Comparison of Corrosion Behavior of Steel Wire Ropes in Different Types Used in Cranes

Öz

The aim of this study is to investigate the behavior after exposure to corrosion of different types of hoisting ropes used in cranes. For this, hempen and steel core 6x19 Standard, 8x19 Seale and 6x36 Warrington Seale group ropes are examined. The ropes are applied rapid aging test in aging test chamber for one month according to ASTM B117 standard. The aging test is made for 3 different process with 24 hours cycle and 30 days period process. In each aging process, temperature and time parameters were changed and effects of corrosion conditions were investigated and comparative results were given. Failures of the ropes are visually  determined after aging tests and effects of corrosion for each process are evaluated examining mass changes before and after aging test. In addition, the effect of corrosion damage on the mechanical properties of the rope was investigated.

Anahtar Kelimeler

• Hoisting Rope,Aging Test,Corrosion,Salt Fog

Krenlerde Kullanılan Farklı Tiplerdeki Çelik Tel Halatların Korozyon Davranışlarının Karşılaştırılması

Öz

Bu çalışmada, krenlerde kullanılan farklı tipteki yük taşıma halatlarının korozyona maruz bırakıldıktan sonraki davranışları incelenmiştir. Bunun için 6x19 Standart, 8x19 Seale ve 6x36 Warrington Seale halat gruplarından kendir ve çelik özlü halatlar alınmıştır. Halatlar ASTM B117 standardına uygun olarak yaşlandırma test kabininde her bir yaşlandırma prosesi için bir aylık sürede olmak üzere hızlı yaşlandırma testine tabi tutulmuştur. 24 saatlik döngülerle 30 periyotluk 3 farklı proses takip edilmiştir. Her bir yaşlandırma işleminde sıcaklık ve zaman parametresi değiştirilerek halatların  korozyona maruz kalma şartlarının etkisi incelenmiş ve karşılaştırmalı olarak sonuçlar verilmiştir. Yapılan yaşlandırma işlemi sonucunda halatlarda oluşan hasarlar gözle muayene ile belirlenmiş ve her bir proses için halatların yaşlandırma öncesi ve sonrası kütle değişimleri incelenerek korozyonun etkileri değerlendirilmiştir. Ayrıca, halatta meydana gelen korozyon hasarının mekanik özelliklere olan etkisi incelenmiştir.

Anahtar Kelimeler

• Yük Taşıma Halatı,Yaşlandırma Testi,Korozyon,Tuz Sisi

Kaynakça

1. Demirsoy, M. 1999. Transport Tekniği Kaldırma Makinaları. Cilt 1. Birsen Yayınevi, İstanbul, s. 6-22.
2. Doruk, M. 2014. Metalik Malzemeler ve Korozyon. Korozyon Derneği Yayınları, Ankara, s. 3-5.
3. Deflorian, F., Rossi, S., Tancon, B. ve Bonora P. L. 2004. Corrosion Behaviour of Steel Ropes for Snow and Rockfall Barriers, Corrosion Engineering, Science and Technology, Cilt. 39, 3, s. 250-254. DOI: 10.1179/147842204X2853
4. Mallick, M., Mitra, S. K. ve Basak, D. 2014. Corrosion Behaviour of FLC Wire Ropes, International Journal of Science and Research, Cilt. 3, 8, s. 816-819.
5. Meknassi, M., Tijani, A., Mouhib, N. ve El Ghorba, M. 2016. Experimental Study on Corrosion of Wire Rope Strands Under Sulfuric Acid Attack, The International Journal of Engineering and Science, Cilt. 5, 6, s. 40-45.
6. Meknassi, M., Mouhib, N., Tijani, A. ve El Ghorba, M. 2015. Experimental Study of Wires Extracted from Steel Wire Rope and Exposed to Sulfuric Acid, International Journal of Mechanical Engineering, Cilt. 3, 11, s. 47-53.
7. Molnár, V., Fedorko, G., Krešák, J., Peterka, P. ve Fabianová, J. 2017. The Influence of Corrosion on The Life of Steel Ropes and Prediction of Their Decommissioning, Engineering Failure Analysis, Cilt. 74, s. 119–132. DOI:10.1016/j.engfailanal.2017.01.010
8. Songquan, W., Dekun, Z., Dagang, W. ve Zefeng Z. 2011. Electrochemical Corrosion Behavior of Steel Wires in a Coalmine with a Corrosive Medium, Mining Science and Technology (China), Cilt. 21, s. 71-76. DOI: 10.1016/j.mstc.2010.12.003

9. Kim, S. H., Ham, S. H. Ve Kwon, J. D. 2014. Bending Fatigue Characteristics of Corroded Wire Ropes, Journal of Mechanical Science and Technology, Cilt. 28, 7, s. 2853-2859. DOI: 10.1007/s12206-014-0639-8
10. Kurashov, D. A., Barsukov, V. K., Barsukov, E. V., Kadochnikov, N. P., Makarova, E. V., Svidovskii, F. G ve Gorbatov, E. K. 2008. Effect of Various Lubricants on Corrosion Resistance of Steel Ropes and on The Resistance of Organic Cores to Biological Attack, Metallurgist, Cilt. 52, s. 111-115.
11. Gorbatov, E. K. vd. 2007. Steel Rope with Longer Service Life and Improved Quality, Metallurgist, Cilt. 51, s. 279-283.
12. Peng, P. C., Wang, C. Y. 2015. Use of Gamma Rays in The Inspection of Steel Wire Ropes in Suspension Bridges, NDT&E International, Cilt. 75, s. 80-86. DOI: 10.1016/j.ndteint.2015.06.006
13. Loeve, A. J., Krijger, T., Mugge, W., Breedveld, P., Dodou, D. ve Dankelman, J. 2014. Static Friction of Stainless Steel Wire Rope-rubber Contacts, Wear, Cilt. 319, s. 27-37. DOI: 10.1016/j.wear.2014.07.005
14. Torkar, M., Arzensek, B. 2002. Failure of Crane Wire Rope, Engineering Failure Analysis, Cilt. 9, s. 227-233.
15. Kresak, J., Kropuch, S. ve Peterka, P. 2012. The Anchors of Steel Wire Ropes, Testing Methods and Their Results, Metalurgija, Cilt. 51, 4, s. 485-488.
16. Singh, V., Lloyd, G. M. ve Wang, M. L. (2004). Effects of temperature and corrosion thickness and composition on magnetic measurements of structural steel wires. NDT&E International, 37, 525-538.
17. Díaz, B., Freire, L., Nóvoa, X. R. ve Pérez, M. C. (2009). Electrochemical behaviour of high strength steel wires in the presence of chlorides. Electrochimica Acta, 54, 5190-5198.
18. Shih, C. C., Shih, C. M., Su, Y. Y. ve Lin, S. J. (2005). Galvanic current induced by heterogeneous structures on stainless steel wire. Corrosion Science, 47, 2199-2212.
19. McCafferty, E. (2005). Validation of corrosion rates measured by the Tafel extrapolation method. Corrosion Science, 47, 3202-3215.
20. Baoyu, Z., Xinge, G., Xiaohua, C., Wenzhi, Y., Ziming, C., Wei, H., Fujun, S. ve Honggang, S. (2016). Improvement of the corrosion resistance of steel wires by manufacturing continuous bulk metallic glass-coated steel wires. Rare Metal Materials and Engineering, 45, 11, 2818-2822.
21. El-Amoush, A. S. ve Al-Duheisat, S. A. (2018). Cathodic polarization behavior of the structural steel wires under different prestressing conditions. Journal of Materials Research and Technology, 7, 1, 1-6.
22. Gabe, D. R. (2005). The centenary of Tafel’s equation. Transactions of The Institute of Metal Finishing, 83, 3, 121-124.
23. ASTM B117 Standard Practice for Operating Salt Spray (Fog) Apparatus.
24. Karasu, H.F., Demirsoy, M. 2016. Yük Taşıma Halatlarının Korozyon Davranışlarının İncelenmesi. XIV. Uluslararası Korozyon Sempozyumu, 5-7 Ekim, Bayburt, s. 152-156.
25. http:// http://www.celsancelik.com/urun-kategorileri/celik-halatlar (Erişim Tarihi: 01.08.2018).