmiştir. Yük hücresinden elde edilen bilgileri kullanarak her numune için kuvvet-deplasman eğrisi oluşturulmuş ve numunelerin taşıyabileceği maksimum kuvvet elde edilmiştir. Hasar mekanizmasının anlaşılması için hasar gözlemi yapılmıştır. Test sonuçları, sıcaklık değişimlerinin bütün numunelerde darbe sonrası bası davranışını etkilediğini göstermektedir. Levha malzemesinin de hasarın büyüklüğünde etkili olduğu görülmüştür.

Anahtar Kelimeler

• Darbe sonrası bası mukavemeti
• Tabakalı kompozitler
• Biaxial cam elyaf
• Biaxial kevlar elyaf
• Biaxial karbon elyaf

Kaynakça

1. Aktaş, M., Karakuzu, R. ve Arman, Y. 2009. Compression-After Impact Behavior of Laminate Composite Plates Subjected to Low Velocity Impact in High Temperatures, Composite structures, Cilt. 89, s. 77-82.
2. Poe, C. C., Portnova, M. A., Sankar, B. V. ve Jackson, W. C. 1991. Comparison of Impact Results for Several Polymeric Composites Over A Wide Range of Low Impact Velocities, NASA Conference Publication, 3104, Part 1.
3. Short, G. J., Guild, F. J. ve Pavier, M. J. 2002. Post-Impact Compressive Strength of Curved Gfrp Laminates, Composites Part A, Cilt. 33, s. 1487–1495.
4. Lal, K. M. 1982. Prediction of Residual Tensile Strength of Transversely Impacted Composite Laminates, Research in Structural and Solid Mechanics, NASA Conference Publication, s. 2245.
5. Irving, P. E. ve Cartie, D. D. R. 2002. Effect of Resin and Fiber Properties on Impact and Compression After Impact Performance of CFRP, Composite, Part A, Cilt. 33, s. 483-493.
6. Sanchez-Saez, S., Barbero, E. ve Navarro, C. 2008. Composite Residual Strength at Low Temperatures of Composite Laminates Subjected to Low-Velocity Impacts, Composites Structure, Cilt. 85, s. 226-232.
7. Corum, J. M., Battiste, R. L. ve Ruggles, M. B. 2003. Low-Energy Impact Effects on Candidate Automotive Structural Composites, Composites Science and Technology, Cilt. 63-6, s. 755–769.
8. Halvorsen, A., Salehi-Khojn, A., Mahinfalah, M. ve Nakhaei-Jazar, R. 2006. Temperature Effects on The Impact Behavior of Fiberglass and Fiberglass/Kevlar Sandwich Composites, Applied Composite Materials, Cilt. 13-6, s. 369-383.

9. Levin, K. 1986. Effect of Low Velocity Impact on Compression Strength of Quasi-Isotropic Laminate, Proceedings of American Society For Composites: First Technical Conference, s. 313–325.
10. Kwang-Hee, I., Cheon-Seok, C., Sun-Kyu, K., In-Young, Y. 2001. Effects of Temperature on Impact Damages in CFRP Composite Laminates, Composite Part B, Cilt. 32-669, s. 82.
11. Khojin, A. S., Bashirzadeh, R., Mahinfalah, M., Jazar, R. K. 2006. The Role of Temperature on Impact Properties of Kevlar/Fiberglass Composite Laminates, Composites: Part B, Cilt. 37(7–8), s. 593–602.
12. Icten, B. 2009. Repeated Impact Behavior of Glass/Epoxy Laminates, ProQuest Polymer, Composites, s. 1562 -1569.
13. Oskay, C., Yan. H., Krishnan, A. ve Xu, L. 2010. Compression-After-Impact Response of Woven Fiber-Reinforced Composites, Composites Science and Technology, Article in press.
14. Kan, H. P. 1988. Enhanced Reliability Prediction Methodology for Impact Damaged Composite Structure. Report, DOT/FAA/AR-97-79.
15. Ibekwe, S. I., Mensah, P. F., Li, G., Pang, S. S., Stubblefield, M. A. 2007. Impact and Post Impact Response of Laminated Beams at Low Temperatures, Compos Struct, Cilt. 79(1):12–7.
16. Gao, S. L., Kim, J. K. 2001. Cooling Rate Influences in Carbon Fibre/PEEK Composites, Part III: Impact Damage Performance, Composites: Part A, Cilt. 32:775–85.
17. Tay, T. E., Shen, F. 2002. Analysis of Delamination Growth in Laminated Composites with Consideration for Residual Thermal Stress Effects, J Compos Mater, Cilt. 36(11):1299–320.
18. Icten, B. M., Atas, C., Aktas, M. ve Karakuzu, R. (2009). Low temperature effect on impact response of quasi-isotropic glass/epoxy laminated plates. Composite Structures, 91(3), 318–323.