INVESTIGATION OF CaSO4.2H2O ADDITION TO KAOLIN USED IN PORCELAIN PRODUCTION

Yıl 2008, Sayı: 016, 105 - 112, 15.09.2008

Veli Uz Hüseyin Özdağ Eda Hocaoğlu

Öz

In this study, the effects on the rheology of kaolin-based ceramic suspension of sulphate salt with Ca+2 cation were investigated. Drying and firing behaviors of ceramic structure obtained from this suspension by using casting and semi solid shaping methods were also studied. Viscosity, plasticity, drying and physico-mechanical characteristic tests for suspension formed by adding CaSO4.2H2O to Kaolin were applied. It was observed that the ratio of 0.25 % - 0.50 % CaSO4.2H2O decreased the viscosity of kaolin. It was determined that this ratio is adequate for plasticity in semi-solid shaping. This ratio affects the drying behaviors positively and also improves the physico-mechanical characteristics. On the other hand, it was observed that this ratio deteriorate the color of ceramic structure.

Anahtar Kelimeler

Kaolin, Porcelain, Additive, Viscosity

CSH KATKISININ PORSELEN SÜSPANSİYON/ÜRÜN ÖZELLİKLERİNE ETKİLERİNİN ARAŞTIRILMASI

Öz

Bu çalışmada, porselen üretiminde kullanılan kaolene Ca+2 değerlikli katyona sahip CaSO4.2H2O tuzu ilave edilerek oluşturulan süspansiyonun vizkozite, plastiklik, kurutma davranışları ve fiziko-mekaniksel özellikleri incelenmiştir. % 0,25 CaSO4.2H2O oranının kaolenin vizkozitesini düşürdüğü, yarı katı şekillendirmede önemli olan plastiklik değeri için bu oranın yeterli olduğu, kurutma davranışlarını olumlu yönde etkilediği ve fiziko-mekaniksel özellikleri iyileştirdiği tespit edilmiştir. Ancak kaolen içerikli seramik bünyelerde çözülebilir sülfat tuzlarının % 0,25 oranında kullanımının seramik bünye rengini bozduğu tespit edilmiştir

Anahtar Kelimeler

Kaolen, Porselen, Katkı Maddesi, Vizkozite

Kaynakça

• [1] Işık, İ., 1996, Kil ve Kil Minerali Tanımı: AIPEA ve CMS Terminoloji Komitelerinin Ortak Raporu (Çeviri), Seramik Dünyası Dergisi, Temmuz-Ağustos sayısı, 15 s.
• [2] Grimshaw, R.W., 1971, The Chemistry And Physics Of Clays, Tech Books, 4012
• [3] Worrall, W.E., 1986, Clays and ceramic raw materials, Elsevier science publishing co., In., 52, Vanderbilt Avenue, New York, NY 10017, USA, 27-47 p.
• [4] Adams J. M. and Evans, S. ,1979, Determination of cation exchange capacity (layer change) of small quantities of clay minerals by nephelometry. Clay and clay Minerals, 27: 137- 13 p.
• [5] Phelps, G.W, Maguire, S.G., Kelly, W.J. and Wood, R.K., 1982, Rheology and Rheometry of Clay–Water Systems, Cyprus Industrial Minerals, Sandersville, CA,39-41 p.
• [6] Phelps, G.W., 1982, Slip Casting, Ceramic Monographs-Handbook of Ceramics, Verlag Schmid GmbH, Freiburg, 1 p.
• [7] Uz, V., Özdağ, H., Işık, İ. ve Yılmaz, B., Bazı Katkı Maddelerinin Tuğla Ve Kiremit Kilinin Vizkozite ve pH Değerlerine Etkisinin Ön Araştırması, 12. Ulusal Kil Sempozyumu Bildiriler Kitabı (Ed: T.Yakupoğlu, M., Açlan ve O. Köse), Yüzüncü Yıl Üniversitesi, Van, 2005.
• [8] Uz, V., Özdağ, H., Işık, İ. Ve Erdinç, E., M., (2005), Ca3(PO4)2 İlavesinin Kiremit Kilinin Özelliklerine Etkisinin Ön Araştırması, (Ed: B. Karasu, A. T. Özen, F. S. Alanyalı ve R. Yamaçlı): Seres III. Uluslar arası katılımlı Seramik, Cam, Emaye, Sır ve Boya Semineri, 221-231, 17-19 Ekim 2005, Eskişehir.
• [9] Uz, V., Isik, I., Ozdag, H., The effect of Na2SO4 addition on ceramic grade kaolin, (in Turkish); Journal of Clay Science and Technology, 2006
• [10] J. Amer. Ceram. Soc. 41, 1958, Theory of ıon exchange and development of charge in kaolinite-water systems, 136-140 p.
• [11] Reed, J., 1986, Introduction to the principles of ceramic processing, Wiley-Interscience Publications, New York, 134-144, 230-231, 380-386 p.
• [12] Chiari, B.V., 1986, Investigations on Drying Sensitivity (part 1), cfi/ber. DKG 9/10-86, 410-412 p.
• [13] Bender,W., Handle,F., 1982, Brick and Tile Making,Procedures and Operating Practice ın the heavy clay Industries, Wiesbaden und Berlin, Deutcshland, 272-282 p.
• [14] Chiari, B.von., 1986, Investigations on drying sensitivity ( a survey), (part 2), cfi/Ber. DKG 9/10 86 , 482-486 p.
• [15] Ryan, W., 1968, Properties of ceramic raw materials, 69-75 p.
• [16] Uz, V., 2004, İnorganik, Organik ve Biyolojik Bazlı İlavelerin Killerin Seramik Özellikleri Üzerine Etkisi, Osmangazi Üniversitesi Fen Bilimleri Enstitüsü Doktora Tezi, 507 s., Eskişehir.