Investigation of the Effects of Pore Widening Times on Oxide Pores on Pure Aluminum in Two-Step Anodic Oxidation Process

Öz

An anodic oxidation process is a commonly used for surface treatment to improve the surface properties of the metals and their alloys such as aluminum, tantalum, titanium, molybdenum etc. and thereby increase the service life of the specimen parts from these metals. A type of anodic oxidation process with different types and conditions is made in the two-step anodic oxidation process. The two-step anodic oxidation is a process that improves several surface properties, such as increasing the corrosion resistance by forming a continuous layer on the surface of a suitable metal such as aluminum. In a two-step anodic oxidation process, which has a more regular pore array than  one-step anodic oxidation, nanotechnology applications have been rapidly developing and with the potential production of various nano-tubes and nano-wires. In this study, the two-step potentiostatic anodic oxidation process on pure aluminum surface was investigated. For this purpose, electrolytically polished samples were anodized at 0,3 M oxalic acid solution at 40 V constant voltage for different times and were subjected to pore expansion in 0.1 M phosphoric acid solution. The current density time graphs obtained during anodic oxidation processes at constant voltages are important for the reproducibility of the anodic oxidation process. The properties of the anodic alumina in the porous structure obtained after pore expansion at different times (0, 30 and 60 minutes) and the average pore diameters were examined by SEM analysis. After the surface investigations, it has been determined that pore arrays become smooth and pore diameters increase depending on an increase in pore widening time. Depending on the desired processes, the fabrication of nanowires/tubes with different sizes can be carried out as desired uniform and homogeneous nanostructures.

Anahtar Kelimeler

• Pore diameters,Pore widening,, Pure Aluminum,Two-step anodic oxidation

Saf Alüminyuma Uygulanan İki Aşamalı Anodik Oksidasyon İşleminde Por Genişletme Süresinin Oksit Porlar Üzerindeki Etkilerinin İncelenmesi

Öz

Anodik oksidasyon işlemi alüminyum, tantalyum, titanyum, molibden vb. metal ve alaşımlarının yüzey özelliklerini geliştirmek ve böylece bu metallerden üretilen parçaların servis ömürlerini arttırmak için yaygın bir şekilde kullanılan bir yüzey işlemidir. Çok farklı türlerde ve koşullrda yapılan anodik oksidasyon işleminin bir çeşiti de iki aşamalı anodik oksidasyon işlemidir. İki aşamalı anodik oksidasyon işlemi, alüminyum gibi uygun bir metalinin yüzeyinde sürekli bir tabaka oluşturarak korozyon direncini arttırma gibi birçok yüzey özelliğini geliştiren bir işlemdir. Tek aşamalı anodik oksidasyona göre daha düzenli bir por dizilimine sahip olan iki aşamalı anodik oksidasyon işleminde, nanoteknoloji uygulamaları çok hızlı bir gelişim göstermiş ve bununla beraber çeşitli nano-tüpler ve nano-tellerin potansiyel üretimleri yapılmaktadır. Bu çalışmada, saf alüminyum yüzeyinde iki aşamalı potansiyostatik anodik oksidasyon işlemi incelenmiştir. Bu amaçla elektrolitik olarak parlatılan numuneler 0,3 M oksalik asit çözeltisinde 40 V sabit gerilim değerinde farklı sürelerde anodize edilen numuneler 0,1 M fosforik asit çözeltisinde por genişletme işlemine tabi tutulmuştur. Sabit geriilim değerinde yapılan anodik oksidasyon işlemleri sırasında elde edilen akım yoğunluğu süre grafikleri anodik oksidasyon işleminin tekrarlanabilirliği açından önem arz etmektedir. Farklı sürelerde (0, 30 ve 60 dakika) yapılan por genişletme işleminden sonra elde edilen gözenekli yapıdaki anodik alüminanın homojenliği ve ortalama por çapları gibi özellikleri yüzeyden yapılan SEM analizleriyle incelenmiştir. Yapılan incelemeler sonunda artan por genişletme süresine bağlı olarak por dizilimlerinin düzgünleştiği ve por çaplarının arttığı tespit edilmiştir. İşlemlerin arzu edilen şekilde yapılmasına bağlı olarak farklı boyutlarda sahip nanotellerin/tüplerin üretimi istenilen düzgün ve homojen nanoyapılar şeklinde gerçekleştirilebilecektir.

 

Anahtar Kelimeler

• Por çapları,Por genişletme,Saf alüminyum,İki aşamalı anodik oksidasyon

Kaynakça

1. Bouchama, L., Azzouz, N., Boukmouche, N., Chopart, J. P., Daltin, a. L., & Bouznit, Y. (2013). Enhancing aluminum corrosion resistance by two-step anodizing process. Surface and Coatings Technology, 235, 676–684. https://doi.org/10.1016/j.surfcoat.2013.08.046
2. Diggle, J., Downie, T., & Goulding, C. (1969). Anodic oxide films on aluminum. Chemical Reviews, 66(3), 365. https://doi.org/10.1021/cr60259a005
3. Dimiduk, D. M., Uchic, M. D., & Parthasarathy, T. A. (2005). Size-affected single-slip behavior of pure nickel microcrystals. Acta Materialia, 53(15), 4065–4077. https://doi.org/10.1016/j.actamat.2005.05.023
4. Erdogan, P., Yuksel, B., & Birol, Y. (2012). Effect of chemical etching on the morphology of anodic aluminum oxides in the two-step anodization process. Applied Surface Science, 258(10), 4544–4550. https://doi.org/10.1016/j.apsusc.2012.01.025
5. Ersching, K., Dorico, E., Da Silva, R. C., Zoldan, V. C., Isoppo, E. a., Viegas, a. D. C., & Pasa, a. a. (2012). Surface and interface characterization of nanoporous alumina templates produced in oxalic acid and submitted to etching procedures. Materials Chemistry and Physics, 137(1), 140–146. https://doi.org/10.1016/j.matchemphys.2012.08.058
6. Greer, J. R., & De Hosson, J. T. M. (2011). Plasticity in small-sized metallic systems: Intrinsic versus extrinsic size effect. Progress in Materials Science, 56(6), 654–724. https://doi.org/10.1016/j.pmatsci.2011.01.005
7. Greer, J. R., Oliver, W. C., & Nix, W. D. (2005). Size dependence of mechanical properties of gold at the micron scale in the absence of strain gradients. Acta Materialia, 53(6), 1821–1830. https://doi.org/10.1016/j.actamat.2004.12.031
8. Han, X. Y., & Shen, W. Z. (2011). Improved two-step anodization technique for ordered porous anodic aluminum membranes. Journal of Electroanalytical Chemistry, 655(1), 56–64. https://doi.org/10.1016/j.jelechem.2011.02.008

9. Iglesias-Rubianes, L., Skeldon, P., Thompson, G. E., Shimizu, K., & Habazaki, H. (2001). Influence of current density in anodizing of an Al-W alloy. Corrosion Science, 43(12), 2217–2227. https://doi.org/10.1016/S0010-938X(01)00022-1
10. Ilango, M. S., Mutalikdesai, A., & Ramasesha, S. K. (2016). Anodization of Aluminium using a fast two-step process. Journal of Chemical Sciences, 128(1), 153–158. https://doi.org/10.1007/s12039-015-1006-8
11. Kiener, D., Motz, C., Schöbert, T., Jenko, M., & Dehm, G. (2006). Determination of mechanical properties of copper at the micron scale. Advanced Engineering Materials, 8(11), 1119–1125. https://doi.org/10.1002/adem.200600129
12. Konno, H., Utaka, K., & Furuichi, R. (1996). A two step anodizing process of aluminium as a means for improving the chemical and physical properties of oxide films. Corrosion Science, 38(12), 2247–2256. https://doi.org/10.1016/S0010-938X(97)83145-9
13. Li, A. P., Müller, F., Birner, A., Nielsch, K., & Gösele, U. (1999). Polycrystalline nanopore arrays with hexagonal ordering on aluminum. Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films, 17(4), 1428–1431. https://doi.org/10.1116/1.581832
14. Liu, Y.-F., Wang, F.-H., Guo, D.-L., Huang, S.-Y., Sang, J.-P., & Zou, X.-W. (2009). Effects of heat treatment on optical absorption properties of Ni–P/AAO nano-array composite structure. Applied Physics A, 97(3), 677–681. https://doi.org/10.1007/s00339-009-5289-9
15. Ma, Y. (2010). Effect of Microstructure on corrosion resistance and anodising behaviour of AA 2099-T8 aluminium alloy, 1–311.
16. Masuda, H., & Fukuda, K. (1995). Ordered Metal Nanohole Arrays Made by a Two-Step Replication of Honeycomb Structuresof Anodic Alumina. Science, 268(5216), 1466–1468. https://doi.org/10.1126/science.268.5216.1466
17. Moldovan, V., Bruj, E., & Jumate, N. (2011). Porous anodic alumina films obtained by two step anodization. Bulletin of the Transilvania University of Braşov Series I: Engineering Sciences, 4(2), 75–80. https://doi.org/10.1007/s10008-011-1471-z
18. Montero-Moreno, J. M., Sarret, M., & Müller, C. (2007). Influence of the aluminum surface on the final results of a two-step anodizing. Surface and Coatings Technology, 201, 6352–6357. https://doi.org/10.1016/j.surfcoat.2006.12.003
19. Montero-Moreno, J. M., Sarret, M., & Müller, C. (2007). Some Considerations on the Influence of Voltage in Potentiostatic Two-Step Anodizing of AA1050. Journal of The Electrochemical Society, 154(3), 169–174. https://doi.org/10.1149/1.2426880
20. Ng, K. S., & Ngan, A. H. W. (2008). Stochastic nature of plasticity of aluminum micro-pillars. Acta Materialia, 56(8), 1712–1720. https://doi.org/10.1016/j.actamat.2007.12.016
21. Sheasby, P., & Pinner, R. (2001). The surface treatment and finishing of aluminium and its alloys.
22. Stelmashenko, N. A., Walls, M. G., Brown, L. M., & Milman, Y. V. (1993). Microindentations on W and Mo oriented single crystals: An STM study. Acta Metallurgica Et Materialia, 41(10), 2855–2865. https://doi.org/10.1016/0956-7151(93)90100-7
23. Sulka, G. D. (2008). Highly Ordered Anodic Porous Alumina Formation by Self-Organized Anodizing. In Nanostructured Materials in Electrochemistry (pp. 1–116). https://doi.org/10.1002/9783527621507.ch1
24. Thompson, G., Xu, Y., & Skeldon, P. (1987). Anodic oxidation of aluminium. Philosophical Magazine Part B, 55(6), 651–667. https://doi.org/10.1080/13642818708218371
25. Uchic, M. D., Dimiduk, D. M., Florando, J. N., & Nix, W. D. (2004). Sample dimensions influence strength and crystal plasticity. Science, 305(5686), 986–989. https://doi.org/10.1126/science.1098993
26. Zaraska, L., Sulka, G. D., & Jaskuła, M. (2010). The effect of n-alcohols on porous anodic alumina formed by self-organized two-step anodizing of aluminum in phosphoric acid. Surface and Coatings Technology, 204(11), 1729–1737. https://doi.org/10.1016/j.surfcoat.2009.10.051
27. Zaraska, L., Sulka, G. D., & Jaskuła, M. (2011). Anodic alumina membranes with defined pore diameters and thicknesses obtained by adjusting the anodizing duration and pore opening/widening time. Journal of Solid State Electrochemistry, 15(11–12), 2427–2436. https://doi.org/10.1007/s10008-011-1471-z
28. Zhou, J. H., He, J. P., Zhao, G. W., Zhang, C. X., Zhao, J. S., & Hu, H. P. (2007). Alumina nanostructures prepared by two-step anodization process. Transactions of Nonferrous Metals Society of China (English Edition), 17(1), 82–86. https://doi.org/10.1016/S1003-6326(07)60052-1