FATIQUE BEHAVIOUR OF X40CrMo 5 1 FROM 20 TO 600oC

Yıl 2003, Cilt: 5 Sayı: 1, 159 - 171, 01.01.2003

Ruhi Yeşildal Sadri Şen İrfan Kaymaz

Öz

Since fatigue is a material behaviour seen in machine elements working under repeated
loadings, they are required to have high fatigue strength. Materials working under repeating
loads and high temperatures, such as high temperature tool steels, should have a very good
high temperature fatigue strength. In this study, fatigue behaviours of X40CrMoV51 hot work
tool steel were investigated in rotating bending fatigue experiment at the temperatures of 50,
100, 200, 300, 400, 500 and 600oC. Although, this material has a fatigue strength of 432 MPa
at room conditions, it decreases to 383 MPa at 400oC, and it remains constant from 400oC to
600oC.

Anahtar Kelimeler

Fatigue, high temperature, rotating bendind loading.

X40CrMo 5 1 ÇELİĞİNİN 20-600oC ARASINDAKİ YORULMA DAVRANIŞI

Öz

Yorulma, tekrarlı yüklemeler altında çalışan makine elamanlarında görülen bir malzeme
davranışı olduğundan bunların yorulma dayanımlarının yüksek olması istenir. Yüksek sıcaklık
takım çelikleri gibi yüksek sıcaklıkta tekrarlı yükler altındaki çalışma koşullarında,
malzemelerin yüksek sıcaklık yorulma dayanımlarının iyi olması gerekir. Bu çalışmada
X40CrMoV 5 1 sıcak iş takım çeliğinin 50, 100, 200, 300, 400, 500 ve 600 oC
sıcaklıklardaki yorulma davranışları, dönen eğmeli yorulma deneyi ile incelenmiştir. Bu
malzemenin oda sıcaklığındaki yorulma mukavemeti 432 MPa olup 400 oC da 383 MPa a
düşmüştür. 400oC ile 600oC arasında ise yaklaşık sabit kalmıştır.

Anahtar Kelimeler

Yorulma, yüksek sıcaklık, dönen eğmeli yükleme.