Investigation of the Effects of Different Duty Cycles on Fe-W Alloy Coatings Produced by Electrodeposition Method

Abstract

In this study, electrodeposition Fe-W coating was applied. When Wolfram is compared in terms of mechanical properties, it has a harder structure than steel and shows high resistance to temperatures. Due to these properties, it will be a preferred coating in industrial applications. Aluminum was preferred as the coated substrate. The reason for this is that Aluminum performs very poorly in terms of corrosion resistance. As a result of the corrosion tests with Fe-W coating, this problem has been significantly eliminated. Different electrodeposition values were used during the coating. The deposition temperature played an important role in crystallization. As a result of characterization tests, images were taken at 3000 magnifications to see the surface morphology in obtaining SEM images. It was observed that granular morphology was formed as a result of the image. As a result of the Tafel polarization analysis, it was observed that the corrosion rate decreased to approximately 5mpy with increasing Ton time.

Keywords

• Fe-W kaplama
• Korozyon oranı
• Scherrer Denklemi
• Nodüler morfoloji
• İş çevrimi

Kaynakça

1. S. Wang, C. Zeng, Y. Ling, J. Wang, G. Xu, Phase transformations and electrochemical characterizations of electrodeposited amorphous Fe–W coatings, Surf. Coatings Technol. 286 (2016) 36–41. https://doi.org/10.1016/j.surfcoat.2015.12.011.
2. A. Nicolenco, N. Tsyntsaru, H. Cesiulis, Fe (III)-Based Ammonia-Free Bath for Electrodeposition of Fe-W Alloys, J. Electrochem. Soc. 164 (2017) D590–D596. https://doi.org/10.1149/2.1001709JES/XML.
3. K.R. Sriraman, S. Ganesh Sundara Raman, S.K. Seshadri, Corrosion behaviour of electrodeposited nanocrystalline Ni-W and Ni-Fe-W alloys, Mater. Sci. Eng. A. 460–461 (2007) 39–45. https://doi.org/10.1016/j.msea.2007.02.055.
4. A.L. Patterson, The scherrer formula for X-ray particle size determination, Phys. Rev. 56 (1939) 978–982. https://doi.org/10.1103/PhysRev.56.978.
5. A. Akyol, H. Algul, M. Uysal, H. Akbulut, A. Alp, A novel approach for wear and corrosion resistance in the electroless Ni-P-W alloy with CNFs co-depositions, Appl. Surf. Sci. 453 (2018). https://doi.org/10.1016/j.apsusc.2018.05.152.