THE DETERMINATION OF VACUUM MELTING CONDITIONS FOR SOME INTERMETALLIC COMPOUNDS

Öz

The fast developments on the technology increase to need materials having high performance. Because of this,

the development of technology depends on development of the materials that have superior properties. The

intermetallic compounds with different physical and mechanical properties to give hope for using these

materials in hard conditions. Intermetallic compounds considered as a mid group between metals and ceramics,

and in the future believed to fill the gap between these two group materials. In this study, the vacuum induction

melting conditions were determined for some intermetallic compounds. In that manner, Ni3Al, NiAl, Ti3Al,

TiAl, Fe3A, FeAl and Mg2Si intermetallic compounds were produced by vacuum induction melting, and their

microstructures were observed.

Anahtar Kelimeler

• Ordered intermetallics,High temperature materials,Vacuum metallurgy

BAZI DÜZENLİ METALLARARASI BİLEŞİKLERİN VAKUMDA ERGİTME ŞARTLARININ BELİRLENMESİ

Öz

Günümüz teknolojisindeki hızlı ilerlemeler daha yüksek performansa sahip malzeme gereksinimini artırmaktır.

Bu yüzden teknolojik ilerleme bir manada üstün özellikli malzeme gelişimine bağlıdır. Metallearası bileşiklerin

çok farklı fiziksel ve mekanik özellikleri bu malzemelerin zor çalışma şartlarında kullanılabilmesi için ümit

vermektedir. Metallerarası bileşikler metaller ile seramikler arasında yeni bir malzeme grubu olarak

düşünülmekte ve gelecekte bu iki malzeme grubu arasındaki boşluğu dolduracağına inanılmaktadır. Bu

çalışmada, gelecek vadeden bazı düzenli metallerarası bileşiklerin vakum indüksiyon ergitme şartları

belirlenmiştir. Bu kapsamda, Ni3Al, NiAl, Ti3Al, TiAl, Fe3A, FeAl ve Mg2Si metallerarası bileşikleri vakumda

indüksiyon ergitme yoluyla üretilmiş ve mikroyapıları incelenmiştir.

Anahtar Kelimeler

• Düzenli İntermetalikler,Yüksek Sıcaklık malzemeleri,vakum metalurjisi

Kaynakça

1. [1] Cahn, R.W., Proceedings of Materials Week ’96 on Nickel and Iron Aluminides: Processing, Properties, and Applications, Ohio, 7-9 October 1996, edited by S.C. Deevi, V.K.Sikka, P.J.Maziasz and R.W.Cahn, USA,ASM International (1997) p 3.
2. [2] Çelikyürek, İ, Vakumda Ergitme Yolu İle Bazı Düzenli Metallerarası Bileşiklerin Üretimi, Yüksek Lisans Tezi, Osmangazi Üniversitesi Fen Bilimleri Enstitüsü, Eskişehir, Ocak 2000.
3. [3] Liu, C.T., Stiegler J.O., (Sam) Froes, F.H., Metals Handbook, 10th ed. Vol 2, 913-942, 1999
4. [4] Liu, C.T., and Kumar, K. S., Ordered Intermetallic Alloys. I. Nickel and Iron Aluminides, J.O.M., 38, May 1993
5. [5] Froes, F.H., Suryanarayana, C. and Eliezer, D., Synthesizing process and modeling advanced materials, J. Mat. Sci., 27, p.5113, 1992
6. [6] Sen S., and Stefanescu D. M.., Melting and casting processes for high-temperature intermetallics, J.O.M., 30-34, May 1991
7. [7] Darolia, R, NiAl alloys for high-temperature structural applications, J.O.M., 44, March 1991
8. [8] Li, G.H., Gill, H.S. and Varin R.A., Magnesium Silicide Intermetallic Alloys, Met. Trans., Vol. 24A, 2383, November 1993.