The Effect of Different Fineness and Substitution Ratios of Limy Fly Ashes on Abrasion and Carbonation Performance of Concrete

Öz

Afşin Elbistan / Kahramanmaraş thermal power plant waste C type fly ash (UK) was used in this study. This ash was ground and 6 different fineness values were obtained. With different fineness values of fly ash, reference concrete samples with and without fly ash admixture were prepared by using 10%, 30% and 50% substitution rates instead of cement in concrete. Abrasion and carbonation resistance tests were performed to determine the effect of fly ash fineness on hardened concrete samples. Abrasion resistance was applied on concrete samples which have completed curing time of 28, 56 and 90 days according to Rotating Cutter method stated in ASTM C 944-99 standard. For carbonation resistance, the samples were left in a dense medium for 360 days and the carbonation depth was determined. According to the experimental results obtained; In 10% and 50% fly ash substitute concrete samples, grinding time did not have much effect on bending strength, but it was found that fly ash substitution increased the strength according to the reference sample. Furthermore, it is seen that the grinding time increases slightly the tensile splitting strength in 30% fly ash substitute concrete samples, but this mixture ratio is below the resistance value obtained by the reference sample. The depth of carbonation increased with the increase of fly ash content added to concrete mixtures. The highest carbonation depth value is in the 50% UK substituted concrete sample (1.0 cm) with 0, 20, 30 and 45 minutes grinding time, the lowest carbonation depth value (0.3 cm) is 10% UK substituted with 10 and 45 minutes grinding time concrete samples. According to the results obtained; It was found that the grinding time of UK used in concrete mixtures did not cause much changes on the carbonation depth. The maximum wear rate in the 10, 30 and 50% UK substituted concrete mixtures occurred during the curing period of 28 days. It can be said that the 28-day curing time increases the wear amount of the samples as the grinding time increases in the 10% UK-substituted concrete mixture, but it is not very effective in curing times of 56 and 90 days. In other UK substitution rates (30 and 50%), it cannot be said that the abrasion amounts of the samples with a curing time of 28, 56 and 90 days are increased as the grinding time increases.

Anahtar Kelimeler

• Fly ash
• Type C
• Concrete
• Abrasion resistance
• Carbonation depth
• Flexural strength

Betonların Aşındırma ve Karbonatlaşma Performanslarına Kireçsi Uçucu Küllerin Farklı İncelik ve İkame Oranlarının Etkisi

Öz

Bu çalışmada Afşin Elbistan/ Kahramanmaraş termik santral atığı C tipi uçucu kül (UK) kullanılmıştır. Bu kül öğütülmüş ve 6 farklı incelik değeri elde edilmiştir. Uçucu küle ait değişik incelik değerleri ile betonda çimento yerine % 10, % 30 ve % 50 ikame oranlarında kullanılarak katkılı ve uçucu kül katkısız referans beton örnekleri hazırlanmıştır. Sertleşmiş beton örnekleri üzerine uçucu kül incelik değerinin etkisini belirlemek için aşınma ve karbonatlaşma direnci deneyleri yapılmıştır. Aşınma direnci ASTM C 944-99 standardında ifade edilen Rotating Cutter yöntemine göre 28, 56 ve 90 günlük kür süresini tamamlamış beton örnekleri üzerine uygulanmıştır. Karbonatlaşma direnci için örnekler 360 gün karbondioksit miktarı yoğun bir ortama bırakılmış ve karbonatlaşma derinliği belirlenmiştir. Elde edilen deney sonuçlarına göre; % 10 ve % 50 uçucu kül ikameli beton numunelerinde öğütme süresinin eğilme dayanımı üzerinde pek fazla etkili olmamış, ama referans numuneye göre uçucu kül ikamesinin dayanımı artırdığı anlaşılmıştır. Ayrıca % 30 uçucu kül ikameli beton numunelerinde öğütme süresinin eğilme dayanımını çok az artırdığı görülmektedir, ancak bu karışım oranıda referans numunenin elde ettiği dayanım değerinin altında değer almıştır. Beton karışımlarına ikame edilen uçucu kül oranlarının artmasıyla birlikte karbonatlaşma derinliği artmıştır. En yüksek karbonatlaşma derinliği değeri 0, 20, 30 ve 45 dakika öğütme sürelerine sahip % 50 UK ikameli beton örneğinde (1,0 cm), en düşük karbonatlaşma derinliği değeri (0.3 cm) ise 10 ve 45 dakika öğütme süresine sahip % 10 UK ikameli beton örneklerinde elde edilmiştir. Elde edilen sonuçlara göre; beton karışımlarında kullanılan UK’ün öğütme süresinin karbonatlaşma derinliği üzerinde pek fazla değişikliğe neden olmadığı görülmüştür. % 10, 30 ve 50 UK ikameli beton karışımları içerisinde en fazla aşınma miktarı 28 günlük kür süresinde meydana gelmiştir. % 10 UK ikameli beton karışımında öğütme süresi artıkça 28 günlük kür süresi numunelerinin aşınma miktarınında genel olarak arttırdığı söylenebilir, ama 56 ve 90 günlük kür sürelerinde pek etkisi olduğu söylenemez. Diğer UK ikame oranlarında (% 30 ve 50) öğütme süresinin artmasıyla 28, 56 ve 90 günlük kür süresine sahip numunelerinin aşınma miktarlarında belirgin bir değişiklik gözlemlenmemiştir.

Anahtar Kelimeler

• Uçucu kül
• C tipi
• Beton
• Aşınma Direnci
• Karbonatlaşma Derinliği

Kaynakça

1. Acharya, P.K. and Patro, S.K., (2016). Strength, sorption and abrasion characteristics of concrete usingferrochrome ash (FCA) and lime as partial replacement of cement, Cement and Concrete Composites, 74, 16-25.
2. Akçaözoğlu,K., Güldür, Ş.M., (2017). Mikrokronize Kalsit ve Uçucu Kül Katkısının Beton Özelliklerine Etkisinin Araştırılması, Afyon Kocatepe Üniversitesi Fen ve Mühendislik Bilimleri Dergisi, 17, 025603 (658-668).
3. Akman, M., S.,(1992). Deniz Yapılarında Beton Teknolojisi İstanbul Teknik Üniversitesi Gemi İnşaatı ve Deniz Bilimleri Fakültesi Baskı Atölyesi; Yayın No:1481,27,175.
4. ASTM C 944-99, (1999). Standard Test Method for Abrasion Resistance of Concrete or Mortar Surfaces by the Rotating-Cutter Method, American Society For Testing And Materials, USA.
5. ASTM C 618-19, (2019). Standard Specification for Coal Fly Ash and Raw or Calcined Natural Pozzolan for Use in Concrete, ASTM International, West Conshohocken, PA, 2019, www.astm.org.
6. Atiş, C. D., (2000). Yüksek Oranda Uçucu Kül Kullanımı ile Betonun Aşınması, İMO Teknik Dergi, Yazı 154, 11(4) 2217-2230.
7. Bilim, C., (2011). Zeolit Katkisinin Harçlarin Aşinma Direncine Etkisi, 6th International Advanced Technologies Symposium (IATS’11), 16-18 May 2011, Elazığ, Turkey.
8. BS EN 13293 (2004). Products and Systems For The Protectgion And Repair of Concrete Structures-Test Methods-Determination of Resistance To Carbonation, (2004).

9. Erdoğan, T., Y., (1997). Admixtures for Concrete. Middle East Technical University Press, Ankara, Turkey.
10. Erdoğan, T., Y., (2003). Beton, ODTÜ Geliştirme Vakfı Yayını, 191-502-518s. Ankara.
11. Gebler, S. H., Klieger, P., (1986). Effect of Fly Ash on the Durability of Air Entrained Concrete. Proceedings of ACI/Canmed Second International Conference on Fly Ash, Silica Fume, Slag and Natural Pozzolans in Concrete SP-91, SPAIN-Madrid, pp. 483-519.
12. Günindi, İ., (2005). Yumurtalık Su gözü Uçucu Külü İçeren Betonların Basınç, Eğilme, Aşınma Dayanımlarının Araştırılması Çukurova Üniversitesi, Fen Bilemleri Enstitüsü inşaat Mühendisliği Anabilim Dalında Yüksek Lisans tezi.
13. Kara, C., Yazıcıoğlu, S., (2016). Mermer Tozu Atığı ve Silis Dumanının Betonun Karbonatlaşma Özelliğine Etkisi, BEU Fen Bilimleri Dergisi BEU Journal of Science 5(2), 191-202.
14. Mehta, P., K., (1993). Pozzolanic and Cementitious by-Products as Mineral Admixtures for Concrete – A Critical Review, Proc. 1st Int. Conf. on the Use of fly ash, silica fume, slag and other mineral by-products in concrete, ACI SP-79, American Concrete Institute, Detroit, pp. 1–48.
15. Özer, Ş., (2012). Farklı Çimentoların Betondaki Karbonatlaşmaya Etkisinin Araştırılması, Fırat Üniversitesi, Fen Bilemleri Enstitüsü Yapı Eğitimi Anabilim Dalında Yüksek Lisans tezi.
16. Ramyar, K., (1993), Uçucu Küllerin Çimento Harcının Büzülmesine ve Betonun Karbonatlaşmasma Olan Etkileri, Endüstriyel Atıkların İnşaat Sektöründe Kullanılması Sempozyumu, TMMOB Ankara Şubesi, 133-147.
17. Ramyar, K., (2007). Portland Çimentosu – Süperakışkanlaştırıcı Katkı Uyumunu Etkileyen Faktörler, 2. Yapılarda Kimyasal Katkılar Sempozyumu ve Sergisi, Ankara.
18. Rashad, A., M., (2015). A brief on High-Volume Class F Fly Ash As Cement Replacement – A guide for Civil Engineer, International Journal of Sustainable Built Environment, 4, 278-306.
19. Siddique, R. (2004). Performance characteristics of high-volume Class F fly ash concrete, Cement and Concrete Research 34, 487 – 493.
20. Siddique, R., Khatib, J.M., (2010). Abrasion Resistance and Mechanical Propertiesof High-Volume Fy Ash Concrete, Materials and Structures, 43:709–718.
21. Siddique, R., Prince, W., Kamalı, S. (2007). Influence of Utilization of High-Volumes of Class F Fly Ash on the Abrasion Resistance of Concrete, Leonardo Electronic Journal of Practices and Technologies, p. 13-28.
22. Şahin, Y., E., (2004). Linyosülfanet Esaslı Beton Katkılarının Beton Performansına Etkileri, İstanbul Teknik Üniversitesi, Fen Bilemleri Enstitüsü İnşaat Mühendisliği Bölümü Yapı malzemesi Anabilim Dalında Yüksek Lisans tezi.
23. TS EN 12390-5, (2019). Beton-Sertleşmiş Beton Deneyleri Bölüm 5: Deney Numunelerinin Eğilme Dayanımının Tayini, TSE.
24. TS 802, (2016). Beton Karışım Tasarımı Hesap Esasları, TSE.
25. Yazıcıoğlu, S., Demirel, B., Gönen, T., Özer, Ş., (2012). Farklı Tip Çimentoların Betonun Karbonatlaşmasına Etkisi, SDU International Journal of Technologic Sciences, Vol. 4, No 3, pp. 112-120.